塑胶原料之家
  1. 首页
  2. 英文物性
  3. PBT
  4. DuPont Performance Polymers Crastin® ST820 NC010 PBT

DuPont Performance Polymers Crastin® ST820 NC010 PBT

DuPont Performance Polymers Crastin® ST820 NC010 PBT 物性表: DuPont Performance Polymers Crastin® ST820 NC010 PBT物性表及特性介绍,DuPont Performance Polymers Crastin® ST820 NC010 PBT注塑参数详情,如需DuPont Performance Polymers Crastin® ST820 NC010 PBT下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.22
  • 吸水率 [%]: 0.12
  • 缺口冲击强度: 1.17
  • 拉伸强度 [MPa]: 38.0
  • 弯曲模量 [MPa]: 0.137
  • 硬度: 98.0
  • 热变形温度 [℃]: 100.0
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.23 g/cc1.23 g/ccASTM D792
Density 1.22 g/cc0.0441 lb/in³ISO 1183
Water Absorption  0.12 %
@Temperature 23.0 °C		0.12 %
@Temperature 73.4 °F		Equilibrium 50%RH; ISO 62, Similar to
 0.31 %
@Temperature 23.0 °C		0.31 %
@Temperature 73.4 °F		Saturation, immersed; ISO 62, Similar to
Linear Mold Shrinkage 0.022 cm/cm0.022 in/inFlow
 0.030 cm/cm0.030 in/inTransverse
Linear Mold Shrinkage, Flow 0.025 cm/cm0.025 in/inParallel; Annealed; ISO 294-4
 0.019 cm/cm
@Thickness 2.00 mm		0.019 in/in
@Thickness 0.0787 in		Parallel; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0225 cm/cm0.0225 in/inNormal; Annealed; ISO 294-4
 0.018 cm/cm
@Thickness 2.00 mm		0.018 in/in
@Thickness 0.0787 in		Normal; ISO 294-4
Melt Index of Compound 5.0 g/10 min5.0 g/10 mincm3/10 min; ISO 1133
 
Mechanical PropertiesMetricEnglishComments
Hardness, Rockwell R 9898ASTM D785
 104104ISO 2039/2
Tensile Strength at Break  21.0 MPa
@Temperature 100 °C		3050 psi
@Temperature 212 °F		ISO 527
 71.0 MPa
@Temperature -40.0 °C		10300 psi
@Temperature -40.0 °F		ISO 527
Tensile Strength  21.0 MPa
@Temperature 149 °C		3050 psi
@Temperature 300 °F		ASTM D638
 28.0 MPa
@Temperature 90.0 °C		4060 psi
@Temperature 194 °F		ASTM D638
 37.0 MPa
@Temperature 23.0 °C		5370 psi
@Temperature 73.4 °F		ASTM D638
 68.0 MPa
@Temperature -40.0 °C		9860 psi
@Temperature -40.0 °F		ASTM D638
Tensile Stress  0.310 MPa
@Strain 0.200 %,
Temperature 150 °C		45.0 psi
@Strain 0.200 %,
Temperature 302 °F		ISO 11403-1/-2
 0.320 MPa
@Strain 0.100 %,
Temperature 150 °C		46.4 psi
@Strain 0.100 %,
Temperature 302 °F		ISO 11403-1/-2
 0.500 MPa
@Strain 0.100 %,
Temperature 80.0 °C		72.5 psi
@Strain 0.100 %,
Temperature 176 °F		ISO 11403-1/-2
 0.550 MPa
@Strain 0.200 %,
Temperature 100 °C		79.8 psi
@Strain 0.200 %,
Temperature 212 °F		ISO 11403-1/-2
 0.590 MPa
@Strain 0.100 %,
Temperature 120 °C		85.6 psi
@Strain 0.100 %,
Temperature 248 °F		ISO 11403-1/-2
 0.600 MPa
@Strain 0.300 %,
Temperature 150 °C		87.0 psi
@Strain 0.300 %,
Temperature 302 °F		ISO 11403-1/-2
 0.630 MPa
@Strain 0.200 %,
Temperature 80.0 °C		91.4 psi
@Strain 0.200 %,
Temperature 176 °F		ISO 11403-1/-2
 0.680 MPa
@Strain 0.100 %,
Temperature 60.0 °C		98.6 psi
@Strain 0.100 %,
Temperature 140 °F		ISO 11403-1/-2
 0.730 MPa
@Strain 0.200 %,
Temperature 120 °C		106 psi
@Strain 0.200 %,
Temperature 248 °F		ISO 11403-1/-2
 0.760 MPa
@Strain 0.400 %,
Temperature 150 °C		110 psi
@Strain 0.400 %,
Temperature 302 °F		ISO 11403-1/-2
 0.860 MPa
@Strain 0.300 %,
Temperature 100 °C		125 psi
@Strain 0.300 %,
Temperature 212 °F		ISO 11403-1/-2
 0.870 MPa
@Strain 0.300 %,
Temperature 120 °C		126 psi
@Strain 0.300 %,
Temperature 248 °F		ISO 11403-1/-2
 0.870 MPa
@Strain 0.300 %,
Temperature 80.0 °C		126 psi
@Strain 0.300 %,
Temperature 176 °F		ISO 11403-1/-2
 0.890 MPa
@Strain 0.500 %,
Temperature 150 °C		129 psi
@Strain 0.500 %,
Temperature 302 °F		ISO 11403-1/-2
 1.00 MPa
@Strain 0.400 %,
Temperature 120 °C		145 psi
@Strain 0.400 %,
Temperature 248 °F		ISO 11403-1/-2
 1.04 MPa
@Strain 0.600 %,
Temperature 150 °C		151 psi
@Strain 0.600 %,
Temperature 302 °F		ISO 11403-1/-2
 1.04 MPa
@Strain 0.400 %,
Temperature 100 °C		151 psi
@Strain 0.400 %,
Temperature 212 °F		ISO 11403-1/-2
 1.10 MPa
@Strain 0.200 %,
Temperature 60.0 °C		160 psi
@Strain 0.200 %,
Temperature 140 °F		ISO 11403-1/-2
 1.15 MPa
@Strain 0.400 %,
Temperature 80.0 °C		167 psi
@Strain 0.400 %,
Temperature 176 °F		ISO 11403-1/-2
 1.18 MPa
@Strain 0.700 %,
Temperature 150 °C		171 psi
@Strain 0.700 %,
Temperature 302 °F		ISO 11403-1/-2
 1.18 MPa
@Strain 0.500 %,
Temperature 120 °C		171 psi
@Strain 0.500 %,
Temperature 248 °F		ISO 11403-1/-2
 1.25 MPa
@Strain 0.500 %,
Temperature 100 °C		181 psi
@Strain 0.500 %,
Temperature 212 °F		ISO 11403-1/-2
 1.26 MPa
@Strain 0.800 %,
Temperature 150 °C		183 psi
@Strain 0.800 %,
Temperature 302 °F		ISO 11403-1/-2
 1.36 MPa
@Strain 0.600 %,
Temperature 120 °C		197 psi
@Strain 0.600 %,
Temperature 248 °F		ISO 11403-1/-2
 1.38 MPa
@Strain 0.500 %,
Temperature 80.0 °C		200 psi
@Strain 0.500 %,
Temperature 176 °F		ISO 11403-1/-2
 1.39 MPa
@Strain 0.900 %,
Temperature 150 °C		202 psi
@Strain 0.900 %,
Temperature 302 °F		ISO 11403-1/-2
 1.42 MPa
@Strain 0.300 %,
Temperature 60.0 °C		206 psi
@Strain 0.300 %,
Temperature 140 °F		ISO 11403-1/-2
 1.49 MPa
@Strain 0.700 %,
Temperature 120 °C		216 psi
@Strain 0.700 %,
Temperature 248 °F		ISO 11403-1/-2
 1.53 MPa
@Strain 1.00 %,
Temperature 150 °C		222 psi
@Strain 1.00 %,
Temperature 302 °F		ISO 11403-1/-2
 1.53 MPa
@Strain 0.600 %,
Temperature 100 °C		222 psi
@Strain 0.600 %,
Temperature 212 °F		ISO 11403-1/-2
 1.61 MPa
@Strain 1.10 %,
Temperature 150 °C		234 psi
@Strain 1.10 %,
Temperature 302 °F		ISO 11403-1/-2
 1.61 MPa
@Strain 0.600 %,
Temperature 80.0 °C		234 psi
@Strain 0.600 %,
Temperature 176 °F		ISO 11403-1/-2
 1.66 MPa
@Strain 0.800 %,
Temperature 120 °C		241 psi
@Strain 0.800 %,
Temperature 248 °F		ISO 11403-1/-2
 1.72 MPa
@Strain 0.700 %,
Temperature 100 °C		249 psi
@Strain 0.700 %,
Temperature 212 °F		ISO 11403-1/-2
 1.73 MPa
@Strain 1.20 %,
Temperature 150 °C		251 psi
@Strain 1.20 %,
Temperature 302 °F		ISO 11403-1/-2
 1.82 MPa
@Strain 0.400 %,
Temperature 60.0 °C		264 psi
@Strain 0.400 %,
Temperature 140 °F		ISO 11403-1/-2
 1.86 MPa
@Strain 0.900 %,
Temperature 120 °C		270 psi
@Strain 0.900 %,
Temperature 248 °F		ISO 11403-1/-2
 1.87 MPa
@Strain 1.30 %,
Temperature 150 °C		271 psi
@Strain 1.30 %,
Temperature 302 °F		ISO 11403-1/-2
 1.87 MPa
@Strain 0.700 %,
Temperature 80.0 °C		271 psi
@Strain 0.700 %,
Temperature 176 °F		ISO 11403-1/-2
 1.93 MPa
@Strain 0.800 %,
Temperature 100 °C		280 psi
@Strain 0.800 %,
Temperature 212 °F		ISO 11403-1/-2
 1.98 MPa
@Strain 1.00 %,
Temperature 120 °C		287 psi
@Strain 1.00 %,
Temperature 248 °F		ISO 11403-1/-2
 1.99 MPa
@Strain 1.40 %,
Temperature 150 °C		289 psi
@Strain 1.40 %,
Temperature 302 °F		ISO 11403-1/-2
 2.10 MPa
@Strain 1.50 %,
Temperature 150 °C		305 psi
@Strain 1.50 %,
Temperature 302 °F		ISO 11403-1/-2
 2.13 MPa
@Strain 0.100 %,
Temperature -40.0 °C		309 psi
@Strain 0.100 %,
Temperature -40.0 °F		ISO 11403-1/-2
 2.15 MPa
@Strain 0.800 %,
Temperature 80.0 °C		312 psi
@Strain 0.800 %,
Temperature 176 °F		ISO 11403-1/-2
 2.16 MPa
@Strain 0.900 %,
Temperature 100 °C		313 psi
@Strain 0.900 %,
Temperature 212 °F		ISO 11403-1/-2
 2.21 MPa
@Strain 1.10 %,
Temperature 120 °C		321 psi
@Strain 1.10 %,
Temperature 248 °F		ISO 11403-1/-2
 2.24 MPa
@Strain 1.60 %,
Temperature 150 °C		325 psi
@Strain 1.60 %,
Temperature 302 °F		ISO 11403-1/-2
 2.25 MPa
@Strain 0.500 %,
Temperature 60.0 °C		326 psi
@Strain 0.500 %,
Temperature 140 °F		ISO 11403-1/-2
 2.33 MPa
@Strain 1.70 %,
Temperature 150 °C		338 psi
@Strain 1.70 %,
Temperature 302 °F		ISO 11403-1/-2
 2.34 MPa
@Strain 1.00 %,
Temperature 100 °C		339 psi
@Strain 1.00 %,
Temperature 212 °F		ISO 11403-1/-2
 2.38 MPa
@Strain 1.20 %,
Temperature 120 °C		345 psi
@Strain 1.20 %,
Temperature 248 °F		ISO 11403-1/-2
 2.41 MPa
@Strain 0.900 %,
Temperature 80.0 °C		350 psi
@Strain 0.900 %,
Temperature 176 °F		ISO 11403-1/-2
 2.44 MPa
@Strain 1.80 %,
Temperature 150 °C		354 psi
@Strain 1.80 %,
Temperature 302 °F		ISO 11403-1/-2
 2.50 MPa
@Strain 1.30 %,
Temperature 120 °C		363 psi
@Strain 1.30 %,
Temperature 248 °F		ISO 11403-1/-2
 2.56 MPa
@Strain 1.10 %,
Temperature 100 °C		371 psi
@Strain 1.10 %,
Temperature 212 °F		ISO 11403-1/-2
 2.58 MPa
@Strain 1.90 %,
Temperature 150 °C		374 psi
@Strain 1.90 %,
Temperature 302 °F		ISO 11403-1/-2
 2.63 MPa
@Strain 1.00 %,
Temperature 80.0 °C		381 psi
@Strain 1.00 %,
Temperature 176 °F		ISO 11403-1/-2
 2.67 MPa
@Strain 2.00 %,
Temperature 150 °C		387 psi
@Strain 2.00 %,
Temperature 302 °F		ISO 11403-1/-2
 2.69 MPa
@Strain 1.40 %,
Temperature 120 °C		390 psi
@Strain 1.40 %,
Temperature 248 °F		ISO 11403-1/-2
 2.71 MPa
@Strain 0.600 %,
