- 密度 [g/cm3]: 0.144
- 拉伸强度 [MPa]: 103.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.144 g/cc | 0.00521 lb/in³ | ASTM D3574-95 Test A |
| 1.395 g/cc | 0.05040 lb/in³ | supporting material; ASTM D1505 | |
| Thickness | 508 - 991 microns | 20.0 - 39.0 mil | Range of Thicknesses Available |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength | 207 MPa | 30000 psi | MD, supporting material; ASTM D882 |
| Tensile Strength, Yield | 103 MPa | 15000 psi | F5, supporting material; ASTM D882 |
| Elongation at Break | 150 % | 150 % | Ultimate, supporting material; ASTM D882 |
| Tensile Modulus | 3.45 GPa | 500 ksi | MD, supporting material; ASTM D882 |
| Compressive Yield Strength | 0.00172 - 0.00931 MPa @Strain 25.0 % | 0.250 - 1.35 psi @Strain 25.0 % | 0.2"/min. strain rate |
| Coefficient of Friction, Dynamic | 0.40 | 0.40 | A/B, supporting material; ASTM D1894 |
| Compression Set | 10 % @Temperature 70.0 °C | 10 % @Temperature 158 °F | ASTM D3574-95 Test D |
| Thermal Properties | Metric | English | Comments |
| Shrinkage, MD | 1.2 % @Temperature 150 °C, Time 2340 sec | 1.2 % @Temperature 302 °F, Time 0.650 hour | supporting material |
| Shrinkage, TD | 0.00 % @Temperature 150 °C, Time 2340 sec | 0.00 % @Temperature 302 °F, Time 0.650 hour | supporting material |