  4. DuPont Performance Polymers Crastin® LW9020 BK580 PBT

DuPont Performance Polymers Crastin® LW9020 BK580 PBT

DuPont Performance Polymers Crastin® LW9020 BK580 PBT 物性表: DuPont Performance Polymers Crastin® LW9020 BK580 PBT物性表及特性介绍,DuPont Performance Polymers Crastin® LW9020 BK580 PBT注塑参数详情,如需DuPont Performance Polymers Crastin® LW9020 BK580 PBT下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.35
  • 缺口冲击强度: 7.0
  • 弯曲模量 [MPa]: 6.20
  • 热变形温度 [℃]: 205.0
 
Physical PropertiesMetricEnglishComments
Density 1.35 g/cc0.0488 lb/in³ISO 1183
Filler Content 20 %20 %
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break 108 MPa
@Temperature 23.0 °C		15700 psi
@Temperature 73.4 °F		ISO 527
Tensile Stress  4.94 MPa
@Strain 0.100 %,
Temperature 100 °C		716 psi
@Strain 0.100 %,
Temperature 212 °F		ISO 11403-1/-2
 5.79 MPa
@Strain 0.100 %,
Temperature 80.0 °C		840 psi
@Strain 0.100 %,
Temperature 176 °F		ISO 11403-1/-2
 7.48 MPa
@Strain 0.100 %,
Temperature 23.0 °C		1080 psi
@Strain 0.100 %,
Temperature 73.4 °F		ISO 11403-1/-2
 7.83 MPa
@Strain 0.100 %,
Temperature -40.0 °C		1140 psi
@Strain 0.100 %,
Temperature -40.0 °F		ISO 11403-1/-2
 9.64 MPa
@Strain 0.200 %,
Temperature 100 °C		1400 psi
@Strain 0.200 %,
Temperature 212 °F		ISO 11403-1/-2
 11.32 MPa
@Strain 0.200 %,
Temperature 80.0 °C		1642 psi
@Strain 0.200 %,
Temperature 176 °F		ISO 11403-1/-2
 13.88 MPa
@Strain 0.300 %,
Temperature 100 °C		2013 psi
@Strain 0.300 %,
Temperature 212 °F		ISO 11403-1/-2
 14.99 MPa
@Strain 0.200 %,
Temperature 23.0 °C		2174 psi
@Strain 0.200 %,
Temperature 73.4 °F		ISO 11403-1/-2
 15.87 MPa
@Strain 0.300 %,
Temperature 80.0 °C		2302 psi
@Strain 0.300 %,
Temperature 176 °F		ISO 11403-1/-2
 16.12 MPa
@Strain 0.200 %,
Temperature -40.0 °C		2338 psi
@Strain 0.200 %,
Temperature -40.0 °F		ISO 11403-1/-2
 17.11 MPa
@Strain 0.400 %,
Temperature 100 °C		2482 psi
@Strain 0.400 %,
Temperature 212 °F		ISO 11403-1/-2
 19.57 MPa
@Strain 0.400 %,
Temperature 80.0 °C		2838 psi
@Strain 0.400 %,
Temperature 176 °F		ISO 11403-1/-2
 21.64 MPa
@Strain 0.500 %,
Temperature 100 °C		3139 psi
@Strain 0.500 %,
Temperature 212 °F		ISO 11403-1/-2
 22.4 MPa
@Strain 0.300 %,
Temperature 23.0 °C		3250 psi
@Strain 0.300 %,
Temperature 73.4 °F		ISO 11403-1/-2
 24.26 MPa
@Strain 0.500 %,
Temperature 80.0 °C		3519 psi
@Strain 0.500 %,
Temperature 176 °F		ISO 11403-1/-2
 24.27 MPa
@Strain 0.300 %,
Temperature -40.0 °C		3520 psi
@Strain 0.300 %,
Temperature -40.0 °F		ISO 11403-1/-2
 25.01 MPa
@Strain 0.600 %,
Temperature 100 °C		3627 psi
