- 熔体流动速率 [g/10min]: 16.8
- 密度 [g/cm3]: 1.53
- 吸水率 [%]: 0.4
- 热变形温度 [℃]: 220.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.53 g/cc | 0.0553 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.40 % | 0.40 % | DIN 53495/1L | ||
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C/50% R.H. | ||
| Viscosity Test | 102 cm³/g | 102 cm³/g | Viscosity number; ISO 1628 | ||
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm | 0.0020 in/in | Sheet | ||
| 0.0034 cm/cm | 0.0034 in/in | 60x60x2mm; ISO 294 | |||
| Linear Mold Shrinkage, Transverse | 0.0107 cm/cm | 0.0107 in/in | 60x60x2mm; ISO 294 | ||
| 0.011 cm/cm | 0.011 in/in | Sheet | |||
| Melt Flow | 16.8 g/10 min @Load 2.16 kg, Temperature 250 °C | 16.8 g/10 min @Load 4.76 lb, Temperature 482 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 190 MPa | 27600 psi | ISO 2039-1 | ||
| Tensile Strength at Break | 135 MPa | 19600 psi | 5mm/min; ISO 527-2 | ||
| Tensile Strength | 75.0 MPa @Temperature 100 °C | 10900 psi @Temperature 212 °F | ISO 527 | ||
| 100 MPa @Temperature 50.0 °C | 14500 psi @Temperature 122 °F | ISO 527 | |||
| 140 MPa @Temperature 23.0 °C | 20300 psi @Temperature 73.4 °F | ISO 527 | |||
| 170 MPa @Temperature -20.0 °C | 24700 psi @Temperature -4.00 °F | ISO 527 | |||
| Tensile Stress | 40.0 MPa @Strain 0.500 %, Temperature 40.0 °C | 5800 psi @Strain 0.500 %, Temperature 104 °F | ISO 527 | ||
| 40.0 MPa @Strain 2.00 %, Temperature 140 °C | 5800 psi @Strain 2.00 %, Temperature 284 °F | ISO 527 | |||
| 50.0 MPa @Strain 4.00 %, Temperature 140 °C | 7250 psi @Strain 4.00 %, Temperature 284 °F | ISO 527 | |||
| 50.0 MPa @Strain 0.500 %, Temperature -40.0 °C | 7250 psi @Strain 0.500 %, Temperature -40.0 °F | ISO 527 | |||
| 52.0 MPa @Strain 5.00 %, Temperature 140 °C | 7540 psi @Strain 5.00 %, Temperature 284 °F | ISO 527 | |||
| 100 MPa @Strain 2.00 %, Temperature 40.0 °C | 14500 psi @Strain 2.00 %, Temperature 104 °F | ISO 527 | |||
| 105 MPa @Strain 3.00 %, Temperature 40.0 °C | 15200 psi @Strain 3.00 %, Temperature 104 °F | ISO 527 | |||
| 170 MPa @Strain 2.00 %, Temperature -40.0 °C | 24700 psi @Strain 2.00 %, Temperature -40.0 °F | ISO 527 | |||
| 200 MPa @Strain 3.00 %, Temperature -40.0 °C | 29000 psi @Strain 3.00 %, Temperature -40.0 °F | ISO 527 | |||
| 20.0 MPa @Strain 1.00 %, Time 3.60e+6 sec | 2900 psi @Strain 1.00 %, Time 1000 hour | 140°C; DIN 50014-23/50-2 | |||
| 25.0 MPa @Strain 1.00 %, Time 3.60e+6 sec | 3630 psi @Strain 1.00 %, Time 1000 hour | 100°C; DIN 50014-23/50-2 | |||
| 30.0 MPa @Strain 1.00 %, Time 3.60e+6 sec | 4350 psi @Strain 1.00 %, Time 1000 hour | 60°C; DIN 50014-23/50-2 | |||
| 30.0 MPa @Strain 2.00 %, Time 3.60e+6 sec | 4350 psi @Strain 2.00 %, Time 1000 hour | 140°C; DIN 50014-23/50-2 | |||
| 35.0 MPa @Strain 3.00 %, Time 3.60e+6 sec | 5080 psi @Strain 3.00 %, Time 1000 hour | 140°C; DIN 50014-23/50-2 | |||
| 35.0 MPa @Strain 2.00 %, Time 3.60e+6 sec | 5080 psi @Strain 2.00 %, Time 1000 hour | 100°C; DIN 50014-23/50-2 | |||
| 40.0 MPa @Strain 3.00 %, Time 3.60e+6 sec | 5800 psi @Strain 3.00 %, Time 1000 hour | 100°C; DIN 50014-23/50-2 | |||
