- 缺口冲击强度: 0.801
- 热变形温度 [℃]: 122.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.63 g/cc | 1.63 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0020 cm/cm @Thickness 3.175 mm | 0.0020 in/in @Thickness 0.1250 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 119 MPa | 17200 psi | ASTM D638 |
| Elongation at Break | 2.8 % | 2.8 % | ASTM D638 |
| Flexural Strength | 183 MPa | 26500 psi | ASTM D790 |
| Izod Impact, Notched | 0.801 J/cm | 1.50 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 6.73 J/cm | 12.6 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C | 252 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 250 - 260 °C | 482 - 500 °F | |
| Mold Temperature | 30.0 - 65.6 °C | 86.0 - 150 °F | |
| Drying Temperature | 130 °C | 266 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Predrying |