Temperature 60.0 °C		393 psi
@Strain 0.600 %,
Temperature 140 °F		ISO 11403-1/-2
 2.75 MPa
@Strain 2.10 %,
Temperature 150 °C		399 psi
@Strain 2.10 %,
Temperature 302 °F		ISO 11403-1/-2
 2.77 MPa
@Strain 1.20 %,
Temperature 100 °C		402 psi
@Strain 1.20 %,
Temperature 212 °F		ISO 11403-1/-2
 2.84 MPa
@Strain 1.50 %,
Temperature 120 °C		412 psi
@Strain 1.50 %,
Temperature 248 °F		ISO 11403-1/-2
 2.88 MPa
@Strain 2.20 %,
Temperature 150 °C		418 psi
@Strain 2.20 %,
Temperature 302 °F		ISO 11403-1/-2
 2.92 MPa
@Strain 1.10 %,
Temperature 80.0 °C		424 psi
@Strain 1.10 %,
Temperature 176 °F		ISO 11403-1/-2
 2.94 MPa
@Strain 1.60 %,
Temperature 120 °C		426 psi
@Strain 1.60 %,
Temperature 248 °F		ISO 11403-1/-2
 3.00 MPa
@Strain 1.30 %,
Temperature 100 °C		435 psi
@Strain 1.30 %,
Temperature 212 °F		ISO 11403-1/-2
 3.01 MPa
@Strain 2.30 %,
Temperature 150 °C		437 psi
@Strain 2.30 %,
Temperature 302 °F		ISO 11403-1/-2
 3.04 MPa
@Strain 0.700 %,
Temperature 60.0 °C		441 psi
@Strain 0.700 %,
Temperature 140 °F		ISO 11403-1/-2
 3.09 MPa
@Strain 2.40 %,
Temperature 150 °C		448 psi
@Strain 2.40 %,
Temperature 302 °F		ISO 11403-1/-2
 3.13 MPa
@Strain 1.70 %,
Temperature 120 °C		454 psi
@Strain 1.70 %,
Temperature 248 °F		ISO 11403-1/-2
 3.14 MPa
@Strain 1.40 %,
Temperature 100 °C		455 psi
@Strain 1.40 %,
Temperature 212 °F		ISO 11403-1/-2
 3.16 MPa
@Strain 1.20 %,
Temperature 80.0 °C		458 psi
@Strain 1.20 %,
Temperature 176 °F		ISO 11403-1/-2
 3.19 MPa
@Strain 0.200 %,
Temperature 23.0 °C		463 psi
@Strain 0.200 %,
Temperature 73.4 °F		ISO 11403-1/-2
 3.22 MPa
@Strain 2.50 %,
Temperature 150 °C		467 psi
@Strain 2.50 %,
Temperature 302 °F		ISO 11403-1/-2
 3.30 MPa
@Strain 2.60 %,
Temperature 150 °C		479 psi
@Strain 2.60 %,
Temperature 302 °F		ISO 11403-1/-2
 3.31 MPa
@Strain 1.80 %,
Temperature 120 °C		480 psi
@Strain 1.80 %,
Temperature 248 °F		ISO 11403-1/-2
 3.34 MPa
@Strain 1.30 %,
Temperature 80.0 °C		484 psi
@Strain 1.30 %,
Temperature 176 °F		ISO 11403-1/-2
 3.34 MPa
@Strain 0.800 %,
Temperature 60.0 °C		484 psi
@Strain 0.800 %,
Temperature 140 °F		ISO 11403-1/-2
 3.40 MPa
@Strain 1.50 %,
Temperature 100 °C		493 psi
@Strain 1.50 %,
Temperature 212 °F		ISO 11403-1/-2
 3.40 MPa
@Strain 2.70 %,
Temperature 150 °C		493 psi
@Strain 2.70 %,
Temperature 302 °F		ISO 11403-1/-2
 3.44 MPa
@Strain 1.90 %,
Temperature 120 °C		499 psi
@Strain 1.90 %,
Temperature 248 °F		ISO 11403-1/-2
 3.51 MPa
@Strain 2.80 %,
Temperature 150 °C		509 psi
@Strain 2.80 %,
Temperature 302 °F		ISO 11403-1/-2
 3.59 MPa
@Strain 1.60 %,
Temperature 100 °C		521 psi
@Strain 1.60 %,
Temperature 212 °F		ISO 11403-1/-2
 3.60 MPa
@Strain 2.90 %,
Temperature 150 °C		522 psi
@Strain 2.90 %,
Temperature 302 °F		ISO 11403-1/-2
 3.63 MPa
@Strain 2.00 %,
Temperature 120 °C		526 psi
@Strain 2.00 %,
Temperature 248 °F		ISO 11403-1/-2
 3.66 MPa
@Strain 1.40 %,
Temperature 80.0 °C		531 psi
@Strain 1.40 %,
Temperature 176 °F		ISO 11403-1/-2
 3.71 MPa
@Strain 3.00 %,
Temperature 150 °C		538 psi
@Strain 3.00 %,
Temperature 302 °F		ISO 11403-1/-2
 3.74 MPa
@Strain 1.70 %,
Temperature 100 °C		542 psi
@Strain 1.70 %,
Temperature 212 °F		ISO 11403-1/-2
 3.74 MPa
@Strain 0.200 %,
Temperature 0.000 °C		542 psi
@Strain 0.200 %,
Temperature 32.0 °F		ISO 11403-1/-2
 3.75 MPa
@Strain 2.10 %,
Temperature 120 °C		544 psi
@Strain 2.10 %,
Temperature 248 °F		ISO 11403-1/-2
 3.79 MPa
@Strain 0.900 %,
Temperature 60.0 °C		550 psi
@Strain 0.900 %,
Temperature 140 °F		ISO 11403-1/-2
 3.81 MPa
@Strain 3.10 %,
Temperature 150 °C		553 psi
@Strain 3.10 %,
Temperature 302 °F		ISO 11403-1/-2
 3.85 MPa
@Strain 1.50 %,
Temperature 80.0 °C		558 psi
@Strain 1.50 %,
Temperature 176 °F		ISO 11403-1/-2
 3.87 MPa
@Strain 2.20 %,
Temperature 120 °C		561 psi
@Strain 2.20 %,
Temperature 248 °F		ISO 11403-1/-2
 3.89 MPa
@Strain 3.20 %,
Temperature 150 °C		564 psi
@Strain 3.20 %,
Temperature 302 °F		ISO 11403-1/-2
 3.96 MPa
@Strain 3.30 %,
Temperature 150 °C		574 psi
@Strain 3.30 %,
Temperature 302 °F		ISO 11403-1/-2
 3.99 MPa
@Strain 1.80 %,
Temperature 100 °C		579 psi
@Strain 1.80 %,
Temperature 212 °F		ISO 11403-1/-2
 4.05 MPa
@Strain 1.60 %,
Temperature 80.0 °C		587 psi
@Strain 1.60 %,
Temperature 176 °F		ISO 11403-1/-2
 4.06 MPa
@Strain 3.40 %,
Temperature 150 °C		589 psi
@Strain 3.40 %,
Temperature 302 °F		ISO 11403-1/-2
 4.08 MPa
@Strain 0.200 %,
Temperature -40.0 °C		592 psi
@Strain 0.200 %,
Temperature -40.0 °F		ISO 11403-1/-2
 4.09 MPa
@Strain 2.30 %,
Temperature 120 °C		593 psi
@Strain 2.30 %,
Temperature 248 °F		ISO 11403-1/-2
 4.12 MPa
@Strain 1.90 %,
Temperature 100 °C		598 psi
@Strain 1.90 %,
Temperature 212 °F		ISO 11403-1/-2
 4.14 MPa
@Strain 3.50 %,
Temperature 150 °C		600 psi
@Strain 3.50 %,
Temperature 302 °F		ISO 11403-1/-2
 4.16 MPa
@Strain 1.00 %,
Temperature 60.0 °C		603 psi
@Strain 1.00 %,
Temperature 140 °F		ISO 11403-1/-2
 4.18 MPa
@Strain 2.40 %,
Temperature 120 °C		606 psi
@Strain 2.40 %,
Temperature 248 °F		ISO 11403-1/-2
 4.22 MPa
@Strain 3.60 %,
Temperature 150 °C		612 psi
@Strain 3.60 %,
Temperature 302 °F		ISO 11403-1/-2
 4.28 MPa
@Strain 2.00 %,
Temperature 100 °C		621 psi
@Strain 2.00 %,
Temperature 212 °F		ISO 11403-1/-2
 4.33 MPa
@Strain 2.50 %,
Temperature 120 °C		628 psi
@Strain 2.50 %,
Temperature 248 °F		ISO 11403-1/-2
 4.34 MPa
@Strain 3.70 %,
Temperature 150 °C		629 psi
@Strain 3.70 %,
Temperature 302 °F		ISO 11403-1/-2
 4.35 MPa
@Strain 1.70 %,
Temperature 80.0 °C		631 psi
@Strain 1.70 %,
Temperature 176 °F		ISO 11403-1/-2
 4.45 MPa
@Strain 3.80 %,
Temperature 150 °C		645 psi
@Strain 3.80 %,
Temperature 302 °F		ISO 11403-1/-2
 4.50 MPa
@Strain 2.60 %,
Temperature 120 °C		653 psi
@Strain 2.60 %,
Temperature 248 °F		ISO 11403-1/-2
 4.50 MPa
@Strain 2.10 %,
Temperature 100 °C		653 psi
@Strain 2.10 %,
Temperature 212 °F		ISO 11403-1/-2
 4.50 MPa
@Strain 1.10 %,
Temperature 60.0 °C		653 psi
@Strain 1.10 %,
Temperature 140 °F		ISO 11403-1/-2
 4.51 MPa
@Strain 3.90 %,
Temperature 150 °C		654 psi
@Strain 3.90 %,
Temperature 302 °F		ISO 11403-1/-2
 4.52 MPa
@Strain 1.80 %,
Temperature 80.0 °C		656 psi
@Strain 1.80 %,
Temperature 176 °F		ISO 11403-1/-2
 4.58 MPa
@Strain 2.70 %,
Temperature 120 °C		664 psi
@Strain 2.70 %,
Temperature 248 °F		ISO 11403-1/-2
 4.59 MPa
@Strain 4.00 %,
Temperature 150 °C		666 psi
@Strain 4.00 %,
Temperature 302 °F		ISO 11403-1/-2
 4.64 MPa
@Strain 2.20 %,
Temperature 100 °C		673 psi
@Strain 2.20 %,
Temperature 212 °F		ISO 11403-1/-2
 4.67 MPa
@Strain 4.10 %,
Temperature 150 °C		677 psi
@Strain 4.10 %,
Temperature 302 °F		ISO 11403-1/-2
 4.69 MPa
@Strain 0.300 %,
Temperature 23.0 °C		680 psi
@Strain 0.300 %,
Temperature 73.4 °F		ISO 11403-1/-2
 4.73 MPa
@Strain 4.20 %,
Temperature 150 °C		686 psi
@Strain 4.20 %,
Temperature 302 °F		ISO 11403-1/-2
 4.74 MPa
@Strain 1.90 %,
Temperature 80.0 °C		687 psi
@Strain 1.90 %,
Temperature 176 °F		ISO 11403-1/-2
 4.76 MPa
@Strain 1.20 %,
Temperature 60.0 °C		690 psi
@Strain 1.20 %,
Temperature 140 °F		ISO 11403-1/-2
 4.79 MPa
@Strain 2.80 %,
Temperature 120 °C		695 psi
@Strain 2.80 %,
Temperature 248 °F		ISO 11403-1/-2
 4.80 MPa
@Strain 4.30 %,
Temperature 150 °C		696 psi
@Strain 4.30 %,
Temperature 302 °F		ISO 11403-1/-2
 4.83 MPa
@Strain 2.30 %,
Temperature 100 °C		701 psi
@Strain 2.30 %,
Temperature 212 °F		ISO 11403-1/-2
 4.89 MPa
@Strain 4.40 %,
Temperature 150 °C		709 psi
@Strain 4.40 %,
Temperature 302 °F		ISO 11403-1/-2
 4.90 MPa
@Strain 2.90 %,
Temperature 120 °C		711 psi
@Strain 2.90 %,
Temperature 248 °F		ISO 11403-1/-2
 4.95 MPa
@Strain 4.50 %,
Temperature 150 °C		718 psi
@Strain 4.50 %,
Temperature 302 °F		ISO 11403-1/-2
 4.98 MPa
@Strain 2.00 %,
Temperature 80.0 °C		722 psi
@Strain 2.00 %,
Temperature 176 °F		ISO 11403-1/-2
 5.00 MPa
@Strain 3.00 %,
Temperature 120 °C		725 psi
@Strain 3.00 %,
Temperature 248 °F		ISO 11403-1/-2
 5.02 MPa
@Strain 2.40 %,
Temperature 100 °C		728 psi
@Strain 2.40 %,
Temperature 212 °F		ISO 11403-1/-2
 5.03 MPa
@Strain 4.60 %,
Temperature 150 °C		730 psi
@Strain 4.60 %,
Temperature 302 °F		ISO 11403-1/-2
 5.11 MPa
@Strain 4.70 %,
Temperature 150 °C		741 psi
@Strain 4.70 %,
Temperature 302 °F		ISO 11403-1/-2
 5.13 MPa
@Strain 1.30 %,
Temperature 60.0 °C		744 psi
@Strain 1.30 %,
Temperature 140 °F		ISO 11403-1/-2
 5.14 MPa
@Strain 2.10 %,
Temperature 80.0 °C		745 psi
@Strain 2.10 %,
Temperature 176 °F		ISO 11403-1/-2
 5.16 MPa
@Strain 3.10 %,
Temperature 120 °C		748 psi
@Strain 3.10 %,
Temperature 248 °F		ISO 11403-1/-2
 5.16 MPa
