- 熔体流动速率 [g/10min]: 18.0
- 密度 [g/cm3]: 1.53
- 缺口冲击强度: 7.4
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.53 g/cc | 0.0553 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.00300 - 0.00500 cm/cm | 0.00300 - 0.00500 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.00800 - 0.0100 cm/cm | 0.00800 - 0.0100 in/in | ISO 294-4 |
| Melt Flow | 18.0 g/10 min @Load 5.00 kg, Temperature 250 °C | 18.0 g/10 min @Load 11.0 lb, Temperature 482 °F | (MVR) cm³/10min; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 83.0 | 83.0 | ISO 2039-2 |
| Tensile Strength at Break | 102 MPa | 14800 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 2.10 % | 2.10 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 9.80 GPa | 1420 ksi | 1mm/min; ISO 527-2/1A |
| Izod Impact, Notched (ISO) | 7.40 kJ/m² | 3.52 ft-lb/in² | ISO 180/1A |
| Charpy Impact Unnotched | 3.50 J/cm² | 16.7 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.690 J/cm² | 3.28 ft-lb/in² | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 2.00e+16 ohm-cm | 2.00e+16 ohm-cm | IEC 60093 |
| Surface Resistance | 4.00e+16 ohm | 4.00e+16 ohm | IEC 60093 |
| Dielectric Constant | 3.60 @Frequency 1.00e+6 Hz | 3.60 @Frequency 1.00e+6 Hz | IEC 60250 |
| Dissipation Factor | 0.0140 @Frequency 1.00e+6 Hz | 0.0140 @Frequency 1.00e+6 Hz | IEC 60250 |
| Comparative Tracking Index | 525 V | 525 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 203 °C | 397 °F | ISO 75-1, -2 |
| Vicat Softening Point | 207 °C | 405 °F | B50 (50°C/h 50N); ISO 306 |
| Flammability, UL94 | V-0 @Thickness 0.400 mm | V-0 @Thickness 0.0157 in | UL94 |