- 密度 [g/cm3]: 1.63
- 缺口冲击强度: 0.8
- 弯曲强度 [MPa]: 119.0
- 弯曲模量 [MPa]: 9.50
- 硬度: 120.0
- 热变形温度 [℃]: 122.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.63 g/cc | 0.0589 lb/in³ | |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Ultimate | 119 MPa | 17300 psi | ASTM D638 |
| Elongation at Break | 2.8 % | 2.8 % | ASTM D638 |
| Flexural Strength | 183 MPa | 26500 psi | ASTM D790 |
| Flexural Modulus | 9.50 GPa | 1380 ksi | ASTM D790 |
| Izod Impact, Notched | 0.800 J/cm | 1.50 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 6.73 J/cm | 12.6 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 210 - 225 °C | 410 - 437 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C | 252 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 235 - 249 °C | 455 - 480 °F | Approximate middle barrel temperature range |