@Strain 4.80 %,
Temperature 150 °C		748 psi
@Strain 4.80 %,
Temperature 302 °F		ISO 11403-1/-2
 5.17 MPa
@Strain 2.50 %,
Temperature 100 °C		750 psi
@Strain 2.50 %,
Temperature 212 °F		ISO 11403-1/-2
 5.22 MPa
@Strain 4.90 %,
Temperature 150 °C		757 psi
@Strain 4.90 %,
Temperature 302 °F		ISO 11403-1/-2
 5.27 MPa
@Strain 3.20 %,
Temperature 120 °C		764 psi
@Strain 3.20 %,
Temperature 248 °F		ISO 11403-1/-2
 5.29 MPa
@Strain 5.00 %,
Temperature 150 °C		767 psi
@Strain 5.00 %,
Temperature 302 °F		ISO 11403-1/-2
 5.34 MPa
@Strain 2.60 %,
Temperature 100 °C		775 psi
@Strain 2.60 %,
Temperature 212 °F		ISO 11403-1/-2
 5.34 MPa
@Strain 0.300 %,
Temperature 0.000 °C		775 psi
@Strain 0.300 %,
Temperature 32.0 °F		ISO 11403-1/-2
 5.35 MPa
@Strain 2.20 %,
Temperature 80.0 °C		776 psi
@Strain 2.20 %,
Temperature 176 °F		ISO 11403-1/-2
 5.41 MPa
@Strain 3.30 %,
Temperature 120 °C		785 psi
@Strain 3.30 %,
Temperature 248 °F		ISO 11403-1/-2
 5.46 MPa
@Strain 1.40 %,
Temperature 60.0 °C		792 psi
@Strain 1.40 %,
Temperature 140 °F		ISO 11403-1/-2
 5.50 MPa
@Strain 2.70 %,
Temperature 100 °C		798 psi
@Strain 2.70 %,
Temperature 212 °F		ISO 11403-1/-2
 5.56 MPa
@Strain 2.30 %,
Temperature 80.0 °C		806 psi
@Strain 2.30 %,
Temperature 176 °F		ISO 11403-1/-2
 5.56 MPa
@Strain 3.40 %,
Temperature 120 °C		806 psi
@Strain 3.40 %,
Temperature 248 °F		ISO 11403-1/-2
 5.64 MPa
@Strain 3.50 %,
Temperature 120 °C		818 psi
@Strain 3.50 %,
Temperature 248 °F		ISO 11403-1/-2
 5.66 MPa
@Strain 2.80 %,
Temperature 100 °C		821 psi
@Strain 2.80 %,
Temperature 212 °F		ISO 11403-1/-2
 5.74 MPa
@Strain 3.60 %,
Temperature 120 °C		833 psi
@Strain 3.60 %,
Temperature 248 °F		ISO 11403-1/-2
 5.76 MPa
@Strain 6.00 %,
Temperature 150 °C		835 psi
@Strain 6.00 %,
Temperature 302 °F		ISO 11403-1/-2
 5.78 MPa
@Strain 2.90 %,
Temperature 100 °C		838 psi
@Strain 2.90 %,
Temperature 212 °F		ISO 11403-1/-2
 5.79 MPa
@Strain 1.50 %,
Temperature 60.0 °C		840 psi
@Strain 1.50 %,
Temperature 140 °F		ISO 11403-1/-2
 5.81 MPa
@Strain 2.40 %,
Temperature 80.0 °C		843 psi
@Strain 2.40 %,
Temperature 176 °F		ISO 11403-1/-2
 5.89 MPa
@Strain 3.70 %,
Temperature 120 °C		854 psi
@Strain 3.70 %,
Temperature 248 °F		ISO 11403-1/-2
 5.95 MPa
@Strain 3.00 %,
Temperature 100 °C		863 psi
@Strain 3.00 %,
Temperature 212 °F		ISO 11403-1/-2
 5.97 MPa
@Strain 2.50 %,
Temperature 80.0 °C		866 psi
@Strain 2.50 %,
Temperature 176 °F		ISO 11403-1/-2
 5.99 MPa
@Strain 3.80 %,
Temperature 120 °C		869 psi
@Strain 3.80 %,
Temperature 248 °F		ISO 11403-1/-2
 6.07 MPa
@Strain 1.60 %,
Temperature 60.0 °C		880 psi
@Strain 1.60 %,
Temperature 140 °F		ISO 11403-1/-2
 6.11 MPa
@Strain 3.90 %,
Temperature 120 °C		886 psi
@Strain 3.90 %,
Temperature 248 °F		ISO 11403-1/-2
 6.13 MPa
@Strain 2.60 %,
Temperature 80.0 °C		889 psi
@Strain 2.60 %,
Temperature 176 °F		ISO 11403-1/-2
 6.13 MPa
@Strain 3.10 %,
Temperature 100 °C		889 psi
@Strain 3.10 %,
Temperature 212 °F		ISO 11403-1/-2
 6.22 MPa
@Strain 0.300 %,
Temperature -40.0 °C		902 psi
@Strain 0.300 %,
Temperature -40.0 °F		ISO 11403-1/-2
 6.23 MPa
@Strain 4.00 %,
Temperature 120 °C		904 psi
@Strain 4.00 %,
Temperature 248 °F		ISO 11403-1/-2
 6.24 MPa
@Strain 3.20 %,
Temperature 100 °C		905 psi
@Strain 3.20 %,
Temperature 212 °F		ISO 11403-1/-2
 6.28 MPa
@Strain 0.400 %,
Temperature 23.0 °C		911 psi
@Strain 0.400 %,
Temperature 73.4 °F		ISO 11403-1/-2
 6.29 MPa
@Strain 1.70 %,
Temperature 60.0 °C		912 psi
@Strain 1.70 %,
Temperature 140 °F		ISO 11403-1/-2
 6.33 MPa
@Strain 4.10 %,
Temperature 120 °C		918 psi
@Strain 4.10 %,
Temperature 248 °F		ISO 11403-1/-2
 6.38 MPa
@Strain 2.70 %,
Temperature 80.0 °C		925 psi
@Strain 2.70 %,
Temperature 176 °F		ISO 11403-1/-2
 6.39 MPa
@Strain 7.00 %,
Temperature 150 °C		927 psi
@Strain 7.00 %,
Temperature 302 °F		ISO 11403-1/-2
 6.40 MPa
@Strain 3.30 %,
Temperature 100 °C		928 psi
@Strain 3.30 %,
Temperature 212 °F		ISO 11403-1/-2
 6.47 MPa
@Strain 4.20 %,
Temperature 120 °C		938 psi
@Strain 4.20 %,
Temperature 248 °F		ISO 11403-1/-2
 6.51 MPa
@Strain 2.80 %,
Temperature 80.0 °C		944 psi
@Strain 2.80 %,
Temperature 176 °F		ISO 11403-1/-2
 6.53 MPa
@Strain 1.80 %,
Temperature 60.0 °C		947 psi
@Strain 1.80 %,
Temperature 140 °F		ISO 11403-1/-2
 6.54 MPa
@Strain 3.40 %,
Temperature 100 °C		949 psi
@Strain 3.40 %,
Temperature 212 °F		ISO 11403-1/-2
 6.55 MPa
@Strain 4.30 %,
Temperature 120 °C		950 psi
@Strain 4.30 %,
Temperature 248 °F		ISO 11403-1/-2
 6.67 MPa
@Strain 4.40 %,
Temperature 120 °C		967 psi
@Strain 4.40 %,
Temperature 248 °F		ISO 11403-1/-2
 6.68 MPa
@Strain 3.50 %,
Temperature 100 °C		969 psi
@Strain 3.50 %,
Temperature 212 °F		ISO 11403-1/-2
 6.70 MPa
@Strain 2.90 %,
Temperature 80.0 °C		972 psi
@Strain 2.90 %,
Temperature 176 °F		ISO 11403-1/-2
 6.79 MPa
@Strain 1.90 %,
Temperature 60.0 °C		985 psi
@Strain 1.90 %,
Temperature 140 °F		ISO 11403-1/-2
 6.80 MPa
@Strain 4.50 %,
Temperature 120 °C		986 psi
@Strain 4.50 %,
Temperature 248 °F		ISO 11403-1/-2
 6.81 MPa
@Strain 8.00 %,
Temperature 150 °C		988 psi
@Strain 8.00 %,
Temperature 302 °F		ISO 11403-1/-2
 6.83 MPa
@Strain 3.60 %,
Temperature 100 °C		991 psi
@Strain 3.60 %,
Temperature 212 °F		ISO 11403-1/-2
 6.85 MPa
@Strain 4.60 %,
Temperature 120 °C		994 psi
@Strain 4.60 %,
Temperature 248 °F		ISO 11403-1/-2
 6.87 MPa
@Strain 3.00 %,
Temperature 80.0 °C		996 psi
@Strain 3.00 %,
Temperature 176 °F		ISO 11403-1/-2
 6.94 MPa
@Strain 4.70 %,
Temperature 120 °C		1010 psi
@Strain 4.70 %,
Temperature 248 °F		ISO 11403-1/-2
 6.98 MPa
@Strain 3.70 %,
Temperature 100 °C		1010 psi
@Strain 3.70 %,
Temperature 212 °F		ISO 11403-1/-2
 7.01 MPa
@Strain 3.10 %,
Temperature 80.0 °C		1020 psi
@Strain 3.10 %,
Temperature 176 °F		ISO 11403-1/-2
 7.03 MPa
@Strain 3.09 %,
Temperature 90.0 °C		1020 psi
@Strain 3.09 %,
Temperature 194 °F		ISO 527
 7.06 MPa
@Strain 4.80 %,
Temperature 120 °C		1020 psi
@Strain 4.80 %,
Temperature 248 °F		ISO 11403-1/-2
 7.11 MPa
@Strain 2.00 %,
Temperature 60.0 °C		1030 psi
@Strain 2.00 %,
Temperature 140 °F		ISO 11403-1/-2
 7.14 MPa
@Strain 4.90 %,
Temperature 120 °C		1040 psi
@Strain 4.90 %,
Temperature 248 °F		ISO 11403-1/-2
 7.14 MPa
@Strain 3.80 %,
Temperature 100 °C		1040 psi
@Strain 3.80 %,
Temperature 212 °F		ISO 11403-1/-2
 7.19 MPa
@Strain 9.00 %,
Temperature 150 °C		1040 psi
@Strain 9.00 %,
Temperature 302 °F		ISO 11403-1/-2
 7.22 MPa
@Strain 3.90 %,
Temperature 100 °C		1050 psi
@Strain 3.90 %,
Temperature 212 °F		ISO 11403-1/-2
 7.25 MPa
@Strain 3.20 %,
Temperature 80.0 °C		1050 psi
@Strain 3.20 %,
Temperature 176 °F		ISO 11403-1/-2
 7.26 MPa
@Strain 5.00 %,
Temperature 120 °C		1050 psi
@Strain 5.00 %,
Temperature 248 °F		ISO 11403-1/-2
 7.29 MPa
@Strain 0.400 %,
Temperature 0.000 °C		1060 psi
@Strain 0.400 %,
Temperature 32.0 °F		ISO 11403-1/-2
 7.33 MPa
@Strain 4.00 %,
Temperature 100 °C		1060 psi
@Strain 4.00 %,
Temperature 212 °F		ISO 11403-1/-2
 7.36 MPa
@Strain 2.10 %,
Temperature 60.0 °C		1070 psi
@Strain 2.10 %,
Temperature 140 °F		ISO 11403-1/-2
 7.38 MPa
@Strain 3.30 %,
Temperature 80.0 °C		1070 psi
@Strain 3.30 %,
Temperature 176 °F		ISO 11403-1/-2
 7.48 MPa
@Strain 4.10 %,
Temperature 100 °C		1080 psi
@Strain 4.10 %,
Temperature 212 °F		ISO 11403-1/-2
 7.53 MPa
@Strain 3.40 %,
Temperature 80.0 °C		1090 psi
@Strain 3.40 %,
Temperature 176 °F		ISO 11403-1/-2
 7.53 MPa
@Strain 10.0 %,
Temperature 150 °C		1090 psi
@Strain 10.0 %,
Temperature 302 °F		ISO 11403-1/-2
 7.62 MPa
@Strain 4.20 %,
Temperature 100 °C		1110 psi
@Strain 4.20 %,
Temperature 212 °F		ISO 11403-1/-2
 7.69 MPa
@Strain 2.20 %,
Temperature 60.0 °C		1120 psi
@Strain 2.20 %,
Temperature 140 °F		ISO 11403-1/-2
 7.73 MPa
@Strain 4.30 %,
Temperature 100 °C		1120 psi
@Strain 4.30 %,
Temperature 212 °F		ISO 11403-1/-2
 7.76 MPa
@Strain 3.50 %,
Temperature 80.0 °C		1130 psi
@Strain 3.50 %,
Temperature 176 °F		ISO 11403-1/-2
 7.82 MPa
@Strain 4.40 %,
Temperature 100 °C		1130 psi
@Strain 4.40 %,
Temperature 212 °F		ISO 11403-1/-2
 7.86 MPa
@Strain 2.30 %,
Temperature 60.0 °C		1140 psi
@Strain 2.30 %,
Temperature 140 °F		ISO 11403-1/-2
 7.87 MPa
@Strain 3.60 %,
Temperature 80.0 °C		1140 psi
@Strain 3.60 %,
Temperature 176 °F		ISO 11403-1/-2
 7.90 MPa
@Strain 6.00 %,
Temperature 120 °C		1150 psi
@Strain 6.00 %,
Temperature 248 °F		ISO 11403-1/-2
 7.98 MPa
@Strain 4.50 %,
Temperature 100 °C		1160 psi
@Strain 4.50 %,
Temperature 212 °F		ISO 11403-1/-2
 8.04 MPa
@Strain 3.70 %,
Temperature 80.0 °C		1170 psi
@Strain 3.70 %,
