- 熔体流动速率 [g/10min]: 33.36
- 密度 [g/cm3]: 1.39
- 吸水率 [%]: 0.4
- 拉伸强度 [MPa]: 96.0
- 热变形温度 [℃]: 216.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.39 g/cc | 0.0502 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.40 % | 0.40 % | Saturation; DIN 53495/1L | ||
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C; 50% RH | ||
| Viscosity Measurement | 107 | 107 | [ml/g]; Viscosity number; ISO 1628 | ||
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | Sheet | ||
| Linear Mold Shrinkage, Transverse | 0.012 cm/cm | 0.012 in/in | Sheet | ||
| Melt Flow | 33.36 g/10 min @Load 2.16 kg, Temperature 275 °C | 33.36 g/10 min @Load 4.76 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 96.0 MPa | 13900 psi | 50 mm/min; ISO 527-2 | ||
| Elongation at Yield | 2.9 % | 2.9 % | 50 mm/min; ISO 527-2 | ||
| Modulus of Elasticity | 5.00 GPa | 725 ksi | ISO 527-2 | ||
| Charpy Impact Unnotched | 2.60 J/cm² | 12.4 ft-lb/in² | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.380 J/cm² | 1.81 ft-lb/in² | ISO 179/1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 - 250 °C | 428 - 482 °F | DSC; ISO 11357-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 216 °C | 421 °F | ISO 75-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 168 °C | 334 °F | ISO 75-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 250 - 275 °C | 482 - 527 °F | Injection-molding | ||
| 270 °C | 518 °F | for shrinkage test | |||
| Mold Temperature | 80.0 °C | 176 °F | for shrinkage test | ||
| 60.0 - 100 °C | 140 - 212 °F | ||||
| Descriptive Properties | |||||
| Color | Colored and Black | ||||
| Commercial Status | Europe | ||||
| Primary Processing Technique | Injection Molding | ||||