- 熔体流动速率 [g/10min]: 30.0
- 缺口冲击强度: 7.56
- 拉伸强度 [MPa]: 62.0
- 弯曲模量 [MPa]: 2.068
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.22 g/cc | 1.22 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0060 - 0.0090 cm/cm | 0.0060 - 0.0090 in/in | ASTM D955 |
| Melt Flow | 30 g/10 min @Load 5.00 kg, Temperature 265 °C | 30 g/10 min @Load 11.0 lb, Temperature 509 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 62.0 MPa | 8990 psi | chs 2.0 in/min; ASTM D638 |
| Flexural Modulus | 2.068 GPa | 299.9 ksi | chs 0.05 in/min; ASTM D790 |
| Izod Impact, Notched | 7.56 J/cm @Thickness 3.17 mm | 14.2 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 133 °C @Load 1.00 kg, Thickness 3.17 mm | 271 °F @Load 2.20 lb, Thickness 0.125 in | ASTM D1527 |