- 熔体流动速率 [g/10min]: 10.5
- 拉伸强度 [MPa]: 50.1
- 弯曲模量 [MPa]: 2.108
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.24 g/cc | 1.24 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0080 cm/cm | 0.0040 - 0.0080 in/in | ASTM D955 |
| Melt Flow | 10.5 g/10 min @Load 3.80 kg, Temperature 230 °C | 10.5 g/10 min @Load 8.38 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 50.1 MPa | 7270 psi | chs 2.0 in/min; ASTM D638 |
| Elongation at Yield | 4.1 % | 4.1 % | chs 2.0 in/min; ASTM D638 |
| Flexural Modulus | 2.108 GPa | 305.7 ksi | chs 0.05 in/min; ASTM D790 |
| Izod Impact, Notched | NB @Thickness 3.17 mm | NB @Thickness 0.125 in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 204 °C @Load 1.00 kg, Thickness 3.17 mm | 399 °F @Load 2.20 lb, Thickness 0.125 in | ASTM D1525 |
| Flammability, UL94 | V-0 @Thickness 3.17 mm | V-0 @Thickness 0.125 in | |
| V-0 @Thickness 1.59 mm | V-0 @Thickness 0.0625 in | ||