- 密度 [g/cm3]: 1.3
- 吸水率 [%]: 0.08
- 缺口冲击强度: 4.8
- 弯曲强度 [MPa]: 53.0
- 弯曲模量 [MPa]: 2.28
- 热变形温度 [℃]: 166.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ASTM D792 |
| Water Absorption | 0.080 % | 0.080 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.019 cm/cm | 0.019 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 53.0 MPa | 7690 psi | ISO 527 |
| Elongation at Break | 180 % | 180 % | ASTM D638 |
| Flexural Strength | 69.0 MPa | 10000 psi | ISO 178 |
| Flexural Modulus | 2.28 GPa | 331 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 4.80 kJ/m² | 2.28 ft-lb/in² | ISO 180/1A |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.20e+17 ohm-cm | >= 1.20e+17 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.2 @Frequency 100 Hz | 3.2 @Frequency 100 Hz | |
| Dielectric Strength | 15.0 kV/mm @Thickness 3.17 mm | 381 kV/in @Thickness 0.125 in | 50% RH; ASTM D149 |
| Dissipation Factor | 0.0010 @Frequency 100 Hz | 0.0010 @Frequency 100 Hz | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 166 °C | 331 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | UL94 |