@Strain 0.600 %,
Temperature 212 °F		ISO 11403-1/-2
 27.88 MPa
@Strain 0.700 %,
Temperature 100 °C		4044 psi
@Strain 0.700 %,
Temperature 212 °F		ISO 11403-1/-2
 28.05 MPa
@Strain 0.600 %,
Temperature 80.0 °C		4068 psi
@Strain 0.600 %,
Temperature 176 °F		ISO 11403-1/-2
 28.34 MPa
@Strain 0.400 %,
Temperature 23.0 °C		4110 psi
@Strain 0.400 %,
Temperature 73.4 °F		ISO 11403-1/-2
 30.46 MPa
@Strain 0.800 %,
Temperature 100 °C		4418 psi
@Strain 0.800 %,
Temperature 212 °F		ISO 11403-1/-2
 30.92 MPa
@Strain 0.400 %,
Temperature -40.0 °C		4485 psi
@Strain 0.400 %,
Temperature -40.0 °F		ISO 11403-1/-2
 31.44 MPa
@Strain 0.700 %,
Temperature 80.0 °C		4560 psi
@Strain 0.700 %,
Temperature 176 °F		ISO 11403-1/-2
 32.81 MPa
@Strain 0.900 %,
Temperature 100 °C		4759 psi
@Strain 0.900 %,
Temperature 212 °F		ISO 11403-1/-2
 34.48 MPa
@Strain 0.800 %,
Temperature 80.0 °C		5001 psi
@Strain 0.800 %,
Temperature 176 °F		ISO 11403-1/-2
 34.78 MPa
@Strain 1.00 %,
Temperature 100 °C		5044 psi
@Strain 1.00 %,
Temperature 212 °F		ISO 11403-1/-2
 36.47 MPa
@Strain 0.500 %,
Temperature 23.0 °C		5290 psi
@Strain 0.500 %,
Temperature 73.4 °F		ISO 11403-1/-2
 36.51 MPa
@Strain 1.10 %,
Temperature 100 °C		5295 psi
@Strain 1.10 %,
Temperature 212 °F		ISO 11403-1/-2
 36.99 MPa
@Strain 0.900 %,
Temperature 80.0 °C		5365 psi
@Strain 0.900 %,
Temperature 176 °F		ISO 11403-1/-2
 37.93 MPa
@Strain 1.20 %,
Temperature 100 °C		5501 psi
@Strain 1.20 %,
Temperature 212 °F		ISO 11403-1/-2
 39.06 MPa
@Strain 1.30 %,
Temperature 100 °C		5665 psi
@Strain 1.30 %,
Temperature 212 °F		ISO 11403-1/-2
 39.42 MPa
@Strain 1.00 %,
Temperature 80.0 °C		5717 psi
@Strain 1.00 %,
Temperature 176 °F		ISO 11403-1/-2
 40.16 MPa
@Strain 0.500 %,
Temperature -40.0 °C		5825 psi
@Strain 0.500 %,
Temperature -40.0 °F		ISO 11403-1/-2
 40.17 MPa
@Strain 1.40 %,
Temperature 100 °C		5826 psi
@Strain 1.40 %,
Temperature 212 °F		ISO 11403-1/-2
 41.38 MPa
@Strain 1.50 %,
Temperature 100 °C		6002 psi
@Strain 1.50 %,
Temperature 212 °F		ISO 11403-1/-2
 41.72 MPa
@Strain 1.10 %,
Temperature 80.0 °C		6051 psi
@Strain 1.10 %,
Temperature 176 °F		ISO 11403-1/-2
 42.43 MPa
@Strain 1.60 %,
Temperature 100 °C		6154 psi
@Strain 1.60 %,
Temperature 212 °F		ISO 11403-1/-2
 43.12 MPa
@Strain 0.600 %,
Temperature 23.0 °C		6254 psi
@Strain 0.600 %,
Temperature 73.4 °F		ISO 11403-1/-2
 43.34 MPa
@Strain 1.70 %,
Temperature 100 °C		6286 psi
@Strain 1.70 %,
Temperature 212 °F		ISO 11403-1/-2
 43.74 MPa
@Strain 1.20 %,
Temperature 80.0 °C		6344 psi
@Strain 1.20 %,
