- 密度 [g/cm3]: 1.5
- 缺口冲击强度: 10.0
- 弯曲模量 [MPa]: 9.00
- 热变形温度 [℃]: 222.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.50 g/cc | 0.0542 lb/in³ | ISO 1183 | ||
| Moisture Absorption | 0.160 % | 0.160 % | 23°C/50%RH; ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.000 - 0.00500 cm/cm | 0.000 - 0.00500 in/in | ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.00700 cm/cm | 0.00700 in/in | ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 115 MPa | 16700 psi | 5mm/min; ISO 527-2/1A | ||
| Elongation at Break | 2.80 % | 2.80 % | 5mm/min; ISO 527-2/1A | ||
| Tensile Modulus | 8.70 GPa | 1260 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Strength | 190 MPa | 27600 psi | ISO 178 | ||
| Flexural Modulus | 9.00 GPa | 1310 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | ISO 180/1A | ||
| Izod Impact, Unnotched (ISO) | 49.0 kJ/m² | 23.3 ft-lb/in² | ISO 180/1U | ||
| 32.0 kJ/m² @Temperature -30.0 °C | 15.2 ft-lb/in² @Temperature -22.0 °F | ISO 180/1U | |||
| Charpy Impact Unnotched | 5.30 J/cm² | 25.2 ft-lb/in² | ISO 179/1eU | ||
| 3.80 J/cm² @Temperature -30.0 °C | 18.1 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | ISO 179/1eA | ||
| 1.00 J/cm² @Temperature -30.0 °C | 4.76 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+17 ohm-cm | 1.00e+17 ohm-cm | IEC 60093 | ||
| Surface Resistance | 2.00e+17 ohm | 2.00e+17 ohm | IEC 60093 | ||
| Dielectric Constant | 2.80 @Frequency 100 Hz | 2.80 @Frequency 100 Hz | IEC 60250 | ||
| 2.80 @Frequency 1.00e+6 Hz | 2.80 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Dielectric Strength | 38.0 kV/mm | 965 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.0110 @Frequency 1.00e+6 Hz | 0.0110 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Comparative Tracking Index | 450 V | 450 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 24.0 µm/m-°C | 13.3 µin/in-°F | ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 86.0 µm/m-°C | 47.8 µin/in-°F | ISO 11359-2 | ||
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 222 °C | 432 °F | ISO 75-1, -2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 208 °C | 406 °F | ISO 75-1, -2 | ||
| Flammability, UL94 | HB | HB | UL94 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | |||
| 65.0 - 93.0 °C | 149 - 199 °F | Cavity temperature | |||
| Feed Temperature | 230 - 245 °C | 446 - 473 °F | |||
| Rear Barrel Temperature | 230 - 240 °C | 446 - 464 °F | |||
| Middle Barrel Temperature | 235 - 250 °C | 455 - 482 °F | |||
| Front Barrel Temperature | 240 - 260 °C | 464 - 500 °F | |||
| Nozzle Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Zone 1 | 230 - 245 °C | 446 - 473 °F | |||
| Zone 2 | 240 - 250 °C | 464 - 482 °F | |||
| Zone 3 | 240 - 250 °C | 464 - 482 °F | |||
| Zone 4 | 245 - 260 °C | 473 - 500 °F | |||
| Die Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Melt Temperature | 235 - 260 °C | 455 - 500 °F | |||
| 240 - 260 °C | 464 - 500 °F | ||||
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |||
| Drying Temperature | 120 - 130 °C | 248 - 266 °F | |||
| Dry Time | 4.00 hour | 4.00 hour | |||
| Moisture Content | 0.0200 % | 0.0200 % | Necessary low maximum residual | ||
| Back Pressure | 0.000 - 0.345 MPa | 0.000 - 50.0 psi | |||
| Hot-Working Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Descriptive Properties | |||||
| Injection molding | Yes | ||||
| Injection speed | medium-fast | ||||
| Longer pre-drying times/storage | lower the temperature to 100° C until processed. | <= 60 h | |||
| Processing Notes | Fast Injection Speed | ||||
| Medium Screw Speed | |||||