- 缺口冲击强度: 0.347
- 弯曲强度 [MPa]: 41.4
- 弯曲模量 [MPa]: 2.83
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.50 g/cc | 1.50 g/cc | ASTM D792 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 41.4 MPa | 6000 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 | ||
| Elongation at Break | 3.0 % | 3.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 | ||
| Tensile Modulus | 2.83 GPa | 410 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 | ||
| Flexural Strength | 77.2 MPa | 11200 psi | ASTM D790 | ||
| Flexural Modulus | 2.83 GPa | 410 ksi | ASTM D790 | ||
| Izod Impact, Notched | 0.347 J/cm @Thickness 6.35 mm, Temperature 23.0 °C | 0.650 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F | Method A, Injection Molded; ASTM D256 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 238 - 266 °C | 460 - 510 °F | Molding | ||
| Mold Temperature | 54.4 - 93.3 °C | 130 - 200 °F | |||
| Drying Temperature | 104 °C | 220 °F | |||
| Dry Time | 2 hour | 2 hour | |||
| Descriptive Properties | |||||
| Product Form | Pellets | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.