- 密度 [g/cm3]: 1.3
- 吸水率 [%]: 0.06
- 弯曲模量 [MPa]: 3.50
- 热变形温度 [℃]: 215.0
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 1.30 g/cc | 0.0470 lb/in³ | ASTM D792 |
Water Absorption | 0.060 % | 0.060 % | 24 hr; ASTM D570 |
Linear Mold Shrinkage | 0.010 - 0.015 cm/cm | 0.010 - 0.015 in/in | ASTM D955 |
Mechanical Properties | Metric | English | Comments |
Tensile Strength at Break | 110 MPa | 16000 psi | ASTM D638 |
Elongation at Break | 15 % | 15 % | ASTM D638 |
Flexural Strength | 165 MPa | 23900 psi | ASTM D790 |
Flexural Modulus | 3.50 GPa | 508 ksi | ASTM D790 |
Charpy Impact Unnotched | 6.50 J/cm² | 30.9 ft-lb/in² | ISO179 |
Charpy Impact, Notched | 2.00 J/cm² | 9.52 ft-lb/in² | ISO179 |
Electrical Properties | Metric | English | Comments |
Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
Dielectric Constant | 3.1 @Frequency 1e+6 Hz | 3.1 @Frequency 1e+6 Hz | ASTM D150 |
Dielectric Strength | 23.0 kV/mm @Thickness 2.00 mm | 584 kV/in @Thickness 0.0787 in | ASTM D149 |
Dissipation Factor | 0.019 @Frequency 1e+6 Hz | 0.019 @Frequency 1e+6 Hz | ASTM D150 |
Comparative Tracking Index | 600 V @Thickness 3.20 mm | 600 V @Thickness 0.126 in | ASTM D3638 |
Thermal Properties | Metric | English | Comments |
CTE, linear | 82.0 µm/m-°C @Temperature -30.0 - 30.0 °C | 45.6 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D696 |
Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ASTM D648 |
Deflection Temperature at 1.8 MPa (264 psi) | 195 °C | 383 °F | ASTM D648 |
Flammability, UL94 | HB @Thickness 3.20 mm | HB @Thickness 0.126 in | |
Processing Properties | Metric | English | Comments |
Middle Barrel Temperature | 225 - 255 °C | 437 - 491 °F | |
Nozzle Temperature | 245 °C | 473 °F | |
Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |
Drying Temperature | 130 °C | 266 °F | |
Dry Time | 4 hour | 4 hour | |
Injection Pressure | 80.0 - 120 MPa | 11600 - 17400 psi | |
Back Pressure | 8.00 - 18.0 MPa | 1160 - 2610 psi | |
Screw Speed | <= 100 rpm | <= 100 rpm |