Temperature 176 °F		ISO 11403-1/-2
 8.10 MPa
@Strain 4.60 %,
Temperature 100 °C		1170 psi
@Strain 4.60 %,
Temperature 212 °F		ISO 11403-1/-2
 8.10 MPa
@Strain 2.40 %,
Temperature 60.0 °C		1170 psi
@Strain 2.40 %,
Temperature 140 °F		ISO 11403-1/-2
 8.17 MPa
@Strain 4.70 %,
Temperature 100 °C		1180 psi
@Strain 4.70 %,
Temperature 212 °F		ISO 11403-1/-2
 8.21 MPa
@Strain 0.400 %,
Temperature -40.0 °C		1190 psi
@Strain 0.400 %,
Temperature -40.0 °F		ISO 11403-1/-2
 8.23 MPa
@Strain 3.80 %,
Temperature 80.0 °C		1190 psi
@Strain 3.80 %,
Temperature 176 °F		ISO 11403-1/-2
 8.25 MPa
@Strain 0.500 %,
Temperature 23.0 °C		1200 psi
@Strain 0.500 %,
Temperature 73.4 °F		ISO 11403-1/-2
 8.32 MPa
@Strain 4.80 %,
Temperature 100 °C		1210 psi
@Strain 4.80 %,
Temperature 212 °F		ISO 11403-1/-2
 8.35 MPa
@Strain 2.50 %,
Temperature 60.0 °C		1210 psi
@Strain 2.50 %,
Temperature 140 °F		ISO 11403-1/-2
 8.36 MPa
@Strain 3.90 %,
Temperature 80.0 °C		1210 psi
@Strain 3.90 %,
Temperature 176 °F		ISO 11403-1/-2
 8.43 MPa
@Strain 4.90 %,
Temperature 100 °C		1220 psi
@Strain 4.90 %,
Temperature 212 °F		ISO 11403-1/-2
 8.52 MPa
@Strain 4.00 %,
Temperature 80.0 °C		1240 psi
@Strain 4.00 %,
Temperature 176 °F		ISO 11403-1/-2
 8.53 MPa
@Strain 5.00 %,
Temperature 100 °C		1240 psi
@Strain 5.00 %,
Temperature 212 °F		ISO 11403-1/-2
 8.57 MPa
@Strain 15.0 %,
Temperature 150 °C		1240 psi
@Strain 15.0 %,
Temperature 302 °F		ISO 11403-1/-2
 8.63 MPa
@Strain 2.60 %,
Temperature 60.0 °C		1250 psi
@Strain 2.60 %,
Temperature 140 °F		ISO 11403-1/-2
 8.64 MPa
@Strain 4.10 %,
Temperature 80.0 °C		1250 psi
@Strain 4.10 %,
Temperature 176 °F		ISO 11403-1/-2
 8.77 MPa
@Strain 4.20 %,
Temperature 80.0 °C		1270 psi
@Strain 4.20 %,
Temperature 176 °F		ISO 11403-1/-2
 8.82 MPa
@Strain 2.70 %,
Temperature 60.0 °C		1280 psi
@Strain 2.70 %,
Temperature 140 °F		ISO 11403-1/-2
 8.83 MPa
@Strain 7.00 %,
Temperature 120 °C		1280 psi
@Strain 7.00 %,
Temperature 248 °F		ISO 11403-1/-2
 8.97 MPa
@Strain 4.30 %,
Temperature 80.0 °C		1300 psi
@Strain 4.30 %,
Temperature 176 °F		ISO 11403-1/-2
 8.99 MPa
@Strain 2.80 %,
Temperature 60.0 °C		1300 psi
@Strain 2.80 %,
Temperature 140 °F		ISO 11403-1/-2
 9.07 MPa
@Strain 4.40 %,
Temperature 80.0 °C		1320 psi
@Strain 4.40 %,
Temperature 176 °F		ISO 11403-1/-2
 9.22 MPa
@Strain 4.50 %,
Temperature 80.0 °C		1340 psi
@Strain 4.50 %,
Temperature 176 °F		ISO 11403-1/-2
 9.26 MPa
@Strain 2.90 %,
Temperature 60.0 °C		1340 psi
@Strain 2.90 %,
Temperature 140 °F		ISO 11403-1/-2
 9.29 MPa
@Strain 6.00 %,
Temperature 100 °C		1350 psi
@Strain 6.00 %,
Temperature 212 °F		ISO 11403-1/-2
 9.38 MPa
@Strain 4.60 %,
Temperature 80.0 °C		1360 psi
@Strain 4.60 %,
Temperature 176 °F		ISO 11403-1/-2
 9.41 MPa
@Strain 3.00 %,
Temperature 60.0 °C		1360 psi
@Strain 3.00 %,
Temperature 140 °F		ISO 11403-1/-2
 9.46 MPa
@Strain 8.00 %,
Temperature 120 °C		1370 psi
@Strain 8.00 %,
Temperature 248 °F		ISO 11403-1/-2
 9.49 MPa
@Strain 4.70 %,
Temperature 80.0 °C		1380 psi
@Strain 4.70 %,
Temperature 176 °F		ISO 11403-1/-2
 9.49 MPa
@Strain 0.500 %,
Temperature 0.000 °C		1380 psi
@Strain 0.500 %,
Temperature 32.0 °F		ISO 11403-1/-2
 9.61 MPa
@Strain 0.600 %,
Temperature 23.0 °C		1390 psi
@Strain 0.600 %,
Temperature 73.4 °F		ISO 11403-1/-2
 9.62 MPa
@Strain 3.10 %,
Temperature 60.0 °C		1400 psi
@Strain 3.10 %,
Temperature 140 °F		ISO 11403-1/-2
 9.64 MPa
@Strain 4.80 %,
Temperature 80.0 °C		1400 psi
@Strain 4.80 %,
Temperature 176 °F		ISO 11403-1/-2
 9.70 MPa
@Strain 20.0 %,
Temperature 150 °C		1410 psi
@Strain 20.0 %,
Temperature 302 °F		ISO 11403-1/-2
 9.74 MPa
@Strain 4.90 %,
Temperature 80.0 °C		1410 psi
@Strain 4.90 %,
Temperature 176 °F		ISO 11403-1/-2
 9.84 MPa
@Strain 3.20 %,
Temperature 60.0 °C		1430 psi
@Strain 3.20 %,
Temperature 140 °F		ISO 11403-1/-2
 9.86 MPa
@Strain 5.00 %,
Temperature 80.0 °C		1430 psi
@Strain 5.00 %,
Temperature 176 °F		ISO 11403-1/-2
 9.88 MPa
@Strain 0.500 %,
Temperature -40.0 °C		1430 psi
@Strain 0.500 %,
Temperature -40.0 °F		ISO 11403-1/-2
 9.98 MPa
@Strain 9.00 %,
Temperature 120 °C		1450 psi
@Strain 9.00 %,
Temperature 248 °F		ISO 11403-1/-2
 10.02 MPa
@Strain 3.30 %,
Temperature 60.0 °C		1453 psi
@Strain 3.30 %,
Temperature 140 °F		ISO 11403-1/-2
 10.21 MPa
@Strain 3.40 %,
Temperature 60.0 °C		1481 psi
@Strain 3.40 %,
Temperature 140 °F		ISO 11403-1/-2
 10.3 MPa
@Strain 7.00 %,
Temperature 100 °C		1490 psi
@Strain 7.00 %,
Temperature 212 °F		ISO 11403-1/-2
 10.32 MPa
@Strain 25.0 %,
Temperature 150 °C		1497 psi
@Strain 25.0 %,
Temperature 302 °F		ISO 11403-1/-2
 10.4 MPa
@Strain 3.50 %,
Temperature 60.0 °C		1510 psi
@Strain 3.50 %,
Temperature 140 °F		ISO 11403-1/-2
 10.45 MPa
@Strain 10.0 %,
Temperature 120 °C		1516 psi
@Strain 10.0 %,
Temperature 248 °F		ISO 11403-1/-2
 10.61 MPa
@Strain 3.60 %,
Temperature 60.0 °C		1539 psi
@Strain 3.60 %,
Temperature 140 °F		ISO 11403-1/-2
 10.73 MPa
@Strain 3.70 %,
Temperature 60.0 °C		1556 psi
@Strain 3.70 %,
Temperature 140 °F		ISO 11403-1/-2
 10.76 MPa
@Strain 6.00 %,
Temperature 80.0 °C		1561 psi
@Strain 6.00 %,
Temperature 176 °F		ISO 11403-1/-2
 10.77 MPa
@Strain 30.0 %,
Temperature 150 °C		1562 psi
@Strain 30.0 %,
Temperature 302 °F		ISO 11403-1/-2
 10.8 MPa
@Strain 6.13 %,
Temperature 90.0 °C		1570 psi
@Strain 6.13 %,
Temperature 194 °F		ISO 527
 10.96 MPa
@Strain 3.80 %,
Temperature 60.0 °C		1590 psi
@Strain 3.80 %,
Temperature 140 °F		ISO 11403-1/-2
 10.97 MPa
@Strain 0.700 %,
Temperature 23.0 °C		1591 psi
@Strain 0.700 %,
Temperature 73.4 °F		ISO 11403-1/-2
 10.99 MPa
@Strain 8.00 %,
Temperature 100 °C		1594 psi
@Strain 8.00 %,
Temperature 212 °F		ISO 11403-1/-2
 11.03 MPa
@Strain 0.600 %,
Temperature 0.000 °C		1600 psi
@Strain 0.600 %,
Temperature 32.0 °F		ISO 11403-1/-2
 11.1 MPa
@Strain 35.0 %,
Temperature 150 °C		1610 psi
@Strain 35.0 %,
Temperature 302 °F		ISO 11403-1/-2
 11.12 MPa
@Strain 3.90 %,
Temperature 60.0 °C		1613 psi
@Strain 3.90 %,
Temperature 140 °F		ISO 11403-1/-2
 11.24 MPa
@Strain 4.00 %,
Temperature 60.0 °C		1630 psi
@Strain 4.00 %,
Temperature 140 °F		ISO 11403-1/-2
 11.37 MPa
@Strain 40.0 %,
Temperature 150 °C		1649 psi
@Strain 40.0 %,
Temperature 302 °F		ISO 11403-1/-2
 11.48 MPa
@Strain 4.10 %,
Temperature 60.0 °C		1665 psi
@Strain 4.10 %,
Temperature 140 °F		ISO 11403-1/-2
 11.59 MPa
@Strain 4.20 %,
Temperature 60.0 °C		1681 psi
@Strain 4.20 %,
Temperature 140 °F		ISO 11403-1/-2
 11.59 MPa
@Strain 45.0 %,
Temperature 150 °C		1681 psi
@Strain 45.0 %,
Temperature 302 °F		ISO 11403-1/-2
 11.6 MPa
@Strain 9.00 %,
Temperature 100 °C		1680 psi
@Strain 9.00 %,
Temperature 212 °F		ISO 11403-1/-2
 11.73 MPa
@Strain 50.0 %,
Temperature 150 °C		1701 psi
@Strain 50.0 %,
Temperature 302 °F		ISO 11403-1/-2
 11.75 MPa
@Strain 0.600 %,
Temperature -40.0 °C		1704 psi
@Strain 0.600 %,
Temperature -40.0 °F		ISO 11403-1/-2
 11.75 MPa
@Strain 4.30 %,
Temperature 60.0 °C		1704 psi
@Strain 4.30 %,
Temperature 140 °F		ISO 11403-1/-2
 11.79 MPa
@Strain 15.0 %,
Temperature 120 °C		1710 psi
@Strain 15.0 %,
Temperature 248 °F		ISO 11403-1/-2
 11.93 MPa
@Strain 7.00 %,
Temperature 80.0 °C		1730 psi
@Strain 7.00 %,
Temperature 176 °F		ISO 11403-1/-2
 11.93 MPa
@Strain 4.40 %,
Temperature 60.0 °C		1730 psi
@Strain 4.40 %,
Temperature 140 °F		ISO 11403-1/-2
 12.07 MPa
@Strain 4.50 %,
Temperature 60.0 °C		1751 psi
@Strain 4.50 %,
Temperature 140 °F		ISO 11403-1/-2
 12.09 MPa
@Strain 10.0 %,
Temperature 100 °C		1754 psi
@Strain 10.0 %,
Temperature 212 °F		ISO 11403-1/-2
 12.24 MPa
@Strain 4.60 %,
Temperature 60.0 °C		1775 psi
@Strain 4.60 %,
Temperature 140 °F		ISO 11403-1/-2
 12.31 MPa
@Strain 0.800 %,
Temperature 23.0 °C		1785 psi
@Strain 0.800 %,
Temperature 73.4 °F		ISO 11403-1/-2
 12.38 MPa
@Strain 4.70 %,
Temperature 60.0 °C		1796 psi
@Strain 4.70 %,
Temperature 140 °F		ISO 11403-1/-2
 12.52 MPa
@Strain 0.700 %,
Temperature 0.000 °C		1816 psi
@Strain 0.700 %,
Temperature 32.0 °F		ISO 11403-1/-2
 12.55 MPa
@Strain 4.80 %,
Temperature 60.0 °C		1820 psi
@Strain 4.80 %,
Temperature 140 °F		ISO 11403-1/-2
 12.66 MPa
@Strain 4.90 %,
Temperature 60.0 °C		1836 psi
@Strain 4.90 %,
Temperature 140 °F		ISO 11403-1/-2
 12.71 MPa
@Strain 8.00 %,
Temperature 80.0 °C		1843 psi
@Strain 8.00 %,
Temperature 176 °F		ISO 11403-1/-2
 12.83 MPa
@Strain 5.00 %,
Temperature 60.0 °C		1861 psi
@Strain 5.00 %,
Temperature 140 °F		ISO 11403-1/-2
 12.9 MPa
@Strain 9.16 %,
Temperature 90.0 °C		1870 psi
@Strain 9.16 %,
Temperature 194 °F		ISO 527
