DuPont Performance Polymers Rynite® 935 NC010 PET

DuPont Performance Polymers Rynite® 935 NC010 PET 物性表: DuPont Performance Polymers Rynite® 935 NC010 PET物性表及特性介绍,DuPont Performance Polymers Rynite® 935 NC010 PET注塑参数详情,如需DuPont Performance Polymers Rynite® 935 NC010 PET下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.58
  • 吸水率 [%]: 0.05
  • 成型收缩率 [%]: 0.0028
  • 缺口冲击强度: 0.43
  • 弯曲模量 [MPa]: 2.20
  • 硬度: 115.0
  • 热变形温度 [℃]: 235.0
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.58 g/cc1.58 g/ccASTM D792
Density 1.58 g/cc0.0571 lb/in³ISO 1183
Filler Content 35 %35 %
Water Absorption  0.050 %
@Temperature 23.0 °C		0.050 %
@Temperature 73.4 °F		50%RH,23°C,24h; ASTM D570
 0.13 %
@Temperature 23.0 °C		0.13 %
@Temperature 73.4 °F		Equilibrium 50%RH; ISO 62, Similar to
 0.83 %
@Temperature 23.0 °C		0.83 %
@Temperature 73.4 °F		Saturation, immersed; ISO 62, Similar to
Viscosity  30000 cP
@Shear Rate 7000 1/s,
Temperature 315 °C		30000 cP
@Shear Rate 7000 1/s,
Temperature 599 °F		ISO 11443
 37000 cP
@Shear Rate 5000 1/s,
Temperature 315 °C		37000 cP
@Shear Rate 5000 1/s,
Temperature 599 °F		ISO 11443
 48000 cP
@Shear Rate 7000 1/s,
Temperature 295 °C		48000 cP
@Shear Rate 7000 1/s,
Temperature 563 °F		ISO 11443
 57000 cP
@Shear Rate 5000 1/s,
Temperature 295 °C		57000 cP
@Shear Rate 5000 1/s,
Temperature 563 °F		ISO 11443
 61000 cP
@Shear Rate 2000 1/s,
Temperature 315 °C		61000 cP
@Shear Rate 2000 1/s,
Temperature 599 °F		ISO 11443
 77000 cP
@Shear Rate 7000 1/s,
Temperature 275 °C		77000 cP
@Shear Rate 7000 1/s,
Temperature 527 °F		ISO 11443
 89000 cP
@Shear Rate 1000 1/s,
Temperature 315 °C		89000 cP
@Shear Rate 1000 1/s,
Temperature 599 °F		ISO 11443
 93000 cP
@Shear Rate 5000 1/s,
Temperature 275 °C		93000 cP
@Shear Rate 5000 1/s,
Temperature 527 °F		ISO 11443
 95000 cP
@Shear Rate 2000 1/s,
Temperature 295 °C		95000 cP
@Shear Rate 2000 1/s,
Temperature 563 °F		ISO 11443
 109000 cP
@Shear Rate 700 1/s,
Temperature 315 °C		109000 cP
@Shear Rate 700 1/s,
Temperature 599 °F		ISO 11443
 130000 cP
@Shear Rate 500 1/s,
Temperature 315 °C		130000 cP
@Shear Rate 500 1/s,
Temperature 599 °F		ISO 11443
 139000 cP
@Shear Rate 1000 1/s,
Temperature 295 °C		139000 cP
@Shear Rate 1000 1/s,
Temperature 563 °F		ISO 11443
 153000 cP
@Shear Rate 2000 1/s,
Temperature 275 °C		153000 cP
@Shear Rate 2000 1/s,
Temperature 527 °F		ISO 11443
 169000 cP
@Shear Rate 700 1/s,
Temperature 295 °C		169000 cP
@Shear Rate 700 1/s,
Temperature 563 °F		ISO 11443
 203000 cP
@Shear Rate 500 1/s,
Temperature 295 °C		203000 cP
@Shear Rate 500 1/s,
Temperature 563 °F		ISO 11443
 224000 cP
@Shear Rate 1000 1/s,
Temperature 275 °C		224000 cP
@Shear Rate 1000 1/s,
Temperature 527 °F		ISO 11443
 272000 cP
@Shear Rate 700 1/s,
Temperature 275 °C		272000 cP
@Shear Rate 700 1/s,
Temperature 527 °F		ISO 11443
 327000 cP
@Shear Rate 500 1/s,
Temperature 275 °C		327000 cP
@Shear Rate 500 1/s,
Temperature 527 °F		ISO 11443
Linear Mold Shrinkage  0.0028 cm/cm
@Thickness 1.57 mm		0.0028 in/in
@Thickness 0.0618 in		Flow
 0.0035 cm/cm
@Thickness 3.20 mm		0.0035 in/in
@Thickness 0.126 in		Flow
 0.0052 cm/cm
@Thickness 1.57 mm		0.0052 in/in
@Thickness 0.0618 in		Transverse
 0.0065 cm/cm
@Thickness 3.20 mm		0.0065 in/in
