- 熔体流动速率 [g/10min]: 29.8
- 密度 [g/cm3]: 1.49
- 吸水率 [%]: 0.25
- 拉伸强度 [MPa]: 105.0
- 热变形温度 [℃]: 195.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.49 g/cc | 0.0538 lb/in³ | ISO 1183 | ||
| Water Absorption at Saturation | 0.25 % | 0.25 % | ISO 62 | ||
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | 4 mm sheets with film gate at rim, mold temperature 60°C | ||
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in | |||
| Melt Flow | 29.8 g/10 min @Load 2.16 kg, Temperature 260 °C | 29.8 g/10 min @Load 4.76 lb, Temperature 500 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 79 | 79 | ISO 868 | ||
| Ball Indentation Hardness | 105 MPa | 15200 psi | H30; ISO 2039-1 | ||
| Tensile Strength, Yield | 105 MPa | 15200 psi | ISO 527-1/2 | ||
| Elongation at Break | 5.5 % | 5.5 % | ISO 527-1/2 | ||
| Elongation at Yield | 5.0 % | 5.0 % | ISO 527-1/2 | ||
| Tensile Modulus | 5.20 GPa | 754 ksi | ISO 527-1/-2 | ||
| Charpy Impact Unnotched | 7.00 J/cm² @Temperature -30.0 °C | 33.3 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | ||
| 8.00 J/cm² @Temperature 23.0 °C | 38.1 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 1.30 J/cm² @Temperature -30.0 °C | 6.19 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | ||
| 1.80 J/cm² @Temperature 23.0 °C | 8.57 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 | ||
| Dielectric Constant | 4.7 @Frequency 100 Hz | 4.7 @Frequency 100 Hz | IEC 60250 | ||
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | K20/P50; IEC 60243-1 | ||
| Dissipation Factor | 0.020 @Frequency 100 Hz | 0.020 @Frequency 100 Hz | IEC 60250 | ||
| Comparative Tracking Index | 575 V | 575 V | 100 drops value; IEC 60112 | ||
| >= 600 V | >= 600 V | Test Solution A CTI; IEC 60112 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 50.0 µm/m-°C @Temperature 23.0 - 55.0 °C | 27.8 µin/in-°F @Temperature 73.4 - 131 °F | Longitudinal; ISO 11359, DIN 53752 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 195 °C | 383 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 175 °C | 347 °F | ISO 75-1/-2 | ||
| Vicat Softening Point | 165 °C | 329 °F | Method B, 50 N; ISO 306 | ||
| 190 °C | 374 °F | Method A, 10 N; ISO 306 | |||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | IEC 60695 | ||
| HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | IEC 60695 | |||
| Descriptive Properties | |||||
| Electrolytic Corrosion | A1 | IEC 60426 | |||