Temperature 176 °F		ISO 11403-1/-2
 44.2 MPa
@Strain 1.80 %,
Temperature 100 °C		6410 psi
@Strain 1.80 %,
Temperature 212 °F		ISO 11403-1/-2
 44.92 MPa
@Strain 1.90 %,
Temperature 100 °C		6515 psi
@Strain 1.90 %,
Temperature 212 °F		ISO 11403-1/-2
 45.58 MPa
@Strain 1.30 %,
Temperature 80.0 °C		6611 psi
@Strain 1.30 %,
Temperature 176 °F		ISO 11403-1/-2
 45.61 MPa
@Strain 2.00 %,
Temperature 100 °C		6615 psi
@Strain 2.00 %,
Temperature 212 °F		ISO 11403-1/-2
 46.23 MPa
@Strain 2.10 %,
Temperature 100 °C		6705 psi
@Strain 2.10 %,
Temperature 212 °F		ISO 11403-1/-2
 46.75 MPa
@Strain 2.20 %,
Temperature 100 °C		6781 psi
@Strain 2.20 %,
Temperature 212 °F		ISO 11403-1/-2
 47.28 MPa
@Strain 1.40 %,
Temperature 80.0 °C		6857 psi
@Strain 1.40 %,
Temperature 176 °F		ISO 11403-1/-2
 47.3 MPa
@Strain 2.30 %,
Temperature 100 °C		6860 psi
@Strain 2.30 %,
Temperature 212 °F		ISO 11403-1/-2
 47.71 MPa
@Strain 2.40 %,
Temperature 100 °C		6920 psi
@Strain 2.40 %,
Temperature 212 °F		ISO 11403-1/-2
 48.19 MPa
@Strain 2.50 %,
Temperature 100 °C		6989 psi
@Strain 2.50 %,
Temperature 212 °F		ISO 11403-1/-2
 48.56 MPa
@Strain 0.600 %,
Temperature -40.0 °C		7043 psi
@Strain 0.600 %,
Temperature -40.0 °F		ISO 11403-1/-2
 48.61 MPa
@Strain 2.60 %,
Temperature 100 °C		7050 psi
@Strain 2.60 %,
Temperature 212 °F		ISO 11403-1/-2
 48.79 MPa
@Strain 1.50 %,
Temperature 80.0 °C		7076 psi
@Strain 1.50 %,
Temperature 176 °F		ISO 11403-1/-2
 48.95 MPa
@Strain 2.70 %,
Temperature 100 °C		7100 psi
@Strain 2.70 %,
Temperature 212 °F		ISO 11403-1/-2
 49.31 MPa
@Strain 2.80 %,
Temperature 100 °C		7152 psi
@Strain 2.80 %,
Temperature 212 °F		ISO 11403-1/-2
 49.44 MPa
@Strain 0.700 %,
Temperature 23.0 °C		7171 psi
@Strain 0.700 %,
Temperature 73.4 °F		ISO 11403-1/-2
 49.57 MPa
@Strain 2.90 %,
Temperature 100 °C		7190 psi
@Strain 2.90 %,
Temperature 212 °F		ISO 11403-1/-2
 49.83 MPa
@Strain 3.00 %,
Temperature 100 °C		7227 psi
@Strain 3.00 %,
Temperature 212 °F		ISO 11403-1/-2
 49.98 MPa
@Strain 3.10 %,
Temperature 100 °C		7249 psi
@Strain 3.10 %,
Temperature 212 °F		ISO 11403-1/-2
 50.13 MPa
@Strain 1.60 %,
Temperature 80.0 °C		7271 psi
@Strain 1.60 %,
Temperature 176 °F		ISO 11403-1/-2
 50.2 MPa
@Strain 3.20 %,
Temperature 100 °C		7280 psi
@Strain 3.20 %,
Temperature 212 °F		ISO 11403-1/-2
 50.32 MPa
@Strain 3.30 %,
Temperature 100 °C		7298 psi
@Strain 3.30 %,
Temperature 212 °F		ISO 11403-1/-2
 50.49 MPa
@Strain 3.40 %,
Temperature 100 °C		7323 psi
@Strain 3.40 %,
Temperature 212 °F		ISO 11403-1/-2
 50.62 MPa
