- 熔体流动速率 [g/10min]: 9.59
- 密度 [g/cm3]: 1.37
- 吸水率 [%]: 0.4
- 拉伸强度 [MPa]: 70.0
- 热变形温度 [℃]: 200.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.40 % | 0.40 % | Saturation; DIN 53495/1L | ||
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C; 50% RH | ||
| Viscosity Measurement | 135 | 135 | [ml/g]; Viscosity number; ISO 1628 | ||
| Linear Mold Shrinkage, Flow | 0.0070 cm/cm | 0.0070 in/in | Sheet | ||
| Linear Mold Shrinkage, Transverse | 0.0075 cm/cm | 0.0075 in/in | Sheet | ||
| Melt Flow | 9.59 g/10 min @Load 2.16 kg, Temperature 275 °C | 9.59 g/10 min @Load 4.76 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 70.0 MPa | 10200 psi | 50 mm/min; ISO 527-2 | ||
| Elongation at Break | 2.9 % | 2.9 % | 50mm/min; ISO 527-2 | ||
| Modulus of Elasticity | 5.90 GPa | 856 ksi | ISO 527-2 | ||
| Flexural Strength | 115 MPa | 16700 psi | ISO 178 | ||
| Charpy Impact Unnotched | 3.50 J/cm² | 16.7 ft-lb/in² | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 93 | ||
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | IEC 93 | ||
| Dielectric Constant | 4.1 @Frequency 1.00e+6 Hz | 4.1 @Frequency 1.00e+6 Hz | IEC 250 | ||
| Dissipation Factor | 0.028 @Frequency 1.00e+6 Hz | 0.028 @Frequency 1.00e+6 Hz | IEC 250 | ||
| Comparative Tracking Index | 250 V | 250 V | Test solution A; IEC 112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 5.00 µm/m-°C @Temperature 23.0 - 80.0 °C | 2.78 µin/in-°F @Temperature 73.4 - 176 °F | DIN 53752 | ||
| Melting Point | 220 - 225 °C | 428 - 437 °F | DSC; ISO 11357-3 | ||
| Maximum Service Temperature, Air | 170 °C | 338 °F | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | ISO 75-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 115 °C | 239 °F | ISO 75-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 250 - 275 °C | 482 - 527 °F | Injection-molding | ||
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | |||
| Descriptive Properties | |||||
| Color | Black | ||||
| Commercial Status | Europe | ||||
| Primary Processing Technique | Injection Molding | ||||