- 熔体流动速率 [g/10min]: 35.0
- 吸水率 [%]: 0.35
- 缺口冲击强度: 6.41
- 拉伸强度 [MPa]: 61.0
- 弯曲模量 [MPa]: 2.34
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.22 g/cc | 1.22 g/cc | ASTM D792 |
| Water Absorption | 0.35 % @Temperature 23.0 °C | 0.35 % @Temperature 73.4 °F | at equilibrium; ASTM D570 |
| 0.15 % @Temperature 23.0 °C, Time 86400 sec | 0.15 % @Temperature 73.4 °F, Time 24.0 hour | ASTM D570 | |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 35 g/10 min @Load 5.00 kg, Temperature 260 °C | 35 g/10 min @Load 11.0 lb, Temperature 500 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 61.0 MPa | 8850 psi | chs 2.0 in/min; ASTM D638 |
| Elongation at Break | 27 % | 27 % | ASTM D638 |
| Flexural Modulus | 2.34 GPa | 339 ksi | tangent; chs 0.05 in/min; ASTM D790 |
| Izod Impact, Notched | 6.41 J/cm @Thickness 3.17 mm, Temperature 23.0 °C | 12.0 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F | ASTM D256 |