- 密度 [g/cm3]: 1.45
- 缺口冲击强度: 9.6
- 断裂伸长率 [%]: 613
- 弯曲强度 [MPa]: 289.0
- 弯曲模量 [MPa]: 34.5
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in³ | ASTM D792 |
| Spiral Flow | 33.0 cm @Pressure 27.6 MPa, Temperature 163 °C | 13.0 in @Pressure 4000 psi, Temperature 325 °F | Mesa |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 289 MPa | 41900 psi | ASTM D638 |
| Elongation at Break | 0.487 % | 0.487 % | ASTM D638 |
| Tensile Modulus | 55.1 GPa | 7990 ksi | ASTM D638 |
| Flexural Yield Strength | 613 MPa | 88900 psi | ASTM D790 |
| Flexural Modulus | 34.5 GPa | 5000 ksi | ASTM D790 |
| Compressive Yield Strength | 275 MPa | 39900 psi | ASTM D695 |
| Compressive Modulus | 31.7 GPa | 4600 ksi | ASTM D695 |
| Shear Modulus | 2.90 GPa | 421 ksi | Interlaminar; ASTM D5379 |
| 11.0 GPa | 1600 ksi | In-Plane; ASTM D5379 | |
| Shear Strength | 65.5 MPa | 9500 psi | Interlaminar; ASTM D5379 |
| 206 MPa | 29900 psi | In Plane; ASTM D5379 | |
| Izod Impact, Notched | 9.60 J/cm | 18.0 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 3.60 µm/m-°C @Temperature 20.0 °C | 2.00 µin/in-°F @Temperature 68.0 °F | TMA |
| Thermal Conductivity | 0.474 W/m-K | 3.29 BTU-in/hr-ft²-°F | |
| Maximum Service Temperature, Air | 175 °C | 347 °F | Continuous (1000 hrs) |
| >= 300 °C | >= 572 °F | Deflection Temp; Load not reported; ASTM D648 | |
| Shrinkage | 0.00 % | 0.00 % | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 120 - 166 °C | 248 - 331 °F | Mold temperature |
| Shelf Life | 6.00 Month @Temperature -12.2 °C | 6.00 Month @Temperature 10.0 °F | |