- 熔体流动速率 [g/10min]: 21.0
- 缺口冲击强度: 10.0
- 弯曲模量 [MPa]: 12.8
- 热变形温度 [℃]: 250.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.74 g/cc | 1.74 g/cc | ISO 1183 | ||
| Bulk Density | 1.00 g/cc | 0.0361 lb/in³ | ISO 60 | ||
| Viscosity Test | 50 cm³/g | 50 cm³/g | Viscosity number; ISO 1628-5 | ||
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 | ||
| 0.0020 cm/cm | 0.0020 in/in | 60x60x2; 280°C / WZ 110°C; 600 bar; ISO 294-4 | |||
| Linear Mold Shrinkage, Transverse | 0.0020 cm/cm | 0.0020 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 | ||
| 0.0070 cm/cm | 0.0070 in/in | 60x60x2; 280°C / WZ 110°C; 600 bar; ISO 294-4 | |||
| Melt Flow | 21 g/10 min @Load 2.16 kg, Temperature 280 °C | 21 g/10 min @Load 4.76 lb, Temperature 536 °F | ISO 1133-1 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 110 MPa | 16000 psi | ISO 527-1, -2; 5 mm/min | ||
| Elongation at Break | 1.3 % | 1.3 % | ISO 527-1, -2; 5 mm/min | ||
| Tensile Modulus | 12.7 GPa | 1840 ksi | ISO 527-1, -2; 1 mm/min | ||
| Flexural Strength | 170 MPa @Strain 1.70 % | 24700 psi @Strain 1.70 % | 2 mm/min; ISO 178-A | ||
| Flexural Modulus | 12.8 GPa | 1860 ksi | 2 mm/min; ISO 178-A | ||
| Izod Impact, Notched (ISO) | <= 10.0 kJ/m² @Temperature 23.0 °C | <= 4.76 ft-lb/in² @Temperature 73.4 °F | ISO 180-1A | ||
| <= 10.0 kJ/m² @Temperature -30.0 °C | <= 4.76 ft-lb/in² @Temperature -22.0 °F | ISO 180-1A | |||
| Izod Impact, Unnotched (ISO) | 25.0 kJ/m² @Temperature 23.0 °C | 11.9 ft-lb/in² @Temperature 73.4 °F | ISO 180-1U | ||
| 25.0 kJ/m² @Temperature -30.0 °C | 11.9 ft-lb/in² @Temperature -22.0 °F | ISO 180-1U | |||
| Charpy Impact Unnotched | 2.50 J/cm² @Temperature -30.0 °C | 11.9 ft-lb/in² @Temperature -22.0 °F | ISO 179-1eU | ||
| 3.00 J/cm² @Temperature 23.0 °C | 14.3 ft-lb/in² @Temperature 73.4 °F | ISO 179-1eU | |||
| Charpy Impact, Notched | <= 1.00 J/cm² @Temperature 23.0 °C | <= 4.76 ft-lb/in² @Temperature 73.4 °F | ISO 179-1eA | ||
| <= 1.00 J/cm² @Temperature -30.0 °C | <= 4.76 ft-lb/in² @Temperature -22.0 °F | ISO 179-1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 2.00e+20 ohm-cm | 2.00e+20 ohm-cm | IEC 60093 | ||
| Surface Resistance | 5.40e+16 ohm | 5.40e+16 ohm | IEC 60093 | ||
| Dielectric Constant | 4.1 @Frequency 1.00e+6 Hz | 4.1 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 4.3 @Frequency 100 Hz | 4.3 @Frequency 100 Hz | IEC 60250 | |||
| Dielectric Strength | 33.0 kV/mm @Thickness 1.00 mm | 838 kV/in @Thickness 0.0394 in | IEC 60243-1 | ||
| Dissipation Factor | 0.0022 @Frequency 100 Hz | 0.0022 @Frequency 100 Hz | IEC 60250 | ||
| 0.0138 @Frequency 1.00e+6 Hz | 0.0138 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Comparative Tracking Index | 275 V | 275 V | d.a.m.; Solution A; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C @Temperature 23.0 - 55.0 °C | 11.1 µin/in-°F @Temperature 73.4 - 131 °F | ISO 11359-1, -2 | ||
| CTE, linear, Transverse to Flow | 50.0 µm/m-°C @Temperature 23.0 - 55.0 °C | 27.8 µin/in-°F @Temperature 73.4 - 131 °F | ISO 11359-1, -2 | ||
| Thermal Conductivity | 0.300 W/m-K | 2.08 BTU-in/hr-ft²-°F | ISO 8302 | ||
| Melting Point | 255 °C | 491 °F | 10°C/min; ISO 11357-1, -3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ISO 75-1, -2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75-1, -2 | ||
| Vicat Softening Point | 225 °C @Load 5.10 kg | 437 °F @Load 11.2 lb | 120°C/hour; ISO 306 | ||
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | |||
| 280 °C | 536 °F | for test specimens; ISO 294 | |||
| Mold Temperature | 110 °C | 230 °F | for test specimens; ISO 294 | ||
| 100 - 130 °C | 212 - 266 °F | ||||
| Drying Temperature | 120 °C | 248 °F | |||
| Dry Time | 4 - 8 hour | 4 - 8 hour | |||
| Moisture Content | 0.00 - 0.020 % | 0.00 - 0.020 % | residual; Karl Fischer Test | ||
| Descriptive Properties | |||||
| ISO Shortname | ISO 7792-1-PET+PBT, GHMR, 07-120, (GF+MD)44 | ||||