| 40.0 MPa @Strain 0.600 %, Time 3.60e+6 sec | 5800 psi @Strain 0.600 %, Time 1000 hour | DIN 50014-23/50-2 | |||
| 55.0 MPa @Strain 2.00 %, Time 3.60e+6 sec | 7980 psi @Strain 2.00 %, Time 1000 hour | 60°C; DIN 50014-23/50-2 | |||
| 60.0 MPa @Strain 1.00 %, Time 3.60e+6 sec | 8700 psi @Strain 1.00 %, Time 1000 hour | DIN 50014-23/50-2 | |||
| 80.0 MPa @Strain 1.60 %, Time 3.60e+6 sec | 11600 psi @Strain 1.60 %, Time 1000 hour | DIN 50014-23/50-2 | |||
| Elongation at Break | 2.5 % | 2.5 % | 5mm/min; ISO 527-2 | ||
| Modulus of Elasticity | 10.0 GPa | 1450 ksi | ISO 527-2 | ||
| Flexural Strength | 200 MPa | 29000 psi | ISO 178 | ||
| Charpy Impact Unnotched | 6.70 J/cm² | 31.9 ft-lb/in² | ISO 179/1eU | ||
| Charpy Impact, Notched | 1.10 J/cm² | 5.24 ft-lb/in² | ISO 179/1eA | ||
| Dart Drop, Total Energy | <= 5.00 J | <= 3.69 ft-lb | ISO 6603-1 | ||
| Tensile Creep Modulus, 1000 hours | 7500 MPa | 1.09e+6 psi | ISO 899 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 | ||
| Dielectric Constant | 3.8 @Frequency 1.00e+6 Hz | 3.8 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 4.0 @Frequency 100 Hz | 4.0 @Frequency 100 Hz | IEC 60250 | |||
| Dielectric Strength | 100 kV/mm | 2540 kV/in | IEC 243/1 | ||
| Dissipation Factor | 0.0025 @Frequency 100 Hz | 0.0025 @Frequency 100 Hz | IEC 60250 | ||
| 0.017 @Frequency 1.00e+6 Hz | 0.017 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Comparative Tracking Index | 125 V | 125 V | Test Solution B; IEC 112 | ||
| 375 V | 375 V | Test solution A; IEC 60112 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 2.00 - 3.00 µm/m-°C @Temperature 23.0 - 80.0 °C | 1.11 - 1.67 µin/in-°F @Temperature 73.4 - 176 °F | DIN 53752 | ||
| Specific Heat Capacity | 1.50 J/g-°C | 0.359 BTU/lb-°F | IEC 1006 | ||
| Thermal Conductivity | 0.270 W/m-K | 1.87 BTU-in/hr-ft²-°F | DIN 52612 | ||
| Melting Point | 220 - 225 °C | 428 - 437 °F | ISO 11357-3 | ||
| Maximum Service Temperature, Air | 140 °C | 284 °F | at 50% loss of tensile strength after 20000h; IEC 216-1 | ||
| 160 °C | 320 °F | at 50% loss of tensile strength after 5000h; IEC 216-1 | |||
| 210 °C | 410 °F | ||||
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | ISO 75 | ||
| Flammability, UL94 | HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | |||
| HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | ||||
| Flame Spread Index | <= 100 | <= 100 | [mm/min]; DIN 75200 | ||
| Glow Wire Test | <= 750 °C @Thickness 3.00 mm | <= 1380 °F @Thickness 0.118 in | IEC 695 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 260 °C | 500 °F | |||
| 250 - 275 °C | 482 - 527 °F | Injection molding | |||
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | |||
| 80.0 °C | 176 °F | ||||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | North America and Europe | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| NSF Std. 61 | Yes | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| Special characteristic | Heat stabilized or stable to heat | ||||
| Light stabilized or stable to light | |||||
| Lubricant | |||||
| Release agent | |||||
| U.V. stabilized or stable to weather | |||||