- 吸水率 [%]: 0.08
- 缺口冲击强度: 0.534
- 拉伸强度 [MPa]: 55.2
- 断裂伸长率 [%]: 75.8
- 弯曲模量 [MPa]: 2.28
- 热变形温度 [℃]: 154.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.31 g/cc | 1.31 g/cc | ASTM D792 |
| Water Absorption | 0.080 % @Time 86400 sec | 0.080 % @Time 24.0 hour | ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 55.2 MPa | 8000 psi | ASTM D638 |
| Elongation at Break | 50 % | 50 % | ASTM D638 |
| Flexural Yield Strength | 75.8 MPa | 11000 psi | ASTM D790 |
| Flexural Modulus | 2.28 GPa | 330 ksi | ASTM D790 |
| Izod Impact, Notched | 0.534 J/cm @Temperature 22.8 °C | 1.00 ft-lb/in @Temperature 73.0 °F | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 154 °C | 310 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 67.2 °C | 153 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 232 - 254 °C | 450 - 490 °F | |
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |
| Dry Time | 2 - 4 hour @Temperature 71.1 °C | 2 - 4 hour @Temperature 160 °F | to eliminate surface defects |
| Injection Pressure | 4.96 - 8.27 MPa | 720 - 1200 psi | Secondary |
| 8.27 - 13.8 MPa | 1200 - 2000 psi | Initial | |
| Back Pressure | 0.345 - 1.72 MPa | 50.0 - 250 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Screw Speed | 20 - 100 rpm | 20 - 100 rpm | |