- 缺口冲击强度: 0.374
- 拉伸强度 [MPa]: 57.2
- 弯曲模量 [MPa]: 2.60
- 热变形温度 [℃]: 155.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.31 g/cc | 1.31 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0180 - 0.0200 cm/cm | 0.0180 - 0.0200 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 78.0 | 78.0 | ISO 2039-2 |
| Tensile Strength at Break | 55.8 MPa | 8100 psi | ASTM D638 |
| Tensile Strength, Yield | 57.2 MPa | 8300 psi | ASTM D638 |
| 60.0 MPa | 8700 psi | 50mm/min; ISO 527-2/1A | |
| Elongation at Break | 30.0 % | 30.0 % | 50mm/min; ISO 527-2/1A |
| Elongation at Yield | 4.00 % | 4.00 % | 50mm/min; ISO 527-2/1A |
| Tensile Modulus | 2.70 GPa | 392 ksi | 1mm/min; ISO 527-2/1A |
| Flexural Strength | 85.0 MPa | 12300 psi | ISO 178 |
| 85.5 MPa | 12400 psi | ASTM D790 | |
| Flexural Modulus | 2.60 GPa | 377 ksi | ISO 178 |
| 2.48 GPa @Temperature 22.8 °C | 360 ksi @Temperature 73.0 °F | ASTM D790 | |
| Izod Impact, Notched | 0.374 J/cm | 0.700 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 3.20 kJ/m² | 1.52 ft-lb/in² | ISO 180/1A |
| Charpy Impact Unnotched | 10.0 J/cm² | 47.6 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| 1.00e+17 ohm-cm | 1.00e+17 ohm-cm | IEC 60093 | |
| Dielectric Constant | 3.20 @Frequency 1.00e+6 Hz | 3.20 @Frequency 1.00e+6 Hz | IEC 60250 |
| Dielectric Strength | 15.0 kV/mm | 381 kV/in | IEC 60243-1 |
| 16.5 kV/mm | 420 kV/in | short term; ASTM D149 | |
| Dissipation Factor | 0.000 @Frequency 1.00e+6 Hz | 0.000 @Frequency 1.00e+6 Hz | IEC 60250 |
| Comparative Tracking Index | >= 600 V | >= 600 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 155 °C | 311 °F | ISO 75-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ISO 75-1, -2 |
| Flammability, UL94 | HB | HB | UL94 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | |
| 65.0 - 93.0 °C | 149 - 199 °F | Cavity temperature | |
| Feed Temperature | 230 - 240 °C | 446 - 464 °F | |
| Zone 1 | 230 - 240 °C | 446 - 464 °F | |
| Zone 2 | 235 - 250 °C | 455 - 482 °F | |
| Zone 3 | 235 - 250 °C | 455 - 482 °F | |
| Zone 4 | 240 - 260 °C | 464 - 500 °F | |
| Die Temperature | 250 - 260 °C | 482 - 500 °F | |
| Melt Temperature | 235 - 260 °C | 455 - 500 °F | |
| Hot-Working Temperature | 250 - 260 °C | 482 - 500 °F | |