- 吸水率 [%]: 0.05
- 缺口冲击强度: 0.961
- 弯曲强度 [MPa]: 160.0
- 弯曲模量 [MPa]: 9.20
- 硬度: 121.0
- 热变形温度 [℃]: 247.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.58 g/cc | 1.58 g/cc | ASTM D792 |
| Water Absorption | 0.050 % | 0.050 % | 24 hr immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0020 - 0.0030 cm/cm | 0.0020 - 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 112 | 112 | ASTM D785 |
| Hardness, Rockwell R | 121 | 121 | ASTM D785 |
| Tensile Strength, Ultimate | 160 MPa | 23200 psi | ASTM D638 |
| Flexural Strength | 240 MPa | 34800 psi | ASTM D790 |
| Flexural Modulus | 9.20 GPa | 1330 ksi | ASTM D790 |
| Compressive Yield Strength | 233 MPa | 33800 psi | ASTM D695 |
| Izod Impact, Notched | 0.961 J/cm @Thickness 3.17 mm | 1.80 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 232 - 249 °C | 450 - 480 °F | ASTM D789 |
| Deflection Temperature at 0.46 MPa (66 psi) | 247 °C | 477 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 225 °C | 437 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | |