- 熔体流动速率 [g/10min]: 12.6
- 密度 [g/cm3]: 1.26
- 吸水率 [%]: 0.35
- 拉伸强度 [MPa]: 27.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.26 g/cc | 0.0455 lb/in³ | ISO 1183 |
| Water Absorption at Saturation | 0.35 % | 0.35 % | ISO 62 |
| Viscosity Test | 180 cm³/g | 180 cm³/g | Viscosity Number; ISO 1628-5 |
| Melt Flow | 12.6 g/10 min @Load 2.16 kg, Temperature 250 °C | 12.6 g/10 min @Load 4.76 lb, Temperature 482 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 65 | 65 | ISO 868 |
| Tensile Strength, Yield | 27.0 MPa | 3920 psi | ISO 527-2/1A |
| Elongation at Break | >= 50 % | >= 50 % | ISO 527-2/1A |
| Elongation at Yield | 25 % | 25 % | ISO 527-2/1A |
| Tensile Modulus | 0.500 GPa | 72.5 ksi | ISO 527-1/2 |
| Charpy Impact Unnotched | NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 179/1eU |
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179/1eU | |
| Charpy Impact, Notched | 0.800 J/cm² @Temperature -30.0 °C | 3.81 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA |
| 3.00 J/cm² @Temperature 23.0 °C | 14.3 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 170 µm/m-°C @Temperature 23.0 - 80.0 °C | 94.4 µin/in-°F @Temperature 73.4 - 176 °F | ISO 11359 |
| Melting Point | 200 - 205 °C | 392 - 401 °F | DSC |