- 熔体流动速率 [g/10min]: 44.0
- 密度 [g/cm3]: 1.34
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | parallel; ISO 294-4, 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.0012 cm/cm | 0.0012 in/in | ISO 294-4, 2577 | ||
| Melt Flow | 44 g/10 min @Load 2.16 kg, Temperature 260 °C | 44 g/10 min @Load 4.76 lb, Temperature 500 °F | Estimated using room temperature density; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 70.0 MPa | 10200 psi | ISO 527-1/-2 | ||
| Elongation at Break | 3.5 % | 3.5 % | ISO 527-1/-2 | ||
| Tensile Modulus | 4.20 GPa | 609 ksi | ISO 527-1/-2 | ||
| Charpy Impact Unnotched | 4.00 J/cm² @Temperature 23.0 °C | 19.0 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | ||
| Charpy Impact, Notched | <= 1.00 J/cm² @Temperature 23.0 °C | <= 4.76 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 222 °C | 432 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 180 °C | 356 °F | ISO 75-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 260 °C | 500 °F | Injection Molding; ISO 294 | ||
| Mold Temperature | 80.0 °C | 176 °F | Injection Molding; ISO 10724 | ||
| Descriptive Properties | |||||
| Form | Pellets | ||||
| Processing | Injection molding | ||||