- 熔体流动速率 [g/10min]: 22.56
- 密度 [g/cm3]: 1.41
- 吸水率 [%]: 0.3
- 热变形温度 [℃]: 215.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.30 % | 0.30 % | Sim. to ISO 62 | ||
| Moisture Absorption at Equilibrium | 0.15 % | 0.15 % | Humidity Absorption; Sim. to ISO 62 | ||
| Melt Flow | 22.56 g/10 min @Load 2.16 kg, Temperature 250 °C | 22.56 g/10 min @Load 4.76 lb, Temperature 482 °F | Calculated from Volume Flow Rate of 16 cm3/10min.; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 95.0 MPa | 13800 psi | ISO 527-1/-2 | ||
| Elongation at Break | 2.5 % | 2.5 % | ISO 527-1/-2 | ||
| Tensile Modulus | 7.00 GPa | 1020 ksi | ISO 527-1/-2 | ||
| Charpy Impact Unnotched | 4.00 J/cm² @Temperature -30.0 °C | 19.0 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | ||
| 4.00 J/cm² @Temperature 23.0 °C | 19.0 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.600 J/cm² @Temperature -30.0 °C | 2.86 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | ||
| 0.600 J/cm² @Temperature 23.0 °C | 2.86 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 | ||
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 | ||
| Dielectric Constant | 3.5 @Frequency 1e+6 Hz | 3.5 @Frequency 1e+6 Hz | IEC 60250 | ||
| 3.7 @Frequency 100 Hz | 3.7 @Frequency 100 Hz | IEC 60250 | |||
| Dielectric Strength | 28.0 kV/mm | 711 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.0025 @Frequency 100 Hz | 0.0025 @Frequency 100 Hz | IEC 60250 | ||
| 0.014 @Frequency 1e+6 Hz | 0.014 @Frequency 1e+6 Hz | IEC 60250 | |||
| Comparative Tracking Index | 250 V | 250 V | IEC 60112 | ||
| 250 - 399 V | 250 - 399 V | PLC 2; UL 746A | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 40.0 µm/m-°C @Temperature 20.0 °C | 22.2 µin/in-°F @Temperature 68.0 °F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C @Temperature 20.0 °C | 44.4 µin/in-°F @Temperature 68.0 °F | ISO 11359-1/-2 | ||
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ISO 75-1/-2 | ||
| UL RTI, Electrical | 130 °C @Thickness 1.50 mm | 266 °F @Thickness 0.0591 in | UL746B | ||
| 130 °C @Thickness 0.750 mm | 266 °F @Thickness 0.0295 in | UL746B | |||
| UL RTI, Mechanical with Impact | 140 °C @Thickness 0.750 mm | 284 °F @Thickness 0.0295 in | UL746B | ||
| 140 °C @Thickness 1.50 mm | 284 °F @Thickness 0.0591 in | UL746B | |||
| UL RTI, Mechanical without Impact | 130 °C @Thickness 1.50 mm | 266 °F @Thickness 0.0591 in | UL746B | ||
| 130 °C @Thickness 0.750 mm | 266 °F @Thickness 0.0295 in | UL746B | |||
| Flammability, UL94 | V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | IEC 60695-11-10 | ||
| V-0 @Thickness 0.750 mm | V-0 @Thickness 0.0295 in | IEC 60695-11-10 | |||
| 5VB @Thickness 1.50 mm | 5VB @Thickness 0.0591 in | IEC 60695-11-20 | |||
| Glow Wire Test | 725 °C @Thickness 1.50 mm | 1340 °F @Thickness 0.0591 in | Glow Wire Ignition Temperature; IEC 60695-2-13 | ||
| 800 °C @Thickness 0.750 mm | 1470 °F @Thickness 0.0295 in | Glow Wire Ignition Temperature; IEC 60695-2-13 | |||
| 960 °C @Thickness 1.50 mm | 1760 °F @Thickness 0.0591 in | Glow Wire Flammability Index; IEC 60695-2-12 | |||
| 960 °C @Thickness 0.750 mm | 1760 °F @Thickness 0.0295 in | Glow Wire Flammability Index; IEC 60695-2-12 | |||
| Descriptive Properties | |||||
| Flame Retardant | Yes | ||||
| Flame Retarding Agent | Yes | ||||
| Injection Molding | Yes | ||||
| Release Agent | Yes | ||||
| With Fillers | Yes | ||||