- 熔体流动速率 [g/10min]: 11.79
- 密度 [g/cm3]: 1.31
- 吸水率 [%]: 0.45
- 拉伸强度 [MPa]: 55.0
- 热变形温度 [℃]: 150.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.31 g/cc | 0.0473 lb/in³ | ISO 1183 | ||
| Water Absorption at Saturation | 0.45 % | 0.45 % | ISO 62 | ||
| Linear Mold Shrinkage | 0.02 cm/cm @Thickness 2.00 mm | 0.02 in/in @Thickness 0.0787 in | sheet with film gate at rim, mold temperature 80°C | ||
| Linear Mold Shrinkage, Transverse | 0.017 cm/cm | 0.017 in/in | |||
| Melt Flow | 11.79 g/10 min @Load 2.16 kg, Temperature 250 °C | 11.79 g/10 min @Load 4.76 lb, Temperature 482 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 77 | 77 | ISO 868 | ||
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | ISO 527-1/2 | ||
| Elongation at Break | >= 50 % | >= 50 % | ISO 527-1/2 | ||
| Elongation at Yield | 9.0 % | 9.0 % | ISO 527-1/2 | ||
| Tensile Modulus | 2.60 GPa | 377 ksi | ISO 527-1/-2 | ||
| Charpy Impact Unnotched | 21.0 J/cm² @Temperature -30.0 °C | 99.9 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | ||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.550 J/cm² @Temperature -30.0 °C | 2.62 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | ||
| 0.650 J/cm² @Temperature 23.0 °C | 3.09 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 | ||
| Dielectric Constant | 3.3 @Frequency 100 Hz | 3.3 @Frequency 100 Hz | IEC 60250 | ||
| 3.5 @Frequency 1e+6 Hz | 3.5 @Frequency 1e+6 Hz | IEC 60250 | |||
| Dielectric Strength | 27.0 kV/mm | 686 kV/in | K20/P50; IEC 60243-1 | ||
| Dissipation Factor | 0.0020 @Frequency 100 Hz | 0.0020 @Frequency 100 Hz | IEC 60250 | ||
| 0.023 @Frequency 1e+6 Hz | 0.023 @Frequency 1e+6 Hz | IEC 60250 | |||
| Comparative Tracking Index | 575 V | 575 V | 100 drops value; IEC 60112 | ||
| 600 V | 600 V | Test Solution A CTI; IEC 60112 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 110 µm/m-°C @Temperature 23.0 - 55.0 °C | 61.1 µin/in-°F @Temperature 73.4 - 131 °F | Longitudinal; ISO 11359, DIN 53752 | ||
| CTE, linear, Transverse to Flow | 110 µm/m-°C @Temperature 23.0 - 55.0 °C | 61.1 µin/in-°F @Temperature 73.4 - 131 °F | ISO 11359, DIN 53752 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 150 °C | 302 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ISO 75-1/-2 | ||
| Vicat Softening Point | 180 °C | 356 °F | Method B, 50 N; ISO 306 | ||
| 220 °C | 428 °F | Method A, 10 N; ISO 306 | |||
| Flammability, UL94 | HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | IEC 60695 | ||
| HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | IEC 60695 | |||
| Oxygen Index | 23 % | 23 % | ISO 4589, ASTM D2863 | ||
| Descriptive Properties | |||||
| Electrolytic Corrosion | A1 | IEC 60426 | |||