- 密度 [g/cm3]: 0.17
- 断裂伸长率 [%]: 9.79
- 弯曲强度 [MPa]: 7.38
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.170 g/cc | 0.00613 lb/in³ | ASTM D1622-63 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 7.38 MPa | 1070 psi | ASTM D638-68 | ||
| Elongation at Break | 5.0 % | 5.0 % | ASTM D638-68 | ||
| Modulus of Elasticity | 0.314 GPa | 45.5 ksi | ASTM D638-68 | ||
| Flexural Yield Strength | 9.79 MPa | 1420 psi | Perpendicular to Sheet; ASTM D 790-66 | ||
| 10.3 MPa | 1490 psi | ASTM D790-66 | |||
| Compressive Yield Strength | 2.74 MPa | 398 psi | Perpendicular to Sheet; ASTM D 1621-64 | ||
| 6.37 MPa | 924 psi | ASTM D1621-64 | |||
| Shear Modulus | 0.0862 GPa | 12.5 ksi | ASTM C273-61 | ||
| Shear Strength | 2.94 MPa | 427 psi | Perpendicular to Sheet; ASTM C 273-61 | ||
| 4.41 MPa | 640 psi | ASTM C273-61 | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 130 °C | 266 °F | Dimensional stability per DIN 53424; oriented cell structure starts to decrease beyond this temperature. | ||
| Descriptive Properties | |||||
| Color | White | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.
Users of our Advanced Search (registration required) may exclude discontinued materials from search results.