- 熔体流动速率 [g/10min]: 59.04
- 密度 [g/cm3]: 1.44
- 吸水率 [%]: 0.45
- 拉伸强度 [MPa]: 65.0
- 热变形温度 [℃]: 165.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.44 g/cc | 0.0520 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.45 % | 0.45 % | Sim. to ISO 62 | ||
| Moisture Absorption at Equilibrium | 0.18 % | 0.18 % | Humidity Absorption; Sim. to ISO 62 | ||
| Melt Flow | 59.04 g/10 min @Load 2.16 kg, Temperature 250 °C | 59.04 g/10 min @Load 4.76 lb, Temperature 482 °F | Calculated from Volume Flow Rate of 41 cm3/10min.; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 65.0 MPa | 9430 psi | ISO 527-1/-2 | ||
| Elongation at Break | 5.5 % | 5.5 % | ISO 527-1/-2 | ||
| Elongation at Yield | 5.0 % | 5.0 % | ISO 527-1/-2 | ||
| Tensile Modulus | 3.20 GPa | 464 ksi | ISO 527-1/-2 | ||
| Charpy Impact Unnotched | NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.500 J/cm² @Temperature 23.0 °C | 2.38 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 | ||
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 | ||
| Comparative Tracking Index | 175 - 249 V | 175 - 249 V | PLC 3; UL 746A | ||
| 225 V | 225 V | IEC 60112 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 70.0 µm/m-°C @Temperature 20.0 °C | 38.9 µin/in-°F @Temperature 68.0 °F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C @Temperature 20.0 °C | 38.9 µin/in-°F @Temperature 68.0 °F | ISO 11359-1/-2 | ||
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | ISO 75-1/-2 | ||
| UL RTI, Electrical | 75.0 °C @Thickness 0.750 mm | 167 °F @Thickness 0.0295 in | UL746B | ||
| 75.0 °C @Thickness 3.00 mm | 167 °F @Thickness 0.118 in | UL746B | |||
| UL RTI, Mechanical with Impact | 75.0 °C @Thickness 0.750 mm | 167 °F @Thickness 0.0295 in | UL746B | ||
| 75.0 °C @Thickness 3.00 mm | 167 °F @Thickness 0.118 in | UL746B | |||
| UL RTI, Mechanical without Impact | 75.0 °C @Thickness 0.750 mm | 167 °F @Thickness 0.0295 in | UL746B | ||
| 75.0 °C @Thickness 3.00 mm | 167 °F @Thickness 0.118 in | UL746B | |||
| Flammability, UL94 | V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | IEC 60695-11-10 | ||
| V-0 @Thickness 0.750 mm | V-0 @Thickness 0.0295 in | IEC 60695-11-10 | |||
| Descriptive Properties | |||||
| Flame Retardant | Yes | ||||
| Flame Retarding Agent | Yes | ||||
| Injection Molding | Yes | ||||
| Release Agent | Yes | ||||
| Without Fillers | Yes | ||||