- 拉伸强度 [MPa]: 1552.0
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Tensile Strength, Yield | 1552 MPa @Temperature 24.0 °C | 225100 psi @Temperature 75.2 °F | |||
| Tensile Modulus | 126.2 GPa @Temperature 24.0 °C | 18300 ksi @Temperature 75.2 °F | |||
| Compressive Yield Strength | 924 MPa @Temperature 71.0 °C | 134000 psi @Temperature 160 °F | |||
| 1158 MPa @Temperature 24.0 °C | 168000 psi @Temperature 75.2 °F | ||||
| Compressive Modulus | 109.6 GPa @Temperature 24.0 °C | 15900 ksi @Temperature 75.2 °F | |||
| Descriptive Properties | |||||
| Cured Thickness per Ply (cm) | 0.0094 | Laminate | |||
| Dry Resin Content (%) | 38-40 | Prepreg | |||
| Fiber Volume (%) | 57 | Laminate | |||
| Flow (%) | 4-16 | ||||