- 熔体流动速率 [g/10min]: 65.0
- 密度 [g/cm3]: 1.3
- 拉伸强度 [MPa]: 53.0
- 热变形温度 [℃]: 140.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.600 - 0.900 g/cc | 0.0217 - 0.0325 lb/in³ | |||
| Density | 1.30 g/cc | 0.0470 lb/in³ | ISO 1183 | ||
| Viscosity Measurement | 115 | 115 | [cm3/g]; ISO 307 | ||
| Linear Mold Shrinkage, Flow | 0.018 cm/cm | 0.018 in/in | ISO 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.019 cm/cm | 0.019 in/in | ISO 2577 | ||
| Melt Flow | 65 g/10 min @Load 2.16 kg, Temperature 250 °C | 65 g/10 min @Load 4.76 lb, Temperature 482 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 53.0 MPa | 7690 psi | 50 mm/min; ISO 527-1/-2 | ||
| Elongation at Yield | 8.0 % | 8.0 % | 50 mm/min; ISO 527-1/-2 | ||
| >= 50 % | >= 50 % | Nominal Strain, 50 mm/min; ISO 527-1/-2 | |||
| Tensile Modulus | 2.20 GPa | 319 ksi | ISO 527-1/-2 | ||
| Flexural Strength | 75.0 MPa | 10900 psi | ISO 178 | ||
| Charpy Impact Unnotched | NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.400 J/cm² @Temperature 23.0 °C | 1.90 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 223 °C | 433 °F | ISO 11357-1/-2 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 140 °C | 284 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ISO 75-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 80.0 °C | 176 °F | Hopper Throat | ||
| Zone 1 | 260 °C | 500 °F | Feeding zone | ||
| Zone 2 | 260 °C | 500 °F | Compression | ||
| Zone 3 | 260 °C | 500 °F | Metering-zone | ||
| Zone 4 | 260 °C | 500 °F | Nozzle | ||
| Melt Temperature | 260 °C | 500 °F | Optimal | ||
| 250 - 275 °C | 482 - 527 °F | Injection molding/Extrusion | |||
| Mold Temperature | 40.0 - 70.0 °C | 104 - 158 °F | Injection molding | ||
| 60.0 °C | 140 °F | Optimal | |||
| Drying Temperature | 80.0 - 120 °C | 176 - 248 °F | |||
| Dry Time | 4 hour | 4 hour | |||
| Descriptive Properties | |||||
| Commercial Status | Europe | ||||
| Ignition Temperature | 350°C | ASTM D1929 | |||
| Peripheral Screw Speed | < 0.25 m/s | ||||