- 熔体流动速率 [g/10min]: 44.0
- 密度 [g/cm3]: 1.48
- 吸水率 [%]: 0.4
- 热变形温度 [℃]: 215.0
Physical Properties | Metric | English | Comments | ||
---|---|---|---|---|---|
Density | 1.48 g/cc | 0.0535 lb/in³ | ISO 1183 | ||
Water Absorption | 0.40 % | 0.40 % | Test Sim. to ISO 62 | ||
Moisture Absorption at Equilibrium | 0.10 % | 0.10 % | 23°C/50% R.H.; Test Sim. to ISO 62 | ||
Melt Flow | 44 g/10 min @Load 2.16 kg, Temperature 260 °C | 44 g/10 min @Load 4.76 lb, Temperature 500 °F | Estimated using room temperature density; ISO 1133 | ||
Mechanical Properties | Metric | English | Comments | ||
Tensile Strength at Break | 130 MPa | 18900 psi | ISO 527-1/-2 | ||
Elongation at Break | 2.7 % | 2.7 % | ISO 527-1/-2 | ||
Tensile Modulus | 9.20 GPa | 1330 ksi | ISO 527-1/-2 | ||
Charpy Impact Unnotched | 6.00 J/cm² @Temperature -30.0 °C | 28.6 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | ||
6.00 J/cm² @Temperature 23.0 °C | 28.6 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | |||
Electrical Properties | Metric | English | Comments | ||
Comparative Tracking Index | 525 V | 525 V | IEC 60112 | ||
Thermal Properties | Metric | English | Comments | ||
CTE, linear, Parallel to Flow | 30.0 µm/m-°C | 16.7 µin/in-°F | ISO 11359-1/-2 | ||
CTE, linear, Transverse to Flow | 130 µm/m-°C | 72.2 µin/in-°F | ISO 11359-1/-2 | ||
Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1/-3 | ||
Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ISO 75-1/-2 | ||
Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO 75-1/-2 | ||
Deflection Temperature at 8.0 MPa | 150 °C | 302 °F | ISO 75-1/-2 | ||
Flammability, UL94 | HB | HB | IEC 60695-11-10 | ||
HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | IEC 60695-11-10 | |||
Processing Properties | Metric | English | Comments | ||
Melt Temperature | 260 °C | 500 °F | Injection Molding; ISO 294 | ||
Mold Temperature | 80.0 °C | 176 °F | Injection Molding; ISO 10724 | ||
Descriptive Properties | |||||
Form | Pellets | ||||
ISO Shortname | ISO 7792-PBT, MHR, -090, GF30 | ||||
Processing | Injection molding | ||||
Region | Asia Pacific | ||||
Europe | |||||
Near East/Africa | |||||
North America | |||||
South and Central America |
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.
Users of our Advanced Search (registration required) may exclude discontinued materials from search results.