- 熔体流动速率 [g/10min]: 32.34
- 密度 [g/cm3]: 1.47
- 吸水率 [%]: 0.4
- 拉伸强度 [MPa]: 120.0
- 热变形温度 [℃]: 215.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.600 - 0.900 g/cc | 0.0217 - 0.0325 lb/in³ | |||
| Density | 1.47 g/cc | 0.0531 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.40 % | 0.40 % | Saturation; DIN 53495/1L | ||
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C; 50% RH | ||
| Viscosity Measurement | 105 | 105 | [ml/g]; Viscosity number; ISO 1628 | ||
| 70 @Temperature 290 °C | 70 @Temperature 554 °F | 20 mins plasticating | |||
| 75 @Temperature 280 °C | 75 @Temperature 536 °F | 30 mins plasticating | |||
| 75 @Temperature 300 °C | 75 @Temperature 572 °F | 10 mins plasticating | |||
| 90 @Temperature 270 °C | 90 @Temperature 518 °F | 30 mins plasticating | |||
| 95 @Temperature 290 °C | 95 @Temperature 554 °F | 10 mins plasticating | |||
| 100 @Temperature 300 °C | 100 @Temperature 572 °F | 5 mins plasticating | |||
| 100 @Temperature 260 °C | 100 @Temperature 500 °F | 30 mins plasticating | |||
| 105 @Temperature 280 °C | 105 @Temperature 536 °F | 10 mins plasticating | |||
| 106 @Temperature 250 °C | 106 @Temperature 482 °F | 30 mins plasticating | |||
| 110 @Temperature 270 °C | 110 @Temperature 518 °F | 10 mins plasticating | |||
| 115 @Temperature 260 °C | 115 @Temperature 500 °F | 10 mins plasticating | |||
| 115 @Temperature 240 °C | 115 @Temperature 464 °F | 30 mins plasticating | |||
| 117 @Temperature 250 °C | 117 @Temperature 482 °F | 10 mins plasticating | |||
| 120 @Temperature 240 °C | 120 @Temperature 464 °F | 10 mins plasticating | |||
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm | 0.0020 in/in | Sheet | ||
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm | 0.011 in/in | Sheet | ||
| Melt Flow | 32.34 g/10 min @Load 2.16 kg, Temperature 275 °C | 32.34 g/10 min @Load 4.76 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 190 MPa @Load 36.5 kg, Time 30.0 sec | 27600 psi @Load 80.5 lb, Time 0.00833 hour | ISO 2039-1 | ||
| Tensile Strength, Yield | 120 MPa | 17400 psi | 50 mm/min; ISO 527-2 | ||
| Elongation at Yield | 2.5 % | 2.5 % | 50 mm/min; ISO 527-2 | ||
| Modulus of Elasticity | 7.50 GPa | 1090 ksi | ISO 527-2 | ||
| Charpy Impact Unnotched | 4.00 J/cm² | 19.0 ft-lb/in² | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | ISO 179/1eA | ||
| Dart Drop, Total Energy | 5.00 J | 3.69 ft-lb | W501 housing; ISO 6603-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 7.00e+13 ohm-cm | 7.00e+13 ohm-cm | IEC 93 | ||
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 93 | ||
| Dielectric Constant | 3.5 @Frequency 1.00e+6 Hz | 3.5 @Frequency 1.00e+6 Hz | IEC 250 | ||
| 3.7 @Frequency 100 Hz | 3.7 @Frequency 100 Hz | IEC 250 | |||
| Dielectric Strength | 18.0 kV/mm | 457 kV/in | IEC 243/1 | ||
| Dissipation Factor | 0.0014 @Frequency 100 Hz | 0.0014 @Frequency 100 Hz | IEC 250 | ||
| 0.018 @Frequency 1.00e+6 Hz | 0.018 @Frequency 1.00e+6 Hz | IEC 250 | |||
| Comparative Tracking Index | 300 V | 300 V | Test solution A; IEC 112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 2.00 - 3.00 µm/m-°C @Temperature 23.0 - 80.0 °C | 1.11 - 1.67 µin/in-°F @Temperature 73.4 - 176 °F | DIN 53752 | ||
| Specific Heat Capacity | 1.70 J/g-°C | 0.406 BTU/lb-°F | IEC 1006 | ||
| Melting Point | 220 - 250 °C | 428 - 482 °F | DSC; ISO 11357-3 | ||
| Maximum Service Temperature, Air | 140 °C | 284 °F | at 50% loss of tensile strength after 20000h; IEC 216-1 | ||
| 140 °C | 284 °F | at 50% loss of tensile strength after 5000h; IEC 216-1 | |||
| 210 °C | 410 °F | ||||
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ISO 75-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 180 °C | 356 °F | ISO 75-2 | ||
| Decomposition Temperature | >= 290 °C | >= 554 °F | |||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |||
| HB @Diameter 0.800 mm | HB @Diameter 0.0315 in | ||||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 80.0 °C | 176 °F | Hopper Throat | ||
| Zone 1 | 260 °C | 500 °F | Feeding zone | ||
| Zone 2 | 265 °C | 509 °F | Compression | ||
| Zone 3 | 270 °C | 518 °F | Metering-zone | ||
| Zone 4 | 270 °C | 518 °F | Nozzle | ||
| Melt Temperature | 250 - 280 °C | 482 - 536 °F | Injection-molding | ||
| 270 °C | 518 °F | for shrinkage test, Optimal | |||
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | Injection molding | ||
| 80.0 °C | 176 °F | for shrinkage test, Optimal | |||
| Drying Temperature | 80.0 - 120 °C | 176 - 248 °F | |||
| Dry Time | 4 hour | 4 hour | |||
| Descriptive Properties | |||||
| Color | Natural, Colored, Black and Special Colors | ||||
| Commercial Status | Europe | ||||
| Ignition Temperature | 350°C | ASTM D1929 | |||
| Peripheral Screw Speed | < 0.25 m/s | ||||
| Primary Processing Technique | Injection Molding | ||||