- 密度 [g/cm3]: 1.5
- 吸水率 [%]: 0.06
- 缺口冲击强度: 1.0
- 弯曲强度 [MPa]: 110.0
- 弯曲模量 [MPa]: 6.90
- 热变形温度 [℃]: 215.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.50 g/cc | 0.0542 lb/in³ | ASTM D792 |
| Water Absorption | 0.060 % | 0.060 % | 24 hrs; ASTM D570 |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 110 MPa | 16000 psi | ASTM D638 |
| Flexural Modulus | 6.90 GPa | 1000 ksi | ASTM D790 |
| Izod Impact, Notched | 1.00 J/cm | 1.87 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 23.0 µm/m-°C @Temperature 20.0 °C | 12.8 µin/in-°F @Temperature 68.0 °F | ASTM E831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 176 °C | 349 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 257 °C | 495 °F | |
| Mold Temperature | 76.0 °C | 169 °F | |
| Drying Temperature | 121 °C | 250 °F | |