@Thickness 0.126 in		Transverse
Linear Mold Shrinkage, Flow 0.0035 cm/cm0.0035 in/inParallel; Annealed; ISO 294-4
 0.0030 cm/cm
@Thickness 2.00 mm		0.0030 in/in
@Thickness 0.0787 in		Parallel; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0090 cm/cm0.0090 in/inNormal; Annealed; ISO 294-4
 0.0070 cm/cm
@Thickness 2.00 mm		0.0070 in/in
@Thickness 0.0787 in		Normal; ISO 294-4
Melt Index of Compound 5.0 g/10 min
@Load 5.00 kg,
Temperature 280 °C		5.0 g/10 min
@Load 11.0 lb,
Temperature 536 °F		cm3/10 min; ISO 1133
 
Mechanical PropertiesMetricEnglishComments
Hardness, Rockwell M 7575ASTM D785
 7575ISO 2039/2
Hardness, Rockwell R 115115ASTM D785
 115115ISO 2039/2
Tensile Strength at Break 85.0 MPa
@Temperature 23.0 °C		12300 psi
@Temperature 73.4 °F		ISO 527
Tensile Strength  29.7 MPa
@Temperature 150 °C		4310 psi
@Temperature 302 °F		ASTM D638
 40.7 MPa
@Temperature 90.0 °C		5900 psi
@Temperature 194 °F		ASTM D638
 89.6 MPa
@Temperature 23.0 °C		13000 psi
@Temperature 73.4 °F		ASTM D638
 121 MPa
@Temperature -40.0 °C		17500 psi
@Temperature -40.0 °F		ASTM D638
Tensile Stress  15.6 MPa
@Strain 0.310 %,
Temperature 60.0 °C		2260 psi
@Strain 0.310 %,
Temperature 140 °F		ISO 527
 16.9 MPa
@Strain 0.200 %,
Temperature 40.0 °C		2450 psi
@Strain 0.200 %,
Temperature 104 °F		ISO 527
 17.7 MPa
@Strain 0.610 %,
Temperature 90.0 °C		2570 psi
@Strain 0.610 %,
Temperature 194 °F		ISO 527
 17.8 MPa
@Strain 0.760 %,
Temperature 120 °C		2580 psi
@Strain 0.760 %,
Temperature 248 °F		ISO 527
 19.5 MPa
@Strain 0.210 %,
Temperature 23.0 °C		2830 psi
@Strain 0.210 %,
Temperature 73.4 °F		ISO 527
 25.0 MPa
@Strain 1.50 %,
Temperature 120 °C		3630 psi
@Strain 1.50 %,
Temperature 248 °F		ISO 527
 27.51 MPa
@Strain 1.25 %,
Temperature 90.0 °C		3990 psi
@Strain 1.25 %,
Temperature 194 °F		ISO 527
 28.21 MPa
@Strain 2.23 %,
Temperature 120 °C		4092 psi
@Strain 2.23 %,
Temperature 248 °F		ISO 527
 29.95 MPa
@Strain 2.96 %,
Temperature 120 °C		4344 psi
@Strain 2.96 %,
Temperature 248 °F		ISO 527
 30.9 MPa
@Strain 0.350 %,
Temperature 23.0 °C		4480 psi
@Strain 0.350 %,
Temperature 73.4 °F		ISO 527
 31.06 MPa
@Strain 3.69 %,
Temperature 120 °C		4505 psi
@Strain 3.69 %,
Temperature 248 °F		ISO 527
 31.3 MPa
@Strain 0.400 %,
Temperature 40.0 °C		4540 psi
@Strain 0.400 %,
Temperature 104 °F		ISO 527
 31.83 MPa
@Strain 4.42 %,
Temperature 120 °C		4617 psi
@Strain 4.42 %,
Temperature 248 °F		ISO 527
 32.0 MPa
@Strain 0.720 %,
Temperature 60.0 °C		4640 psi
@Strain 0.720 %,
Temperature 140 °F		ISO 527
 32.13 MPa
@Strain 1.84 %,
Temperature 90.0 °C		4660 psi
@Strain 1.84 %,
Temperature 194 °F		ISO 527
 32.4 MPa
@Strain 5.15 %,
Temperature 120 °C		4700 psi
@Strain 5.15 %,
Temperature 248 °F		ISO 527
 32.84 MPa
@Strain 5.88 %,
Temperature 120 °C		4763 psi
@Strain 5.88 %,
Temperature 248 °F		ISO 527
 33.17 MPa
@Strain 6.61 %,
Temperature 120 °C		4811 psi
@Strain 6.61 %,
Temperature 248 °F		ISO 527
 33.31 MPa
@Strain 7.34 %,
Temperature 120 °C		4831 psi
@Strain 7.34 %,
Temperature 248 °F		ISO 527
 34.76 MPa
@Strain 2.48 %,
Temperature 90.0 °C		5042 psi
@Strain 2.48 %,
Temperature 194 °F		ISO 527
 36.11 MPa
@Strain 3.06 %,
Temperature 90.0 °C		5237 psi
@Strain 3.06 %,
Temperature 194 °F		ISO 527
 36.99 MPa
@Strain 3.70 %,
