- 熔体流动速率 [g/10min]: 20.0
- 密度 [g/cm3]: 1.38
- 拉伸强度 [MPa]: 50.0
- 热变形温度 [℃]: 130.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.38 g/cc | 0.0499 lb/in³ | |
| Melt Flow | 20 g/10 min | 20 g/10 min | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | |
| Elongation at Break | >= 50 % | >= 50 % | |
| Elongation at Yield | 8.0 % | 8.0 % | |
| Modulus of Elasticity | 2.00 GPa | 290 ksi | |
| Charpy Impact Unnotched | 14.0 J/cm² | 66.6 ft-lb/in² | |
| 8.00 J/cm² @Temperature -30.0 °C | 38.1 ft-lb/in² @Temperature -22.0 °F | ||
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | |
| 0.400 J/cm² @Temperature -30.0 °C | 1.90 ft-lb/in² @Temperature -22.0 °F | ||
| Tensile Impact Strength | 65.0 kJ/m² | 30.9 ft-lb/in² | |
| Tensile Creep Modulus, 1 hour | 1900 MPa | 276000 psi | |
| Tensile Creep Modulus, 1000 hours | 1000 MPa | 145000 psi | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | |
| Dielectric Constant | 3.0 @Frequency 100 Hz | 3.0 @Frequency 100 Hz | |
| 3.0 @Frequency 1e+6 Hz | 3.0 @Frequency 1e+6 Hz | ||
| Dielectric Strength | 25.0 kV/mm | 635 kV/in | |
| Dissipation Factor | 0.0070 @Frequency 100 Hz | 0.0070 @Frequency 100 Hz | |
| 0.021 @Frequency 1e+6 Hz | 0.021 @Frequency 1e+6 Hz | ||
| Comparative Tracking Index | 275 V | 275 V | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 100 µm/m-°C @Temperature 20.0 °C | 55.6 µin/in-°F @Temperature 68.0 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 130 °C | 266 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | |
| Vicat Softening Point | 150 °C | 302 °F | 50°C/hr/50 N |