@Strain 3.50 %,
Temperature 100 °C		7342 psi
@Strain 3.50 %,
Temperature 212 °F		ISO 11403-1/-2
 50.67 MPa
@Strain 4.30 %,
Temperature 100 °C		7349 psi
@Strain 4.30 %,
Temperature 212 °F		ISO 11403-1/-2
 50.74 MPa
@Strain 3.60 %,
Temperature 100 °C		7359 psi
@Strain 3.60 %,
Temperature 212 °F		ISO 11403-1/-2
 50.87 MPa
@Strain 3.70 %,
Temperature 100 °C		7378 psi
@Strain 3.70 %,
Temperature 212 °F		ISO 11403-1/-2
 50.93 MPa
@Strain 3.80 %,
Temperature 100 °C		7387 psi
@Strain 3.80 %,
Temperature 212 °F		ISO 11403-1/-2
 51.03 MPa
@Strain 4.20 %,
Temperature 100 °C		7401 psi
@Strain 4.20 %,
Temperature 212 °F		ISO 11403-1/-2
 51.04 MPa
@Strain 3.90 %,
Temperature 100 °C		7403 psi
@Strain 3.90 %,
Temperature 212 °F		ISO 11403-1/-2
 51.09 MPa
@Strain 4.00 %,
Temperature 100 °C		7410 psi
@Strain 4.00 %,
Temperature 212 °F		ISO 11403-1/-2
 51.1 MPa
@Strain 4.10 %,
Temperature 100 °C		7410 psi
@Strain 4.10 %,
Temperature 212 °F		ISO 11403-1/-2
 51.35 MPa
@Strain 1.70 %,
Temperature 80.0 °C		7448 psi
@Strain 1.70 %,
Temperature 176 °F		ISO 11403-1/-2
 52.45 MPa
@Strain 1.80 %,
Temperature 80.0 °C		7607 psi
@Strain 1.80 %,
Temperature 176 °F		ISO 11403-1/-2
 53.42 MPa
@Strain 1.90 %,
Temperature 80.0 °C		7748 psi
@Strain 1.90 %,
Temperature 176 °F		ISO 11403-1/-2
 54.33 MPa
@Strain 2.00 %,
Temperature 80.0 °C		7880 psi
@Strain 2.00 %,
Temperature 176 °F		ISO 11403-1/-2
 55.14 MPa
@Strain 2.10 %,
Temperature 80.0 °C		7997 psi
@Strain 2.10 %,
Temperature 176 °F		ISO 11403-1/-2
 55.22 MPa
@Strain 0.800 %,
Temperature 23.0 °C		8009 psi
@Strain 0.800 %,
Temperature 73.4 °F		ISO 11403-1/-2
 55.86 MPa
@Strain 2.20 %,
Temperature 80.0 °C		8102 psi
@Strain 2.20 %,
Temperature 176 °F		ISO 11403-1/-2
 56.23 MPa
@Strain 0.700 %,
Temperature -40.0 °C		8155 psi
@Strain 0.700 %,
Temperature -40.0 °F		ISO 11403-1/-2
 56.51 MPa
@Strain 2.30 %,
Temperature 80.0 °C		8196 psi
@Strain 2.30 %,
Temperature 176 °F		ISO 11403-1/-2
 57.1 MPa
@Strain 2.40 %,
Temperature 80.0 °C		8280 psi
@Strain 2.40 %,
Temperature 176 °F		ISO 11403-1/-2
 57.64 MPa
@Strain 2.50 %,
Temperature 80.0 °C		8360 psi
@Strain 2.50 %,
Temperature 176 °F		ISO 11403-1/-2
 58.11 MPa
@Strain 2.60 %,
Temperature 80.0 °C		8428 psi
@Strain 2.60 %,
Temperature 176 °F		ISO 11403-1/-2
 58.53 MPa
@Strain 2.70 %,
Temperature 80.0 °C		8489 psi
@Strain 2.70 %,
Temperature 176 °F		ISO 11403-1/-2
 58.94 MPa
@Strain 2.80 %,
Temperature 80.0 °C		8549 psi
@Strain 2.80 %,
Temperature 176 °F		ISO 11403-1/-2
 59.24 MPa
@Strain 2.90 %,
Temperature 80.0 °C		8592 psi