Temperature 90.0 °C		5365 psi
@Strain 3.70 %,
Temperature 194 °F		ISO 527
 37.49 MPa
@Strain 4.29 %,
Temperature 90.0 °C		5437 psi
@Strain 4.29 %,
Temperature 194 °F		ISO 527
 37.5 MPa
@Strain 0.920 %,
Temperature 60.0 °C		5440 psi
@Strain 0.920 %,
Temperature 140 °F		ISO 527
 37.85 MPa
@Strain 4.93 %,
Temperature 90.0 °C		5490 psi
@Strain 4.93 %,
Temperature 194 °F		ISO 527
 38.06 MPa
@Strain 5.51 %,
Temperature 90.0 °C		5520 psi
@Strain 5.51 %,
Temperature 194 °F		ISO 527
 38.1 MPa
@Strain 6.10 %,
Temperature 90.0 °C		5530 psi
@Strain 6.10 %,
Temperature 194 °F		ISO 527
 41.82 MPa
@Strain 1.13 %,
Temperature 60.0 °C		6065 psi
@Strain 1.13 %,
Temperature 140 °F		ISO 527
 42.67 MPa
@Strain 0.600 %,
Temperature 40.0 °C		6189 psi
@Strain 0.600 %,
Temperature 104 °F		ISO 527
 43.96 MPa
@Strain 0.540 %,
Temperature 23.0 °C		6376 psi
@Strain 0.540 %,
Temperature 73.4 °F		ISO 527
 47.12 MPa
@Strain 1.54 %,
Temperature 60.0 °C		6834 psi
@Strain 1.54 %,
Temperature 140 °F		ISO 527
 48.7 MPa
@Strain 1.74 %,
Temperature 60.0 °C		7060 psi
@Strain 1.74 %,
Temperature 140 °F		ISO 527
 49.81 MPa
@Strain 1.95 %,
Temperature 60.0 °C		7224 psi
@Strain 1.95 %,
Temperature 140 °F		ISO 527
 50.34 MPa
@Strain 0.800 %,
Temperature 40.0 °C		7301 psi
@Strain 0.800 %,
Temperature 104 °F		ISO 527
 50.98 MPa
@Strain 0.680 %,
Temperature 23.0 °C		7394 psi
@Strain 0.680 %,
Temperature 73.4 °F		ISO 527
 51.01 MPa
@Strain 2.36 %,
Temperature 60.0 °C		7398 psi
@Strain 2.36 %,
Temperature 140 °F		ISO 527
 51.21 MPa
@Strain 2.56 %,
Temperature 60.0 °C		7427 psi
@Strain 2.56 %,
Temperature 140 °F		ISO 527
 51.24 MPa
@Strain 2.77 %,
Temperature 60.0 °C		7432 psi
@Strain 2.77 %,
Temperature 140 °F		ISO 527
 55.67 MPa
@Strain 1.00 %,
Temperature 40.0 °C		8074 psi
@Strain 1.00 %,
Temperature 104 °F		ISO 527
 58.01 MPa
@Strain 0.870 %,
Temperature 23.0 °C		8414 psi
@Strain 0.870 %,
Temperature 73.4 °F		ISO 527
 59.46 MPa
@Strain 1.20 %,
Temperature 40.0 °C		8624 psi
@Strain 1.20 %,
Temperature 104 °F		ISO 527
 62.0 MPa
@Strain 1.40 %,
Temperature 40.0 °C		8990 psi
@Strain 1.40 %,
Temperature 104 °F		ISO 527
 62.98 MPa
@Strain 1.06 %,
Temperature 23.0 °C		9134 psi
@Strain 1.06 %,
Temperature 73.4 °F		ISO 527
 63.67 MPa
@Strain 1.60 %,
Temperature 40.0 °C		9235 psi
@Strain 1.60 %,
Temperature 104 °F		ISO 527
 64.38 MPa
@Strain 1.80 %,
Temperature 40.0 °C		9338 psi
@Strain 1.80 %,
Temperature 104 °F		ISO 527
 65.77 MPa
@Strain 1.20 %,
Temperature 23.0 °C		9539 psi
@Strain 1.20 %,
Temperature 73.4 °F		ISO 527
 68.66 MPa
@Strain 1.39 %,
Temperature 23.0 °C		9958 psi
@Strain 1.39 %,
Temperature 73.4 °F		ISO 527
 70.66 MPa
@Strain 1.57 %,
Temperature 23.0 °C		10250 psi
@Strain 1.57 %,
Temperature 73.4 °F		ISO 527
 71.53 MPa
@Strain 1.71 %,
Temperature 23.0 °C		10370 psi
@Strain 1.71 %,
Temperature 73.4 °F		ISO 527
Elongation at Break  1.8 %
@Temperature -40.0 °C		1.8 %
@Temperature -40.0 °F		ASTM D638
 2.0 %
@Temperature 23.0 °C		2.0 %
@Temperature 73.4 °F		ASTM D638
 2.0 %
@Temperature 23.0 °C		2.0 %
@Temperature 73.4 °F		ISO 527
 5.0 %
@Temperature 90.0 °C		5.0 %
@Temperature 194 °F		ASTM D638
 7.0 %
@Temperature 150 °C		7.0 %
@Temperature 302 °F		ASTM D638
Tensile Modulus  2.42 GPa
@Temperature 150 °C		351 ksi
@Temperature 302 °F		ASTM D638
