- 缺口冲击强度: 1.01
- 拉伸强度 [MPa]: 84.8
- 弯曲模量 [MPa]: 4.55
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.30 g/cc | 1.30 g/cc | ASTM D792 | ||
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 84.8 MPa | 12300 psi | Type I, 5.1 mm/min; ASTM D638 | ||
| Elongation at Break | 4.5 % | 4.5 % | Type I, 5.1 mm/min; ASTM D638 | ||
| Flexural Strength | 135 MPa | 19600 psi | ASTM D790 | ||
| Flexural Modulus | 4.55 GPa | 660 ksi | ASTM D790 | ||
| Izod Impact, Notched | 1.01 J/cm @Thickness 3.18 mm, Temperature -20.0 °C | 1.89 ft-lb/in @Thickness 0.125 in, Temperature -4.00 °F | Injection Molded; ASTM D256A | ||
| 1.33 J/cm @Thickness 3.18 mm, Temperature 23.0 °C | 2.49 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F | Injection Molded; ASTM D256A | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 113 °C @Thickness 6.35 mm | 235 °F @Thickness 0.250 in | Annealed; ASTM D648 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 260 - 282 °C | 500 - 540 °F | |||
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |||
| Drying Temperature | 110 °C @Time 7200 sec | 230 °F @Time 2.00 hour | |||
| Descriptive Properties | |||||
| Forms | Pellets | ||||
| Generic Name | Polycarbonate + PBT (PC+PBT) | ||||
| Regional Availability | Africa & Middle East | ||||
| Asia Pacific | |||||
| Europe | |||||
| North America | |||||
| South America | |||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.