- 密度 [g/cm3]: 1.4
- 吸水率 [%]: 0.45
- 拉伸强度 [MPa]: 60.0
- 热变形温度 [℃]: 190.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ISO 1183 | ||
| Water Absorption at Saturation | 0.45 % | 0.45 % | ISO 62 | ||
| Linear Mold Shrinkage | 0.012 - 0.014 cm/cm @Thickness 4.00 mm | 0.012 - 0.014 in/in @Thickness 0.157 in | sheets with film gate at rim, mold temperature 60°C | ||
| Linear Mold Shrinkage, Transverse | 0.012 - 0.014 cm/cm | 0.012 - 0.014 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 166 MPa | 24100 psi | H30; ISO 2039-1 | ||
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | ISO 527-1/2 | ||
| Elongation at Break | 5.5 % | 5.5 % | ISO 527-1/2 | ||
| Elongation at Yield | 4.0 % | 4.0 % | ISO 527-1/2 | ||
| Tensile Modulus | 3.20 GPa | 464 ksi | ISO 527-1/-2 | ||
| Charpy Impact Unnotched | 2.20 J/cm² @Temperature -30.0 °C | 10.5 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | ||
| 2.50 J/cm² @Temperature 23.0 °C | 11.9 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.300 J/cm² @Temperature -30.0 °C | 1.43 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | ||
| 0.300 J/cm² @Temperature 23.0 °C | 1.43 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | IEC 60093 | ||
| Dielectric Constant | 3.7 @Frequency 100 Hz | 3.7 @Frequency 100 Hz | IEC 60250 | ||
| Dielectric Strength | 27.0 kV/mm | 686 kV/in | K20/P50; IEC 60243-1 | ||
| Dissipation Factor | 0.010 @Frequency 100 Hz | 0.010 @Frequency 100 Hz | IEC 60250 | ||
| Comparative Tracking Index | 225 V | 225 V | 100 drops value; IEC 60112 | ||
| 250 V | 250 V | Test Solution A CTI; IEC 60112 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 100 µm/m-°C @Temperature 23.0 - 55.0 °C | 55.6 µin/in-°F @Temperature 73.4 - 131 °F | Longitudinal; ISO 11359, DIN 53752 | ||
| CTE, linear, Transverse to Flow | 100 µm/m-°C @Temperature 23.0 - 55.0 °C | 55.6 µin/in-°F @Temperature 73.4 - 131 °F | ISO 11359, DIN 53752 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 190 °C | 374 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 72.0 °C | 162 °F | ISO 75-1/-2 | ||
| Vicat Softening Point | 193 °C | 379 °F | Method B, 50 N; ISO 306 | ||
| 215 °C | 419 °F | Method A, 10 N; ISO 306 | |||
| Flammability, UL94 | HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | IEC 60695 | ||
| HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | IEC 60695 | |||
| Descriptive Properties | |||||
| Electrolytic Corrosion | A1 | IEC 60426 | |||