 3.17 GPa
@Temperature 90.0 °C		460 ksi
@Temperature 194 °F		ASTM D638
 9.93 GPa
@Temperature 23.0 °C		1440 ksi
@Temperature 73.4 °F		ASTM D638
 10.2 GPa
@Temperature 23.0 °C		1480 ksi
@Temperature 73.4 °F		ISO 527
 11.2 GPa
@Temperature -40.0 °C		1620 ksi
@Temperature -40.0 °F		ASTM D638
Flexural Strength  42.7 MPa
@Temperature 150 °C		6190 psi
@Temperature 302 °F		ASTM D790
 62.1 MPa
@Temperature 90.0 °C		9010 psi
@Temperature 194 °F		ASTM D790
 141 MPa
@Temperature 23.0 °C		20500 psi
@Temperature 73.4 °F		ASTM D790
 176 MPa
@Temperature -40.0 °C		25500 psi
@Temperature -40.0 °F		ASTM D790
Flexural Modulus  2.20 GPa
@Temperature 150 °C		319 ksi
@Temperature 302 °F		ASTM D790
 2.20 GPa
@Temperature 150 °C		319 ksi
@Temperature 302 °F		ISO 178
 3.37 GPa
@Temperature 90.0 °C		489 ksi
@Temperature 194 °F		ASTM D790
 3.40 GPa
@Temperature 93.0 °C		493 ksi
@Temperature 199 °F		ISO 178
 9.10 GPa
@Temperature 23.0 °C		1320 ksi
@Temperature 73.4 °F		ISO 178
 9.60 GPa
@Temperature 23.0 °C		1390 ksi
@Temperature 73.4 °F		ASTM D790
 11.7 GPa
@Temperature -40.0 °C		1700 ksi
@Temperature -40.0 °F		ASTM D790
 11.8 GPa
@Temperature -40.0 °C		1710 ksi
@Temperature -40.0 °F		ISO 178
Compressive Strength 141 MPa
@Temperature 23.0 °C		20500 psi
@Temperature 73.4 °F		ASTM D695
Shear Modulus  0.0390 GPa
@Temperature 250 °C		5.66 ksi
@Temperature 482 °F		ISO 6721
 0.105 GPa
@Temperature 240 °C		15.2 ksi
@Temperature 464 °F		ISO 6721
 0.180 GPa
@Temperature 230 °C		26.1 ksi
@Temperature 446 °F		ISO 6721
 0.260 GPa
@Temperature 220 °C		37.7 ksi
@Temperature 428 °F		ISO 6721
 0.297 GPa
@Temperature 210 °C		43.1 ksi
@Temperature 410 °F		ISO 6721
 0.321 GPa
@Temperature 200 °C		46.6 ksi
@Temperature 392 °F		ISO 6721
 0.342 GPa
@Temperature 190 °C		49.6 ksi
@Temperature 374 °F		ISO 6721
 0.363 GPa
@Temperature 180 °C		52.6 ksi
@Temperature 356 °F		ISO 6721
 0.383 GPa
@Temperature 170 °C		55.6 ksi
@Temperature 338 °F		ISO 6721
 0.404 GPa
@Temperature 160 °C		58.6 ksi
@Temperature 320 °F		ISO 6721
 0.426 GPa
@Temperature 150 °C		61.8 ksi
@Temperature 302 °F		ISO 6721
 0.451 GPa
@Temperature 140 °C		65.4 ksi
@Temperature 284 °F		ISO 6721
 0.483 GPa
@Temperature 130 °C		70.1 ksi
@Temperature 266 °F		ISO 6721
 0.529 GPa
@Temperature 120 °C		76.7 ksi
@Temperature 248 °F		ISO 6721
 0.597 GPa
@Temperature 110 °C		86.6 ksi
@Temperature 230 °F		ISO 6721
 0.694 GPa
@Temperature 100 °C		101 ksi
@Temperature 212 °F		ISO 6721
 0.822 GPa
@Temperature 90.0 °C		119 ksi
@Temperature 194 °F		ISO 6721
 0.975 GPa
@Temperature 80.0 °C		141 ksi
@Temperature 176 °F		ISO 6721
 1.13 GPa
@Temperature 70.0 °C		164 ksi
@Temperature 158 °F		ISO 6721
 1.28 GPa
@Temperature 60.0 °C		186 ksi
@Temperature 140 °F		ISO 6721
 1.39 GPa
@Temperature 50.0 °C		202 ksi
@Temperature 122 °F		ISO 6721
 1.42 GPa
@Temperature 40.0 °C		206 ksi
@Temperature 104 °F		ISO 6721
 1.44 GPa
@Temperature 30.0 °C		209 ksi
@Temperature 86.0 °F		ISO 6721
 1.45 GPa
@Temperature 20.0 °C		210 ksi
@Temperature 68.0 °F		ISO 6721
 1.47 GPa
@Temperature 10.0 °C		213 ksi
@Temperature 50.0 °F		ISO 6721
 1.48 GPa
@Temperature 0.000 °C		215 ksi
@Temperature 32.0 °F		ISO 6721
 1.50 GPa
@Temperature -10.0 °C		218 ksi
@Temperature 14.0 °F		ISO 6721
 1.51 GPa
@Temperature -20.0 °C		219 ksi
@Temperature -4.00 °F		ISO 6721
 1.53 GPa
@Temperature -30.0 °C		222 ksi
@Temperature -22.0 °F		ISO 6721
 1.55 GPa
@Temperature -40.0 °C		225 ksi
@Temperature -40.0 °F		ISO 6721
 1.59 GPa
@Temperature -50.0 °C		231 ksi
@Temperature -58.0 °F		ISO 6721
Shear Strength 53.7 MPa
@Temperature 23.0 °C		7790 psi
@Temperature 73.4 °F		ASTM D732
Izod Impact, Notched  0.430 J/cm
@Temperature -40.0 °C		0.806 ft-lb/in
@Temperature -40.0 °F		ASTM D256
 0.640 J/cm
@Temperature 23.0 °C		1.20 ft-lb/in
@Temperature 73.4 °F		ASTM D256
Izod Impact, Unnotched  2.80 J/cm
@Temperature -40.0 °C		5.25 ft-lb/in
@Temperature -40.0 °F		ASTM D4812
 4.25 J/cm
@Temperature 23.0 °C		7.96 ft-lb/in
@Temperature 73.4 °F		ASTM D4812
Izod Impact, Notched (ISO)  4.00 kJ/m²
@Temperature -30.0 °C		1.90 ft-lb/in²
@Temperature -22.0 °F		ISO 180/1A
 6.00 kJ/m²
@Temperature 23.0 °C		2.86 ft-lb/in²
@Temperature 73.4 °F		ISO 180/1A
Izod Impact, Unnotched (ISO) 30.0 kJ/m²
@Temperature 23.0 °C		14.3 ft-lb/in²
@Temperature 73.4 °F		ISO 180/1U
Charpy Impact Unnotched  2.00 J/cm²
@Temperature -30.0 °C		9.52 ft-lb/in²
@Temperature -22.0 °F		ISO 179/1eU
 2.50 J/cm²
@Temperature 23.0 °C		11.9 ft-lb/in²
@Temperature 73.4 °F		ISO 179/1eU
Charpy Impact, Notched  0.400 J/cm²
@Temperature -30.0 °C		1.90 ft-lb/in²
@Temperature -22.0 °F		ISO 179/1eA
 0.600 J/cm²
@Temperature 23.0 °C		2.86 ft-lb/in²
@Temperature 73.4 °F		ISO 179/1eA
Tensile Creep Modulus, 1 hour 9350 MPa
@Temperature 23.0 °C		1.36e+6 psi
@Temperature 73.4 °F		ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 10.0 MPa
@Strain 0.109 %,
Temperature 23.0 °C		1450 psi
@Strain 0.109 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 10.0 MPa
@Strain 0.105 %,
Temperature 23.0 °C		1450 psi
@Strain 0.105 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 20.0 MPa
@Strain 0.216 %,
Temperature 23.0 °C		2900 psi
@Strain 0.216 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 20.0 MPa
@Strain 0.226 %,
Temperature 23.0 °C		2900 psi
@Strain 0.226 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 30.0 MPa
@Strain 0.360 %,
Temperature 23.0 °C		4350 psi
@Strain 0.360 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 30.0 MPa
@Strain 0.337 %,
Temperature 23.0 °C		4350 psi
@Strain 0.337 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 40.0 MPa
@Strain 0.489 %,
Temperature 23.0 °C		5800 psi
@Strain 0.489 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 40.0 MPa
@Strain 0.537 %,
Temperature 23.0 °C		5800 psi
@Strain 0.537 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 50.0 MPa
@Strain 0.896 %,
Temperature 23.0 °C		7250 psi
@Strain 0.896 %,
Temperature 73.4 °F		10h; Break; Isochronous; ISO 899
 50.0 MPa
@Strain 0.755 %,
Temperature 23.0 °C		7250 psi
@Strain 0.755 %,
Temperature 73.4 °F		1h; Break; Isochronous; ISO 899
Tensile Creep Modulus, 1000 hours 7690 MPa
@Temperature 23.0 °C		1.12e+6 psi
@Temperature 73.4 °F		ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		10000h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		5000h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 10.0 MPa
@Strain 0.126 %,
Temperature 23.0 °C		1450 psi
@Strain 0.126 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 10.0 MPa
@Strain 0.116 %,
Temperature 23.0 °C		1450 psi
@Strain 0.116 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 10.0 MPa
@Strain 0.134 %,
Temperature 23.0 °C		1450 psi
@Strain 0.134 %,
Temperature 73.4 °F		5000h; Isochronous; ISO 899
 10.0 MPa
@Strain 0.139 %,
Temperature 23.0 °C		1450 psi
@Strain 0.139 %,
Temperature 73.4 °F		10000h; Isochronous; ISO 899
 20.0 MPa
@Strain 0.310 %,
Temperature 23.0 °C		2900 psi
@Strain 0.310 %,
Temperature 73.4 °F		10000h; Isochronous; ISO 899
 20.0 MPa
@Strain 0.300 %,
Temperature 23.0 °C		2900 psi
@Strain 0.300 %,
Temperature 73.4 °F		5000h; Isochronous; ISO 899
 20.0 MPa
@Strain 0.246 %,
Temperature 23.0 °C		2900 psi
@Strain 0.246 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 20.0 MPa
@Strain 0.275 %,
Temperature 23.0 °C		2900 psi
@Strain 0.275 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 30.0 MPa
@Strain 0.467 %,
Temperature 23.0 °C		4350 psi
@Strain 0.467 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 30.0 MPa
@Strain 0.404 %,
Temperature 23.0 °C		4350 psi
@Strain 0.404 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 30.0 MPa
@Strain 0.525 %,
Temperature 23.0 °C		4350 psi
@Strain 0.525 %,
Temperature 73.4 °F		5000h; Isochronous; ISO 899
 30.0 MPa
@Strain 0.545 %,
Temperature 23.0 °C		4350 psi
@Strain 0.545 %,
Temperature 73.4 °F		10000h; Isochronous; ISO 899
 40.0 MPa
@Strain 0.921 %,
Temperature 23.0 °C		5800 psi
@Strain 0.921 %,
Temperature 73.4 °F		10000h; Isochronous; ISO 899
 40.0 MPa
@Strain 0.870 %,
Temperature 23.0 °C		5800 psi
@Strain 0.870 %,
Temperature 73.4 °F		5000h; Isochronous; ISO 899
 40.0 MPa
@Strain 0.624 %,
Temperature 23.0 °C		5800 psi
@Strain 0.624 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 40.0 MPa
@Strain 0.749 %,
Temperature 23.0 °C		5800 psi
@Strain 0.749 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 50.0 MPa
@Strain 1.84 %,
Temperature 23.0 °C		7250 psi
@Strain 1.84 %,
Temperature 73.4 °F		10000h; Break; Isochronous; ISO 899
 50.0 MPa
@Strain 1.46 %,
Temperature 23.0 °C		7250 psi
@Strain 1.46 %,
Temperature 73.4 °F		1000h; Break; Isochronous; ISO 899
 50.0 MPa
@Strain 1.74 %,
Temperature 23.0 °C		7250 psi
@Strain 1.74 %,
Temperature 73.4 °F		5000h; Break; Isochronous; ISO 899
 50.0 MPa
@Strain 1.15 %,
Temperature 23.0 °C		7250 psi
@Strain 1.15 %,
Temperature 73.4 °F		100h; Break; Isochronous; ISO 899
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity  1.00e+15 ohm-cm
@Temperature 23.0 °C		1.00e+15 ohm-cm
@Temperature 73.4 °F		ASTM D257
 1.00e+15 ohm-cm
@Temperature 23.0 °C		1.00e+15 ohm-cm
@Temperature 73.4 °F		IEC 60093
Surface Resistance  1.00e+14 ohm
@Temperature 23.0 °C		1.00e+14 ohm
@Temperature 73.4 °F		ASTM D257
 1.00e+14 ohm
@Temperature 23.0 °C		1.00e+14 ohm
@Temperature 73.4 °F		IEC 60093
Dielectric Constant  3.7
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		3.7
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		ASTM D150
 3.8
@Frequency 1000 Hz,
Temperature 23.0 °C		3.8
@Frequency 1000 Hz,
Temperature 73.4 °F		ASTM D150
 4.1
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		4.1
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		IEC 60250
 4.5
@Frequency 100 Hz,
Temperature 23.0 °C		4.5
@Frequency 100 Hz,
Temperature 73.4 °F		IEC 60250
Dielectric Strength  12.0 kV/mm
