- 拉伸强度 [MPa]: 0.552
- 透光率 [%]: 90.0
Physical Properties | Metric | English | Comments | ||
---|---|---|---|---|---|
Specific Gravity | 0.970 g/cc | 0.970 g/cc | Part A | ||
1.04 g/cc | 1.04 g/cc | Mixed | |||
1.10 g/cc | 1.10 g/cc | Part B | |||
Viscosity | 275 cP | 275 cP | Part B | ||
615 cP | 615 cP | Mixed | |||
1000 cP | 1000 cP | Part A | |||
Mechanical Properties | Metric | English | Comments | ||
Hardness, Shore A | 50 | 50 | |||
Tensile Strength, Yield | 0.552 MPa | 80.0 psi | |||
Elongation at Break | 60 % | 60 % | |||
Tensile Modulus | 0.00172 GPa | 0.250 ksi | at 100% | ||
Electrical Properties | Metric | English | Comments | ||
Volume Resistivity | 3.00e+15 ohm-cm | 3.00e+15 ohm-cm | |||
Dielectric Constant | 3.96 @Frequency 100 Hz, Temperature 25.0 °C | 3.96 @Frequency 100 Hz, Temperature 77.0 °F | |||
Dielectric Strength | 19.7 kV/mm | 500 kV/in | |||
Thermal Properties | Metric | English | Comments | ||
CTE, linear | 200 µm/m-°C | 111 µin/in-°F | |||
Optical Properties | Metric | English | Comments | ||
Transmission, Visible | 90.0 % | 90.0 % | clear; thickness not quantified | ||
Processing Properties | Metric | English | Comments | ||
Cure Time | 60.0 min @Temperature 85.0 °C | 1.00 hour @Temperature 185 °F | |||
1440 min @Temperature 25.0 °C | 24.0 hour @Temperature 77.0 °F | ||||
Pot Life | 30 - 45 min | 30 - 45 min | Mass: 100g | ||
Descriptive Properties | |||||
Color | Clear | ||||
Fungus Resistance | Excellent | ||||
Mix Ratio | 1:1 | Volume | |||
88:100 | Weight |