@Strain 2.90 %,
Temperature 176 °F		ISO 11403-1/-2
 59.54 MPa
@Strain 3.00 %,
Temperature 80.0 °C		8636 psi
@Strain 3.00 %,
Temperature 176 °F		ISO 11403-1/-2
 59.74 MPa
@Strain 3.10 %,
Temperature 80.0 °C		8665 psi
@Strain 3.10 %,
Temperature 176 °F		ISO 11403-1/-2
 60.01 MPa
@Strain 3.20 %,
Temperature 80.0 °C		8704 psi
@Strain 3.20 %,
Temperature 176 °F		ISO 11403-1/-2
 60.16 MPa
@Strain 3.30 %,
Temperature 80.0 °C		8725 psi
@Strain 3.30 %,
Temperature 176 °F		ISO 11403-1/-2
 60.36 MPa
@Strain 3.40 %,
Temperature 80.0 °C		8754 psi
@Strain 3.40 %,
Temperature 176 °F		ISO 11403-1/-2
 60.48 MPa
@Strain 3.50 %,
Temperature 80.0 °C		8772 psi
@Strain 3.50 %,
Temperature 176 °F		ISO 11403-1/-2
 60.63 MPa
@Strain 3.60 %,
Temperature 80.0 °C		8794 psi
@Strain 3.60 %,
Temperature 176 °F		ISO 11403-1/-2
 60.71 MPa
@Strain 3.70 %,
Temperature 80.0 °C		8805 psi
@Strain 3.70 %,
Temperature 176 °F		ISO 11403-1/-2
 60.72 MPa
@Strain 3.80 %,
Temperature 80.0 °C		8807 psi
@Strain 3.80 %,
Temperature 176 °F		ISO 11403-1/-2
 60.82 MPa
@Strain 0.900 %,
Temperature 23.0 °C		8821 psi
@Strain 0.900 %,
Temperature 73.4 °F		ISO 11403-1/-2
 63.69 MPa
@Strain 0.800 %,
Temperature -40.0 °C		9237 psi
@Strain 0.800 %,
Temperature -40.0 °F		ISO 11403-1/-2
 66.06 MPa
@Strain 1.00 %,
Temperature 23.0 °C		9581 psi
@Strain 1.00 %,
Temperature 73.4 °F		ISO 11403-1/-2
 70.91 MPa
@Strain 1.10 %,
Temperature 23.0 °C		10280 psi
@Strain 1.10 %,
Temperature 73.4 °F		ISO 11403-1/-2
 70.95 MPa
@Strain 0.900 %,
Temperature -40.0 °C		10290 psi
@Strain 0.900 %,
Temperature -40.0 °F		ISO 11403-1/-2
 75.41 MPa
@Strain 1.20 %,
Temperature 23.0 °C		10940 psi
@Strain 1.20 %,
Temperature 73.4 °F		ISO 11403-1/-2
 77.98 MPa
@Strain 1.00 %,
Temperature -40.0 °C		11310 psi
@Strain 1.00 %,
Temperature -40.0 °F		ISO 11403-1/-2
 79.59 MPa
@Strain 1.30 %,
Temperature 23.0 °C		11540 psi
@Strain 1.30 %,
Temperature 73.4 °F		ISO 11403-1/-2
 83.43 MPa
@Strain 1.40 %,
Temperature 23.0 °C		12100 psi
@Strain 1.40 %,
Temperature 73.4 °F		ISO 11403-1/-2
 84.9 MPa
@Strain 1.10 %,
Temperature -40.0 °C		12300 psi
@Strain 1.10 %,
Temperature -40.0 °F		ISO 11403-1/-2
 87.02 MPa
@Strain 1.50 %,
Temperature 23.0 °C		12620 psi
@Strain 1.50 %,
Temperature 73.4 °F		ISO 11403-1/-2
 91.62 MPa
@Strain 1.60 %,
Temperature 23.0 °C		13290 psi
@Strain 1.60 %,
Temperature 73.4 °F		ISO 11403-1/-2
 91.63 MPa
@Strain 1.20 %,
Temperature -40.0 °C		13290 psi
@Strain 1.20 %,
Temperature -40.0 °F		ISO 11403-1/-2
 94.8 MPa
@Strain 1.70 %,
Temperature 23.0 °C		13700 psi
@Strain 1.70 %,
