- 缺口冲击强度: 0.343
- 弯曲模量 [MPa]: 2.1582
- 热变形温度 [℃]: 155.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.31 g/cc | 1.31 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.016 cm/cm | 0.016 in/in | |
| Linear Mold Shrinkage, Transverse | 0.030 cm/cm | 0.030 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength | 53.955 MPa | 7825.5 psi | ASTM D638 |
| Elongation at Break | >= 100 % | >= 100 % | ASTM D638 |
| Flexural Strength | 78.48 MPa | 11380 psi | ASTM D790 |
| Flexural Modulus | 2.1582 GPa | 313.02 ksi | ASTM D790 |
| Izod Impact, Notched | 0.343 J/cm | 0.643 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 155 °C | 311 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 57.0 °C | 135 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 230 - 250 °C | 446 - 482 °F | |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | |