Beijing Chemical Industry KAIFA® 201-G0R PBT Resin

Beijing Chemical Industry KAIFA® 201-G0R PBT Resin 物性表: Beijing Chemical Industry KAIFA® 201-G0R PBT Resin物性表及特性介绍,Beijing Chemical Industry KAIFA® 201-G0R PBT Resin注塑参数详情,如需Beijing Chemical Industry KAIFA® 201-G0R PBT Resin下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.25
  • 吸水率 [%]: 0.07
  • 弯曲模量 [MPa]: 1.70
  • 热变形温度 [℃]: 170.0
 
Physical PropertiesMetricEnglishComments
Density 1.25 g/cc0.0452 lb/in³ASTM D792
Water Absorption 0.070 %0.070 %24 hr; ASTM D570
Linear Mold Shrinkage 0.028 - 0.036 cm/cm0.028 - 0.036 in/inASTM D955
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break 50.0 MPa7250 psiASTM D638
Elongation at Break 200 %200 %ASTM D638
Flexural Strength 90.0 MPa13100 psiASTM D790
Flexural Modulus 1.70 GPa247 ksiASTM D790
Charpy Impact Unnotched >= 20.1 J/cm²>= 95.7 ft-lb/in²ISO179
Charpy Impact, Notched 8.00 J/cm²38.1 ft-lb/in²ISO179
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity 1.00e+16 ohm-cm1.00e+16 ohm-cmASTM D257
Dielectric Constant 2.9
@Frequency 1e+6 Hz
2.9
@Frequency 1e+6 Hz
ASTM D150
Dielectric Strength 22.0 kV/mm
@Thickness 2.00 mm
559 kV/in
@Thickness 0.0787 in
ASTM D149
Dissipation Factor 0.020
@Frequency 1e+6 Hz
0.020
@Frequency 1e+6 Hz
ASTM D150
Comparative Tracking Index 600 V
@Thickness 3.20 mm
600 V
@Thickness 0.126 in
ASTM D3638
 
Thermal PropertiesMetricEnglishComments
CTE, linear 100 µm/m-°C
@Temperature -30.0 - 30.0 °C
55.6 µin/in-°F
@Temperature -22.0 - 86.0 °F
ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 170 °C338 °FASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 80.0 °C176 °FASTM D648
Flammability, UL94 HB
@Thickness 3.20 mm
HB
@Thickness 0.126 in
 
Processing PropertiesMetricEnglishComments
Middle Barrel Temperature 225 - 255 °C437 - 491 °F
Nozzle Temperature 245 °C473 °F
Mold Temperature 40.0 - 80.0 °C104 - 176 °F
Drying Temperature 130 °C266 °F
Dry Time 4 hour4 hour
Injection Pressure 80.0 - 120 MPa11600 - 17400 psi
Back Pressure 8.00 - 18.0 MPa1160 - 2610 psi
Screw Speed <= 100 rpm<= 100 rpm

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-38621.html

免责声明: 本文 Beijing Chemical Industry KAIFA® 201-G0R PBT Resin 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4