- 熔体流动速率 [g/10min]: 22.0
- 缺口冲击强度: 2.1
- 弯曲模量 [MPa]: 2.10
- 硬度: 105.0
- 热变形温度 [℃]: 95.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.07 g/cc @Temperature 23.0 °C | 1.07 g/cc @Temperature 73.4 °F | ASTM D792 | ||
| Linear Mold Shrinkage | 0.0060 - 0.0080 cm/cm @Temperature 23.0 °C | 0.0060 - 0.0080 in/in @Temperature 73.4 °F | Plumb; ASTM D955 | ||
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0060 cm/cm @Temperature 23.0 °C | 0.0050 - 0.0060 in/in @Temperature 73.4 °F | Parallel; ASTM D955 | ||
| Melt Flow | 22 g/10 min @Load 5.00 kg, Temperature 230 °C | 22 g/10 min @Load 11.0 lb, Temperature 446 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 105 | 105 | ASTM D785 | ||
| Tensile Strength at Break | 45.0 MPa | 6530 psi | 50mm/min; ASTM D638 | ||
| Elongation at Break | >= 20 % | >= 20 % | 50mm/min; ASTM D638 | ||
| Flexural Strength | 65.0 MPa | 9430 psi | 2mm/min; ASTM D790 | ||
| Flexural Modulus | 2.10 GPa | 305 ksi | 2mm/min; ASTM D790 | ||
| Izod Impact, Notched | 2.10 J/cm @Thickness 3.20 mm, Temperature 23.0 °C | 3.93 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F | ASTM D256 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 95.0 °C @Thickness 6.40 mm | 203 °F @Thickness 0.252 in | ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 84.0 °C @Thickness 6.40 mm | 183 °F @Thickness 0.252 in | ASTM D648 | ||
| Flammability, UL94 | V-2 @Thickness 3.20 mm | V-2 @Thickness 0.126 in | |||
| V-2 @Thickness 1.60 mm | V-2 @Thickness 0.0630 in | ||||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | <= 250 °C | <= 482 °F | |||
| Rear Barrel Temperature | 210 - 230 °C | 410 - 446 °F | Start Point: 215°C | ||
| Middle Barrel Temperature | 220 - 230 °C | 428 - 446 °F | Start Point: 225°C | ||
| Front Barrel Temperature | 220 - 240 °C | 428 - 464 °F | Start Point: 230°C | ||
| Melt Temperature | 220 - 240 °C | 428 - 464 °F | Start Point: 230°C | ||
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | Start Point: 60°C | ||
| Drying Temperature | 80.0 - 90.0 °C @Time 10800 - 14400 sec | 176 - 194 °F @Time 3.00 - 4.00 hour | Pre-dry | ||
| Back Pressure | 0.300 - 1.00 MPa | 43.5 - 145 psi | |||
| Descriptive Properties | |||||
| Injection Speed | 60-80% | ||||