- 密度 [g/cm3]: 1.3
- 弯曲模量 [MPa]: 10.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 - 1.80 g/cc | 0.0470 - 0.0650 lb/in³ | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | <= 10.0 MPa | <= 1450 psi | Transverse |
| 40.0 - 70.0 MPa | 5800 - 10200 psi | Longitudinal | |
| Tensile Modulus | 20.0 - 30.0 GPa | 2900 - 4350 ksi | Parallel to Plane |
| Flexural Strength | 80.0 - 200 MPa | 11600 - 29000 psi | Parallel to Plane |
| Flexural Modulus | 10.0 - 20.0 GPa | 1450 - 2900 ksi | Parallel to Plane |
| Compressive Strength | 60.0 - 150 MPa | 8700 - 21800 psi | Perpendicular to Plane |
| 120 - 200 MPa | 17400 - 29000 psi | Parallel to Plane | |
| Shear Strength | 20.0 - 30.0 MPa | 2900 - 4350 psi | in Plane |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 0.00300 ohm-cm | 0.00300 ohm-cm | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 1.50 µm/m-°C @Temperature 20.0 - 1000 °C | 0.833 µin/in-°F @Temperature 68.0 - 1830 °F | |
| CTE, linear, Transverse to Flow | 6.00 µm/m-°C @Temperature 20.0 - 1000 °C | 3.33 µin/in-°F @Temperature 68.0 - 1830 °F | |
| 6.00 µm/m-°C @Temperature 20.0 - 1000 °C | 3.33 µin/in-°F @Temperature 68.0 - 1830 °F | ||
| Thermal Conductivity | 50.0 - 100 W/m-K | 347 - 694 BTU-in/hr-ft²-°F | Perpendicular to Plane |
| 250 - 300 W/m-K | 1740 - 2080 BTU-in/hr-ft²-°F | Parallel to Plane | |