Temperature 73.4 °F		ISO 11403-1/-2
 97.8 MPa
@Strain 1.80 %,
Temperature 23.0 °C		14200 psi
@Strain 1.80 %,
Temperature 73.4 °F		ISO 11403-1/-2
 97.97 MPa
@Strain 1.30 %,
Temperature -40.0 °C		14210 psi
@Strain 1.30 %,
Temperature -40.0 °F		ISO 11403-1/-2
 100.5 MPa
@Strain 1.90 %,
Temperature 23.0 °C		14580 psi
@Strain 1.90 %,
Temperature 73.4 °F		ISO 11403-1/-2
 102.6 MPa
@Strain 2.00 %,
Temperature 23.0 °C		14880 psi
@Strain 2.00 %,
Temperature 73.4 °F		ISO 11403-1/-2
 104.01 MPa
@Strain 1.40 %,
Temperature -40.0 °C		15085 psi
@Strain 1.40 %,
Temperature -40.0 °F		ISO 11403-1/-2
 104.22 MPa
@Strain 2.10 %,
Temperature 23.0 °C		15116 psi
@Strain 2.10 %,
Temperature 73.4 °F		ISO 11403-1/-2
 105.6 MPa
@Strain 2.20 %,
Temperature 23.0 °C		15320 psi
@Strain 2.20 %,
Temperature 73.4 °F		ISO 11403-1/-2
 106.9 MPa
@Strain 2.30 %,
Temperature 23.0 °C		15500 psi
@Strain 2.30 %,
Temperature 73.4 °F		ISO 11403-1/-2
 107.8 MPa
@Strain 2.40 %,
Temperature 23.0 °C		15640 psi
@Strain 2.40 %,
Temperature 73.4 °F		ISO 11403-1/-2
 108 MPa
@Strain 2.50 %,
Temperature 23.0 °C		15700 psi
@Strain 2.50 %,
Temperature 73.4 °F		ISO 11403-1/-2
 109.84 MPa
@Strain 1.50 %,
Temperature -40.0 °C		15931 psi
@Strain 1.50 %,
Temperature -40.0 °F		ISO 11403-1/-2
 115.64 MPa
@Strain 1.60 %,
Temperature -40.0 °C		16772 psi
@Strain 1.60 %,
Temperature -40.0 °F		ISO 11403-1/-2
 121.14 MPa
@Strain 1.70 %,
Temperature -40.0 °C		17570 psi
@Strain 1.70 %,
Temperature -40.0 °F		ISO 11403-1/-2
 126.32 MPa
@Strain 1.80 %,
Temperature -40.0 °C		18321 psi
@Strain 1.80 %,
Temperature -40.0 °F		ISO 11403-1/-2
 131.15 MPa
@Strain 1.90 %,
Temperature -40.0 °C		19022 psi
@Strain 1.90 %,
Temperature -40.0 °F		ISO 11403-1/-2
 135.83 MPa
@Strain 2.00 %,
Temperature -40.0 °C		19701 psi
@Strain 2.00 %,
Temperature -40.0 °F		ISO 11403-1/-2
 140.25 MPa
@Strain 2.10 %,
Temperature -40.0 °C		20342 psi
@Strain 2.10 %,
Temperature -40.0 °F		ISO 11403-1/-2
Elongation at Break 2.5 %
@Temperature 23.0 °C		2.5 %
@Temperature 73.4 °F		ISO 527
Tensile Modulus 7.00 GPa
@Temperature 23.0 °C		1020 ksi
@Temperature 73.4 °F		ISO 527
Flexural Strength 160 MPa
@Temperature 23.0 °C		23200 psi
@Temperature 73.4 °F		ISO 178
Flexural Modulus 6.20 GPa
@Temperature 23.0 °C		899 ksi
@Temperature 73.4 °F		ISO 178
Izod Impact, Notched (ISO) 7.00 kJ/m²
@Temperature 23.0 °C		3.33 ft-lb/in²
@Temperature 73.4 °F		ISO 180/1A
Charpy Impact Unnotched 5.00 J/cm²
@Temperature 23.0 °C		23.8 ft-lb/in²
@Temperature 73.4 °F		ISO 179/1eU
Charpy Impact, Notched 0.700 J/cm²
@Temperature 23.0 °C		3.33 ft-lb/in²
@Temperature 73.4 °F		ISO 179/1eA
 
Thermal PropertiesMetricEnglishComments
Deflection Temperature at 0.46 MPa (66 psi) 205 °C401 °FISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 150 °C302 °FISO 75-1/-2
UL RTI, Electrical  130 °C
@Thickness 0.750 mm		266 °F
@Thickness 0.0295 in		UL 746B
 130 °C
@Thickness 1.50 mm		266 °F
@Thickness 0.0591 in		UL 746B
 130 °C
@Thickness 3.00 mm		266 °F
@Thickness 0.118 in		UL 746B
UL RTI, Mechanical with Impact  125 °C
@Thickness 0.750 mm		257 °F
@Thickness 0.0295 in		UL 746B
 125 °C
@Thickness 1.50 mm		257 °F
@Thickness 0.0591 in		UL 746B
 130 °C
@Thickness 3.00 mm		266 °F
@Thickness 0.118 in		UL 746B
UL RTI, Mechanical without Impact  130 °C
@Thickness 0.750 mm		266 °F
@Thickness 0.0295 in		UL 746B
 130 °C
@Thickness 1.50 mm		266 °F
@Thickness 0.0591 in		UL 746B
 130 °C
@Thickness 3.00 mm		266 °F
@Thickness 0.118 in		UL 746B
Flammability, UL94  HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		UL94
 HB
@Thickness 6.00 mm		HB
@Thickness 0.236 in		UL94
 HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		UL94
 HB
@Thickness 6.00 mm		HB
@Thickness 0.236 in		IEC 60695-11-10
 HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		IEC 60695-11-10
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		IEC 60695-11-10
 
Processing PropertiesMetricEnglishComments
Melt Temperature 225 °C437 °F10°C/min; ISO 11357-1/-3
 240 - 260 °C464 - 500 °F
 250 °C482 °FOptimum
Mold Temperature 30.0 - 130 °C86.0 - 266 °F
 80.0 °C176 °Foptimum
Drying Temperature 110 - 130 °C230 - 266 °F
Dry Time 2.00 - 4.00 hour2.00 - 4.00 hour
Moisture Content <= 0.040 %<= 0.040 %
 
Descriptive Properties
AdditiveLubricant
AppearanceBlack Color
Drying RecommendedYes
FeaturesAppearance, Pleasing Surface
 Chemical Resistance, Good
 Dimensional Stability, Good
 Moisture Absorption, Low
 Processability, Good
 Warp Resistant
 Warpage, Low
FillerGlass fiber reinforcement
FormsPellets
GenericPBT Alloy
Material StatusCurrent
Part Marking Code>PBT+ASA-GF20<ISO 11469
Polymer FamilyPolyester
Polymer TypePBT
Processing MethodInjection Molding
Product CategoryGlass Reinforced Resins
 Low Warp Resins
Region Available - GlobalYes
Resin IdentificationPBT+ASA-GF20ISO 1043
RoHS ComplianceContact Manufacturer
UsesAutomotive Applications
 Housings
 Industrial Applications

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-38072.html

免责声明: 本文 DuPont Performance Polymers Crastin® LW9020 BK580 PBT 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4