 13.12 MPa
@Strain 20.0 %,
Temperature 120 °C		1903 psi
@Strain 20.0 %,
Temperature 248 °F		ISO 11403-1/-2
 13.37 MPa
@Strain 9.00 %,
Temperature 80.0 °C		1939 psi
@Strain 9.00 %,
Temperature 176 °F		ISO 11403-1/-2
 13.49 MPa
@Strain 15.0 %,
Temperature 100 °C		1957 psi
@Strain 15.0 %,
Temperature 212 °F		ISO 11403-1/-2
 13.65 MPa
@Strain 0.900 %,
Temperature 23.0 °C		1980 psi
@Strain 0.900 %,
Temperature 73.4 °F		ISO 11403-1/-2
 13.67 MPa
@Strain 0.700 %,
Temperature -40.0 °C		1983 psi
@Strain 0.700 %,
Temperature -40.0 °F		ISO 11403-1/-2
 13.8 MPa
@Strain 6.00 %,
Temperature 60.0 °C		2000 psi
@Strain 6.00 %,
Temperature 140 °F		ISO 11403-1/-2
 13.8 MPa
@Strain 25.0 %,
Temperature 120 °C		2000 psi
@Strain 25.0 %,
Temperature 248 °F		ISO 11403-1/-2
 13.94 MPa
@Strain 10.0 %,
Temperature 80.0 °C		2022 psi
@Strain 10.0 %,
Temperature 176 °F		ISO 11403-1/-2
 14.06 MPa
@Strain 0.800 %,
Temperature 0.000 °C		2039 psi
@Strain 0.800 %,
Temperature 32.0 °F		ISO 11403-1/-2
 14.2 MPa
@Strain 12.19 %,
Temperature 90.0 °C		2060 psi
@Strain 12.19 %,
Temperature 194 °F		ISO 527
 14.28 MPa
@Strain 30.0 %,
Temperature 120 °C		2071 psi
@Strain 30.0 %,
Temperature 248 °F		ISO 11403-1/-2
 14.62 MPa
@Strain 35.0 %,
Temperature 120 °C		2120 psi
@Strain 35.0 %,
Temperature 248 °F		ISO 11403-1/-2
 14.86 MPa
@Strain 20.0 %,
Temperature 100 °C		2155 psi
@Strain 20.0 %,
Temperature 212 °F		ISO 11403-1/-2
 14.9 MPa
@Strain 40.0 %,
Temperature 120 °C		2160 psi
@Strain 40.0 %,
Temperature 248 °F		ISO 11403-1/-2
 14.94 MPa
@Strain 1.00 %,
Temperature 23.0 °C		2167 psi
@Strain 1.00 %,
Temperature 73.4 °F		ISO 11403-1/-2
 15.08 MPa
@Strain 7.00 %,
Temperature 60.0 °C		2187 psi
@Strain 7.00 %,
Temperature 140 °F		ISO 11403-1/-2
 15.1 MPa
@Strain 15.22 %,
Temperature 90.0 °C		2190 psi
@Strain 15.22 %,
Temperature 194 °F		ISO 527
 15.12 MPa
@Strain 45.0 %,
Temperature 120 °C		2193 psi
@Strain 45.0 %,
Temperature 248 °F		ISO 11403-1/-2
 15.27 MPa
@Strain 50.0 %,
Temperature 120 °C		2215 psi
@Strain 50.0 %,
Temperature 248 °F		ISO 11403-1/-2
 15.49 MPa
@Strain 15.0 %,
Temperature 80.0 °C		2247 psi
@Strain 15.0 %,
Temperature 176 °F		ISO 11403-1/-2
 15.52 MPa
@Strain 0.900 %,
Temperature 0.000 °C		2251 psi
@Strain 0.900 %,
Temperature 32.0 °F		ISO 11403-1/-2
 15.53 MPa
@Strain 25.0 %,
Temperature 100 °C		2252 psi
@Strain 25.0 %,
Temperature 212 °F		ISO 11403-1/-2
 15.53 MPa
@Strain 2.75 %,
Temperature 40.0 °C		2252 psi
@Strain 2.75 %,
Temperature 104 °F		ISO 527
 15.56 MPa
@Strain 0.800 %,
Temperature -40.0 °C		2257 psi
@Strain 0.800 %,
Temperature -40.0 °F		ISO 11403-1/-2
 15.6 MPa
@Strain 18.25 %,
Temperature 90.0 °C		2260 psi
@Strain 18.25 %,
Temperature 194 °F		ISO 527
 15.93 MPa
@Strain 8.00 %,
Temperature 60.0 °C		2310 psi
@Strain 8.00 %,
Temperature 140 °F		ISO 11403-1/-2
 16.0 MPa
@Strain 21.29 %,
Temperature 90.0 °C		2320 psi
@Strain 21.29 %,
Temperature 194 °F		ISO 527
 16.01 MPa
@Strain 30.0 %,
Temperature 100 °C		2322 psi
@Strain 30.0 %,
Temperature 212 °F		ISO 11403-1/-2
 16.2 MPa
@Strain 1.10 %,
Temperature 23.0 °C		2350 psi
@Strain 1.10 %,
Temperature 73.4 °F		ISO 11403-1/-2
 16.3 MPa
@Strain 24.32 %,
Temperature 90.0 °C		2360 psi
@Strain 24.32 %,
Temperature 194 °F		ISO 527
 16.35 MPa
@Strain 35.0 %,
Temperature 100 °C		2371 psi
@Strain 35.0 %,
Temperature 212 °F		ISO 11403-1/-2
 16.5 MPa
@Strain 27.35 %,
Temperature 90.0 °C		2390 psi
@Strain 27.35 %,
Temperature 194 °F		ISO 527
 16.6 MPa
@Strain 30.38 %,
Temperature 90.0 °C		2410 psi
@Strain 30.38 %,
Temperature 194 °F		ISO 527
 16.62 MPa
@Strain 40.0 %,
Temperature 100 °C		2411 psi
@Strain 40.0 %,
Temperature 212 °F		ISO 11403-1/-2
 16.67 MPa
@Strain 9.00 %,
Temperature 60.0 °C		2418 psi
@Strain 9.00 %,
Temperature 140 °F		ISO 11403-1/-2
 16.86 MPa
@Strain 45.0 %,
Temperature 100 °C		2445 psi
@Strain 45.0 %,
Temperature 212 °F		ISO 11403-1/-2
 16.93 MPa
@Strain 20.0 %,
Temperature 80.0 °C		2455 psi
@Strain 20.0 %,
Temperature 176 °F		ISO 11403-1/-2
 16.99 MPa
@Strain 1.00 %,
Temperature 0.000 °C		2464 psi
@Strain 1.00 %,
Temperature 32.0 °F		ISO 11403-1/-2
 17.02 MPa
@Strain 50.0 %,
Temperature 100 °C		2469 psi
@Strain 50.0 %,
Temperature 212 °F		ISO 11403-1/-2
 17.28 MPa
@Strain 10.0 %,
Temperature 60.0 °C		2506 psi
@Strain 10.0 %,
Temperature 140 °F		ISO 11403-1/-2
 17.36 MPa
@Strain 0.900 %,
Temperature -40.0 °C		2518 psi
@Strain 0.900 %,
Temperature -40.0 °F		ISO 11403-1/-2
 17.46 MPa
@Strain 1.20 %,
Temperature 23.0 °C		2532 psi
@Strain 1.20 %,
Temperature 73.4 °F		ISO 11403-1/-2
 17.62 MPa
@Strain 25.0 %,
Temperature 80.0 °C		2556 psi
@Strain 25.0 %,
Temperature 176 °F		ISO 11403-1/-2
 18.07 MPa
@Strain 30.0 %,
Temperature 80.0 °C		2621 psi
@Strain 30.0 %,
Temperature 176 °F		ISO 11403-1/-2
 18.28 MPa
@Strain 1.10 %,
Temperature 0.000 °C		2651 psi
@Strain 1.10 %,
Temperature 32.0 °F		ISO 11403-1/-2
 18.42 MPa
@Strain 35.0 %,
Temperature 80.0 °C		2672 psi
@Strain 35.0 %,
Temperature 176 °F		ISO 11403-1/-2
 18.62 MPa
@Strain 1.30 %,
Temperature 23.0 °C		2701 psi
@Strain 1.30 %,
Temperature 73.4 °F		ISO 11403-1/-2
 18.7 MPa
@Strain 40.0 %,
Temperature 80.0 °C		2710 psi
@Strain 40.0 %,
Temperature 176 °F		ISO 11403-1/-2
 18.92 MPa
@Strain 15.0 %,
Temperature 60.0 °C		2744 psi
@Strain 15.0 %,
Temperature 140 °F		ISO 11403-1/-2
 18.93 MPa
@Strain 45.0 %,
Temperature 80.0 °C		2746 psi
@Strain 45.0 %,
Temperature 176 °F		ISO 11403-1/-2
 19.16 MPa
@Strain 50.0 %,
Temperature 80.0 °C		2779 psi
@Strain 50.0 %,
Temperature 176 °F		ISO 11403-1/-2
 19.17 MPa
@Strain 1.00 %,
Temperature -40.0 °C		2780 psi
@Strain 1.00 %,
Temperature -40.0 °F		ISO 11403-1/-2
 19.75 MPa
@Strain 1.40 %,
Temperature 23.0 °C		2865 psi
@Strain 1.40 %,
Temperature 73.4 °F		ISO 11403-1/-2
 20.08 MPa
@Strain 5.39 %,
Temperature 40.0 °C		2912 psi
@Strain 5.39 %,
Temperature 104 °F		ISO 527
 20.38 MPa
@Strain 1.20 %,
Temperature 0.000 °C		2956 psi
@Strain 1.20 %,
Temperature 32.0 °F		ISO 11403-1/-2
 20.44 MPa
@Strain 20.0 %,
Temperature 60.0 °C		2965 psi
@Strain 20.0 %,
Temperature 140 °F		ISO 11403-1/-2
 20.82 MPa
@Strain 1.50 %,
Temperature 23.0 °C		3020 psi
@Strain 1.50 %,
Temperature 73.4 °F		ISO 11403-1/-2
 20.96 MPa
@Strain 1.10 %,
Temperature -40.0 °C		3040 psi
@Strain 1.10 %,
Temperature -40.0 °F		ISO 11403-1/-2
 21.15 MPa
@Strain 25.0 %,
Temperature 60.0 °C		3068 psi
@Strain 25.0 %,
Temperature 140 °F		ISO 11403-1/-2
 21.63 MPa
@Strain 30.0 %,
Temperature 60.0 °C		3137 psi
@Strain 30.0 %,
Temperature 140 °F		ISO 11403-1/-2
 21.85 MPa
@Strain 1.60 %,
Temperature 23.0 °C		3169 psi
@Strain 1.60 %,
Temperature 73.4 °F		ISO 11403-1/-2
 21.98 MPa
@Strain 35.0 %,
Temperature 60.0 °C		3188 psi
@Strain 35.0 %,
Temperature 140 °F		ISO 11403-1/-2
 22.25 MPa
@Strain 40.0 %,
Temperature 60.0 °C		3227 psi
@Strain 40.0 %,
Temperature 140 °F		ISO 11403-1/-2
 22.39 MPa
@Strain 1.30 %,
Temperature 0.000 °C		3247 psi
@Strain 1.30 %,
Temperature 32.0 °F		ISO 11403-1/-2
 22.46 MPa
@Strain 8.04 %,
Temperature 40.0 °C		3258 psi
@Strain 8.04 %,
Temperature 104 °F		ISO 527
 22.48 MPa
@Strain 45.0 %,
Temperature 60.0 °C		3260 psi
@Strain 45.0 %,
Temperature 140 °F		ISO 11403-1/-2
 22.57 MPa
@Strain 1.20 %,
Temperature -40.0 °C		3274 psi
@Strain 1.20 %,
Temperature -40.0 °F		ISO 11403-1/-2
 22.63 MPa
@Strain 50.0 %,
Temperature 60.0 °C		3282 psi
@Strain 50.0 %,
Temperature 140 °F		ISO 11403-1/-2
 22.81 MPa
@Strain 1.70 %,
Temperature 23.0 °C		3308 psi
@Strain 1.70 %,
Temperature 73.4 °F		ISO 11403-1/-2
 23.71 MPa
@Strain 1.90 %,
Temperature 23.0 °C		3439 psi
@Strain 1.90 %,
Temperature 73.4 °F		ISO 11403-1/-2
 23.72 MPa
@Strain 1.40 %,
Temperature 0.000 °C		3440 psi
@Strain 1.40 %,
Temperature 32.0 °F		ISO 11403-1/-2
 23.84 MPa
@Strain 10.69 %,
Temperature 40.0 °C		3458 psi
@Strain 10.69 %,
Temperature 104 °F		ISO 527
 24.32 MPa
@Strain 1.30 %,
Temperature -40.0 °C		3527 psi
@Strain 1.30 %,
Temperature -40.0 °F		ISO 11403-1/-2
 24.52 MPa
@Strain 2.00 %,
Temperature 23.0 °C		3556 psi
@Strain 2.00 %,
Temperature 73.4 °F		ISO 11403-1/-2
 24.72 MPa
@Strain 13.33 %,
Temperature 40.0 °C		3585 psi
@Strain 13.33 %,
Temperature 104 °F		ISO 527
 25.04 MPa
@Strain 1.50 %,
Temperature 0.000 °C		3632 psi
@Strain 1.50 %,
Temperature 32.0 °F		ISO 11403-1/-2
 25.27 MPa
@Strain 2.10 %,
Temperature 23.0 °C		3665 psi
@Strain 2.10 %,
Temperature 73.4 °F		ISO 11403-1/-2
 25.34 MPa
@Strain 15.98 %,
Temperature 40.0 °C		3675 psi
@Strain 15.98 %,
Temperature 104 °F		ISO 527
 25.71 MPa
@Strain 18.63 %,
