- 密度 [g/cm3]: 1.22
- 缺口冲击强度: 12.0
- 拉伸强度 [MPa]: 40.0
Physical Properties | Metric | English | Comments | ||
---|---|---|---|---|---|
Density | 1.22 g/cc | 0.0441 lb/in³ | ISO 1183 | ||
Moisture Absorption | 0.200 % @Temperature 23.0 °C | 0.200 % @Temperature 73.4 °F | 50% RH; ISO 960 | ||
Linear Mold Shrinkage, Flow | 0.018 cm/cm | 0.018 in/in | Eurotec | ||
Linear Mold Shrinkage, Transverse | 0.018 cm/cm | 0.018 in/in | Eurotec | ||
Mechanical Properties | Metric | English | Comments | ||
Tensile Strength, Yield | 40.0 MPa | 5800 psi | ISO 527 | ||
Tensile Modulus | 1.75 GPa | 254 ksi | ISO 527 | ||
Izod Impact, Notched (ISO) | 12.0 kJ/m² @Temperature -30.0 °C | 5.71 ft-lb/in² @Temperature -22.0 °F | ISO 180/1A | ||
15.0 kJ/m² @Temperature 23.0 °C | 7.14 ft-lb/in² @Temperature 73.4 °F | ISO 180/1A | |||
Izod Impact, Unnotched (ISO) | NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 180/1U | ||
NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 180/1U | |||
Electrical Properties | Metric | English | Comments | ||
Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 60093 | ||
Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | IEC 60093 | ||
Thermal Properties | Metric | English | Comments | ||
Melting Point | 225 °C | 437 °F | [10 K/min], ISO 11357 | ||
Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | ISO 75 | ||
Flammability, UL94 | HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | |||
HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | ||||
Processing Properties | Metric | English | Comments | ||
Processing Temperature | 240 - 260 °C | 464 - 500 °F | |||
Feed Temperature | 50.0 - 70.0 °C | 122 - 158 °F | Throat | ||
Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | |||
Drying Temperature | 120 °C | 248 °F | |||
Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | |||
Moisture Content | <= 0.080 % | <= 0.080 % | ISO 960 | ||
Hold Pressure | 40.0 - 80.0 MPa | 5800 - 11600 psi | |||
Descriptive Properties | |||||
Back Pressure | Low | ||||
Injection Speed | Medium - Fast |