@Thickness 3.20 mm,
Temperature 150 °C		305 kV/in
@Thickness 0.126 in,
Temperature 302 °F		500 V/s, in oil; Short Time; ASTM D149
 14.5 kV/mm
@Thickness 1.60 mm,
Temperature 150 °C		368 kV/in
@Thickness 0.0630 in,
Temperature 302 °F		500 V/s, in oil; Short Time; ASTM D149
 19.5 kV/mm
@Thickness 3.20 mm,
Temperature 95.0 °C		495 kV/in
@Thickness 0.126 in,
Temperature 203 °F		500 V/s, in oil; Short Time; ASTM D149
 23.5 kV/mm
@Thickness 3.20 mm,
Temperature 23.0 °C		597 kV/in
@Thickness 0.126 in,
Temperature 73.4 °F		500 V/s, in oil; Short Time; ASTM D149
 25.5 kV/mm
@Thickness 1.60 mm,
Temperature 95.0 °C		648 kV/in
@Thickness 0.0630 in,
Temperature 203 °F		500 V/s, in oil; Short Time; ASTM D149
 29.5 kV/mm
@Thickness 1.60 mm,
Temperature 23.0 °C		749 kV/in
@Thickness 0.0630 in,
Temperature 73.4 °F		500 V/s, in oil; Short Time; ASTM D149
 39.0 kV/mm
@Thickness 1.00 mm,
Temperature 23.0 °C		991 kV/in
@Thickness 0.0394 in,
Temperature 73.4 °F		IEC 60243-1
Dissipation Factor  0.0080
@Frequency 1000 Hz,
Temperature 23.0 °C		0.0080
@Frequency 1000 Hz,
Temperature 73.4 °F		ASTM D150
 0.010
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.010
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		ASTM D150
 0.014
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.014
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		IEC 60250
 0.030
@Frequency 100 Hz,
Temperature 23.0 °C		0.030
@Frequency 100 Hz,
Temperature 73.4 °F		IEC 60250
Comparative Tracking Index  250 V
@Temperature 23.0 °C		250 V
@Temperature 73.4 °F		UL 746A
 300 V
@Temperature 23.0 °C		300 V
@Temperature 73.4 °F		IEC 60112
 250 - 400 V
@Temperature 23.0 °C		250 - 400 V
@Temperature 73.4 °F		UL 746A
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow  500 µm/m-°C
@Temperature -40.0 - 23.0 °C		278 µin/in-°F
@Temperature -40.0 - 73.4 °F		ASTM E 831
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		ASTM E 831
 500 µm/m-°C
@Temperature 55.0 - 160 °C		278 µin/in-°F
@Temperature 131 - 320 °F		ASTM E 831
 500 µm/m-°C
@Temperature -40.0 - 23.0 °C		278 µin/in-°F
@Temperature -40.0 - 73.4 °F		ISO 11359-1/-2
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		ISO 11359-1/-2
 500 µm/m-°C
@Temperature 55.0 - 160 °C		278 µin/in-°F
@Temperature 131 - 320 °F		ISO 11359-1/-2
 500 µm/m-°C
@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Thickness 0.0787 in,
Temperature 73.4 - 131 °F		ASTM E 831
 500 µm/m-°C
@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Thickness 0.0787 in,
Temperature 73.4 - 131 °F		ISO 11359-1/-2
CTE, linear, Transverse to Flow  52.0 µm/m-°C
@Temperature 23.0 - 55.0 °C		28.9 µin/in-°F
@Temperature 73.4 - 131 °F		ISO 11359-1/-2
 52.0 µm/m-°C
@Temperature 23.0 - 55.0 °C		28.9 µin/in-°F
@Temperature 73.4 - 131 °F		ASTM E 831
 53.0 µm/m-°C
@Temperature -40.0 - 23.0 °C		29.4 µin/in-°F
@Temperature -40.0 - 73.4 °F		ISO 11359-1/-2
 53.0 µm/m-°C
@Temperature -40.0 - 23.0 °C		29.4 µin/in-°F
@Temperature -40.0 - 73.4 °F		ASTM E 831
 81.0 µm/m-°C
@Temperature 55.0 - 160 °C		45.0 µin/in-°F
@Temperature 131 - 320 °F		ISO 11359-1/-2
 81.0 µm/m-°C
@Temperature 55.0 - 160 °C		45.0 µin/in-°F
@Temperature 131 - 320 °F		ASTM E 831
 74.0 µm/m-°C
@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C		41.1 µin/in-°F