Temperature 40.0 °C		3729 psi
@Strain 18.63 %,
Temperature 104 °F		ISO 527
 25.95 MPa
@Strain 2.20 %,
Temperature 23.0 °C		3764 psi
@Strain 2.20 %,
Temperature 73.4 °F		ISO 11403-1/-2
 25.98 MPa
@Strain 21.48 %,
Temperature 40.0 °C		3768 psi
@Strain 21.48 %,
Temperature 104 °F		ISO 527
 26.03 MPa
@Strain 1.40 %,
Temperature -40.0 °C		3775 psi
@Strain 1.40 %,
Temperature -40.0 °F		ISO 11403-1/-2
 26.12 MPa
@Strain 24.12 %,
Temperature 40.0 °C		3788 psi
@Strain 24.12 %,
Temperature 104 °F		ISO 527
 26.21 MPa
@Strain 26.77 %,
Temperature 40.0 °C		3801 psi
@Strain 26.77 %,
Temperature 104 °F		ISO 527
 26.29 MPa
@Strain 1.60 %,
Temperature 0.000 °C		3813 psi
@Strain 1.60 %,
Temperature 32.0 °F		ISO 11403-1/-2
 26.56 MPa
@Strain 2.30 %,
Temperature 23.0 °C		3852 psi
@Strain 2.30 %,
Temperature 73.4 °F		ISO 11403-1/-2
 27.07 MPa
@Strain 2.40 %,
Temperature 23.0 °C		3926 psi
@Strain 2.40 %,
Temperature 73.4 °F		ISO 11403-1/-2
 27.54 MPa
@Strain 1.70 %,
Temperature 0.000 °C		3994 psi
@Strain 1.70 %,
Temperature 32.0 °F		ISO 11403-1/-2
 27.55 MPa
@Strain 2.60 %,
Temperature 23.0 °C		3996 psi
@Strain 2.60 %,
Temperature 73.4 °F		ISO 11403-1/-2
 27.68 MPa
@Strain 1.50 %,
Temperature -40.0 °C		4015 psi
@Strain 1.50 %,
Temperature -40.0 °F		ISO 11403-1/-2
 27.95 MPa
@Strain 2.70 %,
Temperature 23.0 °C		4054 psi
@Strain 2.70 %,
Temperature 73.4 °F		ISO 11403-1/-2
 28.3 MPa
@Strain 2.80 %,
Temperature 23.0 °C		4100 psi
@Strain 2.80 %,
Temperature 73.4 °F		ISO 11403-1/-2
 28.61 MPa
@Strain 3.00 %,
Temperature 23.0 °C		4150 psi
@Strain 3.00 %,
Temperature 73.4 °F		ISO 11403-1/-2
 28.66 MPa
@Strain 1.80 %,
Temperature 0.000 °C		4157 psi
@Strain 1.80 %,
Temperature 32.0 °F		ISO 11403-1/-2
 28.88 MPa
@Strain 3.10 %,
Temperature 23.0 °C		4189 psi
@Strain 3.10 %,
Temperature 73.4 °F		ISO 11403-1/-2
 29.1 MPa
@Strain 3.30 %,
Temperature 23.0 °C		4220 psi
@Strain 3.30 %,
Temperature 73.4 °F		ISO 11403-1/-2
 29.28 MPa
@Strain 1.60 %,
Temperature -40.0 °C		4247 psi
@Strain 1.60 %,
Temperature -40.0 °F		ISO 11403-1/-2
 29.3 MPa
@Strain 3.40 %,
Temperature 23.0 °C		4250 psi
@Strain 3.40 %,
Temperature 73.4 °F		ISO 11403-1/-2
 29.49 MPa
@Strain 3.50 %,
Temperature 23.0 °C		4277 psi
@Strain 3.50 %,
Temperature 73.4 °F		ISO 11403-1/-2
 29.64 MPa
@Strain 3.70 %,
Temperature 23.0 °C		4299 psi
@Strain 3.70 %,
Temperature 73.4 °F		ISO 11403-1/-2
 29.78 MPa
@Strain 3.80 %,
Temperature 23.0 °C		4319 psi
@Strain 3.80 %,
Temperature 73.4 °F		ISO 11403-1/-2
 29.78 MPa
@Strain 1.90 %,
Temperature 0.000 °C		4319 psi
@Strain 1.90 %,
Temperature 32.0 °F		ISO 11403-1/-2
 29.93 MPa
@Strain 4.00 %,
Temperature 23.0 °C		4341 psi
@Strain 4.00 %,
Temperature 73.4 °F		ISO 11403-1/-2
 30.02 MPa
@Strain 4.10 %,
Temperature 23.0 °C		4354 psi
@Strain 4.10 %,
Temperature 73.4 °F		ISO 11403-1/-2
 30.14 MPa
@Strain 4.30 %,
Temperature 23.0 °C		4371 psi
@Strain 4.30 %,
Temperature 73.4 °F		ISO 11403-1/-2
 30.25 MPa
@Strain 4.40 %,
Temperature 23.0 °C		4387 psi
@Strain 4.40 %,
Temperature 73.4 °F		ISO 11403-1/-2
 30.35 MPa
@Strain 4.60 %,
Temperature 23.0 °C		4402 psi
@Strain 4.60 %,
Temperature 73.4 °F		ISO 11403-1/-2
 30.43 MPa
@Strain 4.70 %,
Temperature 23.0 °C		4414 psi
@Strain 4.70 %,
Temperature 73.4 °F		ISO 11403-1/-2
 30.53 MPa
@Strain 4.90 %,
Temperature 23.0 °C		4428 psi
@Strain 4.90 %,
Temperature 73.4 °F		ISO 11403-1/-2
 30.62 MPa
@Strain 5.00 %,
Temperature 23.0 °C		4441 psi
@Strain 5.00 %,
Temperature 73.4 °F		ISO 11403-1/-2
 30.84 MPa
@Strain 2.00 %,
Temperature 0.000 °C		4473 psi
@Strain 2.00 %,
Temperature 32.0 °F		ISO 11403-1/-2
 30.99 MPa
@Strain 6.00 %,
Temperature 23.0 °C		4495 psi
@Strain 6.00 %,
Temperature 73.4 °F		ISO 11403-1/-2
 30.99 MPa
@Strain 1.70 %,
Temperature -40.0 °C		4495 psi
@Strain 1.70 %,
Temperature -40.0 °F		ISO 11403-1/-2
 31.0 MPa
@Strain 25.0 %,
Temperature 23.0 °C		4500 psi
@Strain 25.0 %,
Temperature 73.4 °F		ISO 11403-1/-2
 31.37 MPa
@Strain 50.0 %,
Temperature 23.0 °C		4550 psi
@Strain 50.0 %,
Temperature 73.4 °F		ISO 11403-1/-2
 31.44 MPa
@Strain 30.0 %,
Temperature 23.0 °C		4560 psi
@Strain 30.0 %,
Temperature 73.4 °F		ISO 11403-1/-2
 31.45 MPa
@Strain 7.00 %,
Temperature 23.0 °C		4561 psi
@Strain 7.00 %,
Temperature 73.4 °F		ISO 11403-1/-2
 31.46 MPa
@Strain 45.0 %,
Temperature 23.0 °C		4563 psi
@Strain 45.0 %,
Temperature 73.4 °F		ISO 11403-1/-2
 31.58 MPa
@Strain 40.0 %,
Temperature 23.0 °C		4580 psi
@Strain 40.0 %,
Temperature 73.4 °F		ISO 11403-1/-2
 31.72 MPa
@Strain 8.00 %,
Temperature 23.0 °C		4601 psi
@Strain 8.00 %,
Temperature 73.4 °F		ISO 11403-1/-2
 31.87 MPa
@Strain 35.0 %,
Temperature 23.0 °C		4622 psi
@Strain 35.0 %,
Temperature 73.4 °F		ISO 11403-1/-2
 31.91 MPa
@Strain 2.10 %,
Temperature 0.000 °C		4628 psi
@Strain 2.10 %,
Temperature 32.0 °F		ISO 11403-1/-2
 31.92 MPa
@Strain 20.0 %,
Temperature 23.0 °C		4630 psi
@Strain 20.0 %,
Temperature 73.4 °F		ISO 11403-1/-2
 31.96 MPa
@Strain 9.00 %,
Temperature 23.0 °C		4635 psi
@Strain 9.00 %,
Temperature 73.4 °F		ISO 11403-1/-2
 32.13 MPa
@Strain 10.0 %,
Temperature 23.0 °C		4660 psi
@Strain 10.0 %,
Temperature 73.4 °F		ISO 11403-1/-2
 32.35 MPa
@Strain 15.0 %,
Temperature 23.0 °C		4692 psi
@Strain 15.0 %,
Temperature 73.4 °F		ISO 11403-1/-2
 32.69 MPa
@Strain 1.80 %,
Temperature -40.0 °C		4741 psi
@Strain 1.80 %,
Temperature -40.0 °F		ISO 11403-1/-2
 32.85 MPa
@Strain 2.20 %,
Temperature 0.000 °C		4764 psi
@Strain 2.20 %,
Temperature 32.0 °F		ISO 11403-1/-2
 33.79 MPa
@Strain 2.30 %,
Temperature 0.000 °C		4901 psi
@Strain 2.30 %,
Temperature 32.0 °F		ISO 11403-1/-2
 34.2 MPa
@Strain 1.90 %,
Temperature -40.0 °C		4960 psi
@Strain 1.90 %,
Temperature -40.0 °F		ISO 11403-1/-2
 34.63 MPa
@Strain 2.40 %,
Temperature 0.000 °C		5023 psi
@Strain 2.40 %,
Temperature 32.0 °F		ISO 11403-1/-2
 35.44 MPa
@Strain 2.50 %,
Temperature 0.000 °C		5140 psi
@Strain 2.50 %,
Temperature 32.0 °F		ISO 11403-1/-2
 35.65 MPa
@Strain 2.00 %,
Temperature -40.0 °C		5171 psi
@Strain 2.00 %,
Temperature -40.0 °F		ISO 11403-1/-2
 36.18 MPa
@Strain 2.60 %,
Temperature 0.000 °C		5247 psi
@Strain 2.60 %,
Temperature 32.0 °F		ISO 11403-1/-2
 36.87 MPa
@Strain 2.70 %,
Temperature 0.000 °C		5348 psi
@Strain 2.70 %,
Temperature 32.0 °F		ISO 11403-1/-2
 37.07 MPa
@Strain 2.10 %,
Temperature -40.0 °C		5377 psi
@Strain 2.10 %,
Temperature -40.0 °F		ISO 11403-1/-2
 37.5 MPa
@Strain 2.80 %,
Temperature 0.000 °C		5440 psi
@Strain 2.80 %,
Temperature 32.0 °F		ISO 11403-1/-2
 38.05 MPa
@Strain 2.90 %,
Temperature 0.000 °C		5519 psi
@Strain 2.90 %,
Temperature 32.0 °F		ISO 11403-1/-2
 38.41 MPa
@Strain 2.20 %,
Temperature -40.0 °C		5571 psi
@Strain 2.20 %,
Temperature -40.0 °F		ISO 11403-1/-2
 38.49 MPa
@Strain 3.00 %,
Temperature 0.000 °C		5583 psi
@Strain 3.00 %,
Temperature 32.0 °F		ISO 11403-1/-2
 38.92 MPa
@Strain 3.10 %,
Temperature 0.000 °C		5645 psi
@Strain 3.10 %,
Temperature 32.0 °F		ISO 11403-1/-2
 39.4 MPa
@Strain 3.20 %,
Temperature 0.000 °C		5710 psi
@Strain 3.20 %,
Temperature 32.0 °F		ISO 11403-1/-2
 39.7 MPa
@Strain 2.30 %,
Temperature -40.0 °C		5760 psi
@Strain 2.30 %,
Temperature -40.0 °F		ISO 11403-1/-2
 39.85 MPa
@Strain 3.30 %,
Temperature 0.000 °C		5780 psi
@Strain 3.30 %,
Temperature 32.0 °F		ISO 11403-1/-2
 40.31 MPa
@Strain 3.40 %,
Temperature 0.000 °C		5846 psi
@Strain 3.40 %,
Temperature 32.0 °F		ISO 11403-1/-2
 40.69 MPa
@Strain 3.50 %,
Temperature 0.000 °C		5902 psi
@Strain 3.50 %,
Temperature 32.0 °F		ISO 11403-1/-2
 41.06 MPa
@Strain 3.70 %,
Temperature 0.000 °C		5955 psi
@Strain 3.70 %,
Temperature 32.0 °F		ISO 11403-1/-2
 41.17 MPa
@Strain 2.40 %,
Temperature -40.0 °C		5971 psi
@Strain 2.40 %,
Temperature -40.0 °F		ISO 11403-1/-2
 41.33 MPa
@Strain 3.80 %,
Temperature 0.000 °C		5994 psi
@Strain 3.80 %,
Temperature 32.0 °F		ISO 11403-1/-2
 41.62 MPa
@Strain 3.90 %,
Temperature 0.000 °C		6036 psi
@Strain 3.90 %,
Temperature 32.0 °F		ISO 11403-1/-2
 41.66 MPa
@Strain 20.0 %,
Temperature 0.000 °C		6042 psi
@Strain 20.0 %,
Temperature 32.0 °F		ISO 11403-1/-2
 41.84 MPa
@Strain 4.10 %,
Temperature 0.000 °C		6068 psi
@Strain 4.10 %,
Temperature 32.0 °F		ISO 11403-1/-2
 41.97 MPa
@Strain 25.0 %,
Temperature 0.000 °C		6087 psi
@Strain 25.0 %,
Temperature 32.0 °F		ISO 11403-1/-2
 42.0 MPa
@Strain 30.0 %,
Temperature 0.000 °C		6090 psi
@Strain 30.0 %,
Temperature 32.0 °F		ISO 11403-1/-2
 42.06 MPa
@Strain 35.0 %,
Temperature 0.000 °C		6100 psi
@Strain 35.0 %,
Temperature 32.0 °F		ISO 11403-1/-2
 42.08 MPa
@Strain 40.0 %,
Temperature 0.000 °C		6103 psi
