- 缺口冲击强度: 1.3
- 拉伸强度 [MPa]: 60.7
- 弯曲模量 [MPa]: 2.34
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.21 g/cc | 1.21 g/cc | ASTM D792 | ||
| Linear Mold Shrinkage, Flow | 0.0070 - 0.0090 cm/cm | 0.0070 - 0.0090 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 60.7 MPa | 8800 psi | Type I, 5.1 mm/min; ASTM D638 | ||
| Elongation at Break | 110 % | 110 % | Type I, 5.1 mm/min; ASTM D638 | ||
| Flexural Strength | 89.6 MPa | 13000 psi | ASTM D790 | ||
| Flexural Modulus | 2.34 GPa | 339 ksi | ASTM D790 | ||
| Izod Impact, Notched | 1.30 J/cm @Thickness 1.57 mm, Temperature -20.0 °C | 2.44 ft-lb/in @Thickness 0.0618 in, Temperature -4.00 °F | Injection Molded; ASTM D256A | ||
| 8.00 J/cm @Thickness 3.18 mm, Temperature 23.0 °C | 15.0 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F | Injection Molded; ASTM D256A | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 98.3 °C @Thickness 6.35 mm | 209 °F @Thickness 0.250 in | Unannealed; ASTM D648 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 260 - 277 °C | 500 - 531 °F | |||
| Mold Temperature | 65.6 - 87.8 °C | 150 - 190 °F | |||
| Drying Temperature | 110 °C | 230 °F | |||
| Dry Time | 2.00 hour | 2.00 hour | |||
| Descriptive Properties | |||||
| Additive | UV Stabilizer | ||||
| Features | High Flow | ||||
| Forms | Pellets | ||||
| Generic Material | PC+PBT | ||||
| Generic Name | Polycarbonate + PBT (PC+PBT) | ||||
| Regional Availability | Africa & Middle East | ||||
| Asia Pacific | |||||
| Europe | |||||
| North America | |||||
| South America | |||||