@Thickness 0.0787 in,
Temperature 73.4 - 131 °F		ISO 11359-1/-2
 74.0 µm/m-°C
@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C		41.1 µin/in-°F
@Thickness 0.0787 in,
Temperature 73.4 - 131 °F		ASTM E 831
Melting Point 252 °C486 °FASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 235 °C455 °FISO 75-1/-2
 241 °C466 °FASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 200 °C392 °FISO 75-1/-2
 215 °C419 °FASTM D648
UL RTI, Electrical  140 °C
@Thickness 3.00 mm		284 °F
@Thickness 0.118 in		UL 746B
 140 °C
@Thickness 1.50 mm		284 °F
@Thickness 0.0591 in		UL 746B
 140 °C
@Thickness 0.750 mm		284 °F
@Thickness 0.0295 in		UL 746B
UL RTI, Mechanical with Impact  140 °C
@Thickness 0.750 mm		284 °F
@Thickness 0.0295 in		UL 746B
 140 °C
@Thickness 1.50 mm		284 °F
@Thickness 0.0591 in		UL 746B
 140 °C
@Thickness 3.00 mm		284 °F
@Thickness 0.118 in		UL 746B
UL RTI, Mechanical without Impact  140 °C
@Thickness 3.00 mm		284 °F
@Thickness 0.118 in		UL 746B
 140 °C
@Thickness 1.50 mm		284 °F
@Thickness 0.0591 in		UL 746B
 140 °C
@Thickness 0.750 mm		284 °F
@Thickness 0.0295 in		UL 746B
Flammability, UL94  HB
@Thickness 0.750 mm		HB
@Thickness 0.0295 in		IEC 60695-11-10
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		IEC 60695-11-10
 HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		IEC 60695-11-10
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		UL94
 HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		UL94
 HB
@Thickness 0.750 mm		HB
@Thickness 0.0295 in		UL94
Oxygen Index 21 %21 %ISO 4589-1/-2
Glow Wire Test  775 °C
@Thickness 0.750 mm		1430 °F
@Thickness 0.0295 in		IEC 60695-2-12
 775 °C
@Thickness 1.50 mm		1430 °F
@Thickness 0.0591 in		IEC 60695-2-12
 800 °C
@Thickness 1.50 mm		1470 °F
@Thickness 0.0591 in		Ignition; IEC 60695-2-13
 800 °C
@Thickness 0.750 mm		1470 °F
@Thickness 0.0295 in		Ignition; IEC 60695-2-13
 825 °C
@Thickness 3.00 mm		1520 °F
@Thickness 0.118 in		IEC 60695-2-12
 850 °C
@Thickness 3.00 mm		1560 °F
@Thickness 0.118 in		Ignition; IEC 60695-2-13
 
Processing PropertiesMetricEnglishComments
Melt Temperature 252 °C486 °F10°C/min; ISO 11357-1/-3
 285 °C545 °FOptimum
 280 - 300 °C536 - 572 °F
Mold Temperature >= 95.0 °C>= 203 °F
 110 °C230 °Foptimum
Drying Temperature 120 °C248 °F
Dry Time 4.00 hour4.00 hour
Moisture Content <= 0.020 %<= 0.020 %
 
Descriptive Properties
AppearanceNatural Color
Drying RecommendedYes
FeaturesDimensional Stability, Good
 Electrical Properties, Good
 Stiffness, Good
 Strength, Good
 Thermal Aging Resistance, Good
 Warp Resistant
FillerGlass/Mica
FormsPellets
GenericPET
Heat StabilizedYes
Material StatusCurrent
Part Marking Code>PET-(MD+GF)35<ISO 11469
Polymer FamilyPolyester
Polymer TypePET
Processing MethodInjection Molding
Product CategoryGlass/Mineral Reinforced Resins
 Low Warp Resins
Region Available - GlobalYes
Resin IdentificationPET-(MD+GF)35ISO 1043
RoHS ComplianceContact Manufacturer
Ultrasonic WeldableYes
UsesAutomotive Applications
 Electrical/Electronic Applications
 Housings
 Phenolic Replacement
 Structural Parts

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-38896.html

免责声明: 本文 DuPont Performance Polymers Rynite® 935 NC010 PET 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4