@Strain 40.0 %,
Temperature 32.0 °F		ISO 11403-1/-2
 42.12 MPa
@Strain 4.20 %,
Temperature 0.000 °C		6109 psi
@Strain 4.20 %,
Temperature 32.0 °F		ISO 11403-1/-2
 42.13 MPa
@Strain 45.0 %,
Temperature 0.000 °C		6110 psi
@Strain 45.0 %,
Temperature 32.0 °F		ISO 11403-1/-2
 42.14 MPa
@Strain 50.0 %,
Temperature 0.000 °C		6112 psi
@Strain 50.0 %,
Temperature 32.0 °F		ISO 11403-1/-2
 42.3 MPa
@Strain 4.30 %,
Temperature 0.000 °C		6140 psi
@Strain 4.30 %,
Temperature 32.0 °F		ISO 11403-1/-2
 42.35 MPa
@Strain 15.0 %,
Temperature 0.000 °C		6142 psi
@Strain 15.0 %,
Temperature 32.0 °F		ISO 11403-1/-2
 42.44 MPa
@Strain 2.50 %,
Temperature -40.0 °C		6155 psi
@Strain 2.50 %,
Temperature -40.0 °F		ISO 11403-1/-2
 42.5 MPa
@Strain 4.50 %,
Temperature 0.000 °C		6160 psi
@Strain 4.50 %,
Temperature 32.0 °F		ISO 11403-1/-2
 42.63 MPa
@Strain 4.60 %,
Temperature 0.000 °C		6183 psi
@Strain 4.60 %,
Temperature 32.0 °F		ISO 11403-1/-2
 42.78 MPa
@Strain 4.80 %,
Temperature 0.000 °C		6205 psi
@Strain 4.80 %,
Temperature 32.0 °F		ISO 11403-1/-2
 42.89 MPa
@Strain 4.90 %,
Temperature 0.000 °C		6221 psi
@Strain 4.90 %,
Temperature 32.0 °F		ISO 11403-1/-2
 43.45 MPa
@Strain 6.00 %,
Temperature 0.000 °C		6302 psi
@Strain 6.00 %,
Temperature 32.0 °F		ISO 11403-1/-2
 43.62 MPa
@Strain 2.60 %,
Temperature -40.0 °C		6327 psi
@Strain 2.60 %,
Temperature -40.0 °F		ISO 11403-1/-2
 43.85 MPa
@Strain 10.0 %,
Temperature 0.000 °C		6360 psi
@Strain 10.0 %,
Temperature 32.0 °F		ISO 11403-1/-2
 43.87 MPa
@Strain 7.00 %,
Temperature 0.000 °C		6363 psi
@Strain 7.00 %,
Temperature 32.0 °F		ISO 11403-1/-2
 43.96 MPa
@Strain 9.00 %,
Temperature 0.000 °C		6376 psi
@Strain 9.00 %,
Temperature 32.0 °F		ISO 11403-1/-2
 43.98 MPa
@Strain 8.00 %,
Temperature 0.000 °C		6379 psi
@Strain 8.00 %,
Temperature 32.0 °F		ISO 11403-1/-2
 44.86 MPa
@Strain 2.70 %,
Temperature -40.0 °C		6506 psi
@Strain 2.70 %,
Temperature -40.0 °F		ISO 11403-1/-2
 45.94 MPa
@Strain 2.80 %,
Temperature -40.0 °C		6663 psi
@Strain 2.80 %,
Temperature -40.0 °F		ISO 11403-1/-2
 46.84 MPa
@Strain 2.90 %,
Temperature -40.0 °C		6794 psi
@Strain 2.90 %,
Temperature -40.0 °F		ISO 11403-1/-2
 47.58 MPa
@Strain 3.00 %,
Temperature -40.0 °C		6901 psi
@Strain 3.00 %,
Temperature -40.0 °F		ISO 11403-1/-2
 48.46 MPa
@Strain 3.10 %,
Temperature -40.0 °C		7029 psi
@Strain 3.10 %,
Temperature -40.0 °F		ISO 11403-1/-2
 49.3 MPa
@Strain 3.20 %,
Temperature -40.0 °C		7150 psi
@Strain 3.20 %,
Temperature -40.0 °F		ISO 11403-1/-2
 49.98 MPa
@Strain 3.30 %,
Temperature -40.0 °C		7249 psi
@Strain 3.30 %,
Temperature -40.0 °F		ISO 11403-1/-2
 50.61 MPa
@Strain 3.40 %,
Temperature -40.0 °C		7340 psi
@Strain 3.40 %,
Temperature -40.0 °F		ISO 11403-1/-2
 51.24 MPa
@Strain 3.50 %,
Temperature -40.0 °C		7432 psi
@Strain 3.50 %,
Temperature -40.0 °F		ISO 11403-1/-2
 51.87 MPa
@Strain 3.60 %,
Temperature -40.0 °C		7523 psi
@Strain 3.60 %,
Temperature -40.0 °F		ISO 11403-1/-2
 52.37 MPa
@Strain 3.70 %,
Temperature -40.0 °C		7596 psi
@Strain 3.70 %,
Temperature -40.0 °F		ISO 11403-1/-2
 52.88 MPa
@Strain 3.80 %,
Temperature -40.0 °C		7670 psi
@Strain 3.80 %,
Temperature -40.0 °F		ISO 11403-1/-2
 53.38 MPa
@Strain 3.90 %,
Temperature -40.0 °C		7742 psi
@Strain 3.90 %,
Temperature -40.0 °F		ISO 11403-1/-2
 53.84 MPa
@Strain 4.00 %,
Temperature -40.0 °C		7809 psi
@Strain 4.00 %,
Temperature -40.0 °F		ISO 11403-1/-2
 54.29 MPa
@Strain 4.10 %,
Temperature -40.0 °C		7874 psi
@Strain 4.10 %,
Temperature -40.0 °F		ISO 11403-1/-2
 54.64 MPa
@Strain 4.20 %,
Temperature -40.0 °C		7925 psi
@Strain 4.20 %,
Temperature -40.0 °F		ISO 11403-1/-2
 54.89 MPa
@Strain 30.0 %,
Temperature -40.0 °C		7961 psi
@Strain 30.0 %,
Temperature -40.0 °F		ISO 11403-1/-2
 54.98 MPa
@Strain 4.30 %,
Temperature -40.0 °C		7974 psi
@Strain 4.30 %,
Temperature -40.0 °F		ISO 11403-1/-2
 55.41 MPa
@Strain 4.40 %,
Temperature -40.0 °C		8037 psi
@Strain 4.40 %,
Temperature -40.0 °F		ISO 11403-1/-2
 55.82 MPa
@Strain 4.50 %,
Temperature -40.0 °C		8096 psi
@Strain 4.50 %,
Temperature -40.0 °F		ISO 11403-1/-2
 56.16 MPa
@Strain 4.60 %,
Temperature -40.0 °C		8145 psi
@Strain 4.60 %,
Temperature -40.0 °F		ISO 11403-1/-2
 56.5 MPa
@Strain 4.70 %,
Temperature -40.0 °C		8190 psi
@Strain 4.70 %,
Temperature -40.0 °F		ISO 11403-1/-2
 56.73 MPa
@Strain 4.80 %,
Temperature -40.0 °C		8228 psi
@Strain 4.80 %,
Temperature -40.0 °F		ISO 11403-1/-2
 56.94 MPa
@Strain 4.90 %,
Temperature -40.0 °C		8258 psi
@Strain 4.90 %,
Temperature -40.0 °F		ISO 11403-1/-2
 57.23 MPa
@Strain 5.00 %,
Temperature -40.0 °C		8301 psi
@Strain 5.00 %,
Temperature -40.0 °F		ISO 11403-1/-2
 57.26 MPa
@Strain 25.0 %,
Temperature -40.0 °C		8305 psi
@Strain 25.0 %,
Temperature -40.0 °F		ISO 11403-1/-2
 58.7 MPa
@Strain 6.00 %,
Temperature -40.0 °C		8510 psi
@Strain 6.00 %,
Temperature -40.0 °F		ISO 11403-1/-2
 60.41 MPa
@Strain 7.00 %,
Temperature -40.0 °C		8762 psi
@Strain 7.00 %,
Temperature -40.0 °F		ISO 11403-1/-2
 61.32 MPa
@Strain 8.00 %,
Temperature -40.0 °C		8894 psi
@Strain 8.00 %,
Temperature -40.0 °F		ISO 11403-1/-2
 62.0 MPa
@Strain 9.00 %,
Temperature -40.0 °C		8990 psi
@Strain 9.00 %,
Temperature -40.0 °F		ISO 11403-1/-2
 62.44 MPa
@Strain 10.0 %,
Temperature -40.0 °C		9056 psi
@Strain 10.0 %,
Temperature -40.0 °F		ISO 11403-1/-2
 62.92 MPa
@Strain 20.0 %,
Temperature -40.0 °C		9126 psi
@Strain 20.0 %,
Temperature -40.0 °F		ISO 11403-1/-2
 63.58 MPa
@Strain 15.0 %,
Temperature -40.0 °C		9222 psi
@Strain 15.0 %,
Temperature -40.0 °F		ISO 11403-1/-2
Tensile Strength, Yield 38.0 MPa
@Temperature 23.0 °C		5510 psi
@Temperature 73.4 °F		ISO 527
Elongation at Break  12 %
@Temperature -40.0 °C		12 %
@Temperature -40.0 °F		nominal; ISO 527
 14 %
@Temperature -40.0 °C		14 %
@Temperature -40.0 °F		ASTM D638
 >= 50 %
@Temperature 23.0 °C		>= 50 %
@Temperature 73.4 °F		nominal; ISO 527
 >= 50 %
@Temperature 100 °C		>= 50 %
@Temperature 212 °F		nominal; ISO 527
 145 %
@Temperature 23.0 °C		145 %
@Temperature 73.4 °F		ASTM D638
 150 %
@Temperature 23.0 °C		150 %
@Temperature 73.4 °F		50mm/min; ISO 527
 170 %
@Temperature 90.0 °C		170 %
@Temperature 194 °F		ASTM D638
 190 %
@Temperature 150 °C		190 %
@Temperature 302 °F		ASTM D638
Elongation at Yield 7.0 %
@Temperature 23.0 °C		7.0 %
@Temperature 73.4 °F		ISO 527
Tensile Modulus  0.140 GPa
@Temperature 150 °C		20.3 ksi
@Temperature 302 °F		DAM; ISO 527
 0.177 GPa
@Temperature 120 °C		25.7 ksi
@Temperature 248 °F		DAM; ISO 527
 0.188 GPa
@Temperature 100 °C		27.3 ksi
@Temperature 212 °F		ISO 527
 0.244 GPa
@Temperature 90.0 °C		35.4 ksi
@Temperature 194 °F		DAM; ISO 527
 0.396 GPa
@Temperature 60.0 °C		57.4 ksi
@Temperature 140 °F		DAM; ISO 527
 0.807 GPa
@Temperature 40.0 °C		117 ksi
@Temperature 104 °F		DAM; ISO 527
 1.60 GPa
@Temperature 23.0 °C		232 ksi
@Temperature 73.4 °F		ASTM D638
 1.70 GPa
@Temperature 23.0 °C		247 ksi
@Temperature 73.4 °F		ISO 527
 1.863 GPa
@Temperature 0.000 °C		270.2 ksi
@Temperature 32.0 °F		DAM; ISO 527
 2.008 GPa
@Temperature -20.0 °C		291.2 ksi
@Temperature -4.00 °F		DAM; ISO 527
 2.14 GPa
@Temperature -40.0 °C		310 ksi
@Temperature -40.0 °F		ISO 527
 2.295 GPa
@Temperature -40.0 °C		332.9 ksi
@Temperature -40.0 °F		DAM; ISO 527
Flexural Strength  5.00 MPa
@Temperature 149 °C		725 psi
@Temperature 300 °F		ASTM D790
 8.40 MPa
@Temperature 100 °C		1220 psi
@Temperature 212 °F		ISO 178
 9.00 MPa
@Temperature 90.0 °C		1310 psi
@Temperature 194 °F		ASTM D790
 50.0 MPa
@Temperature 23.0 °C		7250 psi
@Temperature 73.4 °F		ISO 178
 53.0 MPa
@Temperature 23.0 °C		7690 psi
@Temperature 73.4 °F		ASTM D790
 73.4 MPa
@Temperature -40.0 °C		10600 psi
@Temperature -40.0 °F		ISO 178
 75.0 MPa
@Temperature -40.0 °C		10900 psi
@Temperature -40.0 °F		ASTM D790
Flexural Modulus  0.137 GPa
@Temperature 149 °C		19.9 ksi
@Temperature 300 °F		ASTM D790
 0.234 GPa
@Temperature 90.0 °C		33.9 ksi
@Temperature 194 °F		ASTM D790
 0.245 GPa
@Temperature 100 °C		35.5 ksi
@Temperature 212 °F		ISO 178
 1.55 GPa
@Temperature 23.0 °C		225 ksi
@Temperature 73.4 °F		ISO 178
 1.682 GPa
@Temperature 23.0 °C		244.0 ksi
@Temperature 73.4 °F		ASTM D790
 2.034 GPa
@Temperature -40.0 °C		295.0 ksi
@Temperature -40.0 °F		ASTM D790
 2.20 GPa
@Temperature -40.0 °C		319 ksi
@Temperature -40.0 °F		ISO 178
Compressive Strength 43.0 MPa
@Temperature 23.0 °C		6240 psi
@Temperature 73.4 °F		ASTM D695
Izod Impact, Notched  1.17 J/cm
@Temperature -40.0 °C		2.19 ft-lb/in
@Temperature -40.0 °F		ASTM D256
 NB
@Temperature 23.0 °C		NB
@Temperature 73.4 °F		ASTM D256
Izod Impact, Unnotched  NB
@Temperature -40.0 °C		NB
@Temperature -40.0 °F		ASTM D4812
 NB
@Temperature 23.0 °C		NB
@Temperature 73.4 °F		ASTM D4812
Izod Impact, Notched (ISO)  10.0 kJ/m²
@Temperature -40.0 °C		4.76 ft-lb/in²
@Temperature -40.0 °F		ISO 180/1A
 15.0 kJ/m²
@Temperature -30.0 °C		7.14 ft-lb/in²
@Temperature -22.0 °F		ISO 180/1A
 60.0 kJ/m²
@Temperature 23.0 °C		28.6 ft-lb/in²
@Temperature 73.4 °F		ISO 180/1A
Izod Impact, Unnotched (ISO)  270 kJ/m²
@Temperature -40.0 °C		128 ft-lb/in²
@Temperature -40.0 °F		ISO 180/1U
 NB
@Temperature -30.0 °C		NB
@Temperature -22.0 °F		ISO 180/1U
 NB
@Temperature 23.0 °C		NB
@Temperature 73.4 °F		ISO 180/1U
Charpy Impact Unnotched  NB
@Temperature -30.0 °C		NB
@Temperature -22.0 °F		ISO 179/1eU
 NB
@Temperature 23.0 °C		NB
@Temperature 73.4 °F		ISO 179/1eU
Charpy Impact, Notched  1.00 J/cm²
@Temperature -40.0 °C		4.76 ft-lb/in²
@Temperature -40.0 °F		ISO 179/1eA
 1.00 J/cm²
@Temperature -30.0 °C		4.76 ft-lb/in²
@Temperature -22.0 °F		ISO 179/1eA
 8.50 J/cm²
@Temperature 23.0 °C		40.4 ft-lb/in²
@Temperature 73.4 °F		ISO 179/1eA
Tensile Creep Modulus, 1 hour  413 MPa
@Temperature 23.0 °C,
Time 3.60e+7 sec		59900 psi
@Temperature 73.4 °F,
Time 10000 hour		10MPa; ISO 899
 591 MPa
@Temperature 23.0 °C,
Time 3.60e+7 sec		85700 psi
@Temperature 73.4 °F,
Time 10000 hour		5MPa; ISO 899
 714 MPa
@Temperature 23.0 °C,
Time 3.60e+6 sec		104000 psi
@Temperature 73.4 °F,
Time 1000 hour		10MPa; ISO 899
 896 MPa
@Temperature 23.0 °C,
Time 3.60e+6 sec		130000 psi
@Temperature 73.4 °F,
Time 1000 hour		5MPa; ISO 899
 1070 MPa
@Temperature 23.0 °C,
Time 360000 sec		155000 psi
@Temperature 73.4 °F,
Time 100 hour		10MPa; ISO 899
 1180 MPa
@Temperature 23.0 °C,
Time 360000 sec		171000 psi
@Temperature 73.4 °F,
Time 100 hour		5MPa; ISO 899
 1360 MPa
@Temperature 23.0 °C,
Time 36000 sec		197000 psi
@Temperature 73.4 °F,
Time 10.0 hour		10MPa; ISO 899
 1410 MPa
@Temperature 23.0 °C,
Time 36000 sec		205000 psi
@Temperature 73.4 °F,
Time 10.0 hour		5MPa; ISO 899
 1500 MPa
@Temperature 23.0 °C,
Time 3600 sec		218000 psi
@Temperature 73.4 °F,
Time 1.00 hour		10MPa; ISO 899
 1540 MPa
@Temperature 23.0 °C,
Time 3600 sec		223000 psi
@Temperature 73.4 °F,
Time 1.00 hour		5MPa; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 5.00 MPa
@Strain 0.325 %,
Temperature 23.0 °C		725 psi
@Strain 0.325 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 5.00 MPa
@Strain 0.355 %,
Temperature 23.0 °C		725 psi
@Strain 0.355 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 10.0 MPa
@Strain 0.738 %,
Temperature 23.0 °C		1450 psi
@Strain 0.738 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 10.0 MPa
@Strain 0.667 %,
Temperature 23.0 °C		1450 psi
@Strain 0.667 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
Tensile Creep Modulus, 1000 hours  0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		10000h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 5.00 MPa
@Strain 0.423 %,
Temperature 23.0 °C		725 psi
@Strain 0.423 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 5.00 MPa
@Strain 0.558 %,
Temperature 23.0 °C		725 psi
@Strain 0.558 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 5.00 MPa
@Strain 0.846 %,
Temperature 23.0 °C		725 psi
@Strain 0.846 %,
Temperature 73.4 °F		10000h; Isochronous; ISO 899
 10.0 MPa
@Strain 2.42 %,
Temperature 23.0 °C		1450 psi
@Strain 2.42 %,
Temperature 73.4 °F		10000h; Isochronous; ISO 899
 10.0 MPa
@Strain 1.40 %,
Temperature 23.0 °C		1450 psi
@Strain 1.40 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 10.0 MPa
@Strain 0.933 %,
Temperature 23.0 °C		1450 psi
@Strain 0.933 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity  >= 1.00e+15 ohm-cm
@Temperature 23.0 °C		>= 1.00e+15 ohm-cm
@Temperature 73.4 °F		IEC 60093
 1.00e+16 ohm-cm
@Temperature 23.0 °C		1.00e+16 ohm-cm
@Temperature 73.4 °F		ASTM D257
Surface Resistance  1.00e+14 ohm
@Temperature 23.0 °C		1.00e+14 ohm
@Temperature 73.4 °F		ASTM D257
 1.00e+15 ohm
@Temperature 23.0 °C		1.00e+15 ohm
@Temperature 73.4 °F		IEC 60093
Dielectric Constant  3.4
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		3.4
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		IEC 60250
 3.5
@Frequency 1000 Hz,
Temperature 23.0 °C		3.5
@Frequency 1000 Hz,
Temperature 73.4 °F		IEC 60250
 3.7
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		3.7
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		ASTM D150
 3.8
@Frequency 1000 Hz,
Temperature 23.0 °C		3.8
@Frequency 1000 Hz,
Temperature 73.4 °F		ASTM D150
Dielectric Strength  15.0 kV/mm
@Thickness 3.20 mm,
Temperature 23.0 °C		381 kV/in
@Thickness 0.126 in,
Temperature 73.4 °F		Short Time; ASTM D149
 16.0 kV/mm
@Thickness 2.00 mm,
Temperature 150 °C		406 kV/in
@Thickness 0.0787 in,
Temperature 302 °F		IEC 60243-1
 21.0 kV/mm
@Thickness 2.00 mm,
Temperature 100 °C		533 kV/in
@Thickness 0.0787 in,
Temperature 212 °F		IEC 60243-1
 23.0 kV/mm
@Thickness 1.60 mm,
Temperature 23.0 °C		584 kV/in
@Thickness 0.0630 in,
Temperature 73.4 °F		Short Time; ASTM D149
 23.0 kV/mm
@Thickness 2.00 mm,
Temperature 23.0 °C		584 kV/in
@Thickness 0.0787 in,
Temperature 73.4 °F		IEC 60243-1
Dissipation Factor  0.0030
@Frequency 1000 Hz,
Temperature 23.0 °C		0.0030
@Frequency 1000 Hz,
Temperature 73.4 °F		ASTM D150
 0.0030
@Frequency 1000 Hz,
Temperature 23.0 °C		0.0030
@Frequency 1000 Hz,
Temperature 73.4 °F		IEC 60250
 0.019
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.019
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		IEC 60250
 0.020
@Frequency 100 Hz,
Temperature 23.0 °C		0.020
@Frequency 100 Hz,
Temperature 73.4 °F		IEC 60250
 0.021
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.021
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		ASTM D150
Comparative Tracking Index 600 V
@Temperature 23.0 °C		600 V
@Temperature 73.4 °F		IEC 60112
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow  500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		ASTM E 831
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		ISO 11359-1/-2
CTE, linear, Transverse to Flow  190 µm/m-°C
@Temperature 23.0 - 55.0 °C		106 µin/in-°F
@Temperature 73.4 - 131 °F		ASTM E 831
 190 µm/m-°C
@Temperature 23.0 - 55.0 °C		106 µin/in-°F
@Temperature 73.4 - 131 °F		ISO 11359-1/-2
Melting Point 225 °C437 °FASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 100 °C212 °FISO 75-1/-2
 120 °C248 °FASTM D648
 145 °C293 °FAnnealed; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 47.0 °C117 °FASTM D648
 50.0 °C122 °FISO 75-1/-2
UL RTI, Electrical 75.0 °C
@Thickness 0.800 mm		167 °F
@Thickness 0.0315 in		UL 746B
UL RTI, Mechanical with Impact 75.0 °C
@Thickness 0.800 mm		167 °F
@Thickness 0.0315 in		UL 746B
UL RTI, Mechanical without Impact 75.0 °C
@Thickness 0.800 mm		167 °F
@Thickness 0.0315 in		UL 746B
Flammability, UL94  HB
@Thickness 0.800 mm		HB
@Thickness 0.0315 in		IEC 60695-11-10
 HB
@Thickness 0.800 mm		HB
@Thickness 0.0315 in		UL94
Oxygen Index 19 %19 %ISO 4589-1/-2
 22 %22 %ASTM D2863
Glow Wire Test 700 °C
@Thickness 3.00 mm		1290 °F
@Thickness 0.118 in		IEC 60695-2-12
 
Processing PropertiesMetricEnglishComments
Melt Temperature 225 °C437 °F10°C/min; ISO 11357-1/-3
 250 °C482 °FOptimum
 240 - 260 °C464 - 500 °F
Mold Temperature 80.0 °C176 °Foptimum
 30.0 - 130 °C86.0 - 266 °F
Drying Temperature 110 - 130 °C230 - 266 °F
Dry Time 2.00 - 4.00 hour2.00 - 4.00 hour
Moisture Content <= 0.040 %<= 0.040 %
 
Descriptive Properties
AdditiveImpact Modifier
 Lubricant
AppearanceNatural Color
Drying RecommendedYes
Extrudable - SheetYes
Extrudable - TubingYes
Extrudable - Wire and CableYes
FeaturesChemical Resistance, Good
 Dimensional Stability, Good
 Elongation, Good
 Impact Resistance, High
 Moisture Absorption, Low
 Processability, Good
 Toughness, Good
FormsPellets
GenericPBT
Material StatusCurrent
Part Marking Code>PBT-HI<ISO 11469
Polymer FamilyPolyester
Polymer TypePBT
Processing MethodExtrusion
 Injection Molding
Product CategoryExtrusion Resins
 Toughened Resins
 Unreinforced Resins
Region Available - GlobalYes
Resin IdentificationPBT-HIISO 1043
RoHS ComplianceContact Manufacturer
Ultrasonic WeldableYes
UsesAutomotive Applications
 Industrial Applications
 Parts, Engineering

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-38119.html

免责声明: 本文 DuPont Performance Polymers Crastin® ST820 NC010 PBT 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4