- 密度 [g/cm3]: 1.3
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.803 g/cc | 0.0290 lb/in³ | Poured; ASTM D1895 | ||
| 0.881 g/cc | 0.0318 lb/in³ | Vibrated; ASTM D1895 | |||
| Density | 1.30 g/cc | 0.0470 lb/in³ | Film; ASTM D1505 | ||
| 1.40 g/cc | 0.0506 lb/in³ | Crystalline Density; ASTM D1505 | |||
| Melt Density | 1.20 g/cc @Temperature 285 °C | 0.0434 lb/in³ @Temperature 545 °F | ASTM D1238 | ||
| Viscosity Measurement | 0.78 | 0.78 | Intrinsic; EMN-A-AC-G-V-1 | ||
| 0.78 - 0.82 | 0.78 - 0.82 | Pellet, Intrinsic; VGAS-A-AN-G-V-1 | |||
| Thickness | 250 microns | 9.84 mil | |||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 55.0 MPa | 7980 psi | ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 53.0 MPa | 7690 psi | ASTM D882 | ||
| Film Elongation at Break, MD | 600 % | 600 % | ASTM D882 | ||
| Film Elongation at Break, TD | 600 % | 600 % | ASTM D882 | ||
| Film Elongation at Yield, MD | 6.0 % | 6.0 % | ASTM D882 | ||
| Film Elongation at Yield, TD | 6.0 % | 6.0 % | ASTM D882 | ||
| Tensile Modulus | 2.00 GPa | 290 ksi | TD; ASTM D882 | ||
| 2.10 GPa | 305 ksi | MD; ASTM D882 | |||
| Izod Impact, Unnotched (ISO) | NB | NB | ISO 180 | ||
| 181 kJ/m² @Temperature -40.0 °C | 86.1 ft-lb/in² @Temperature -40.0 °F | ISO 180 | |||
| Tear Strength, Total | 92.0 N | 20.7 lb (f) | PPT Tear Resistance, MD; ASTM D2582 | ||
| 106 N | 23.8 lb (f) | PPT Tear Resistance, TD; ASTM D2582 | |||
| Elmendorf Tear Strength, MD | 3.14 g/micron | 79.8 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 3.236 g/micron | 82.19 g/mil | ASTM D1922 | ||
| Dart Drop | 1.08 g/micron | 27.4 g/mil | at -18°C; ASTM D1709 | ||
| 1.876 g/micron | 47.65 g/mil | 23°C; ASTM D1709 | |||
| Film Tensile Strength at Break, MD | 60.0 MPa | 8700 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 48.0 MPa | 6960 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Heat of Fusion | 61.0 J/g | 26.2 BTU/lb | ASTM E793 | ||
| Specific Heat Capacity | 1.20 J/g-°C | 0.287 BTU/lb-°F | ASTM E1269 | ||
| 1.40 J/g-°C @Temperature 80.0 °C | 0.335 BTU/lb-°F @Temperature 176 °F | ASTM E1269 | |||
| 1.60 J/g-°C @Temperature 100 °C | 0.382 BTU/lb-°F @Temperature 212 °F | ASTM E1269 | |||
| 2.00 J/g-°C @Temperature 200 °C | 0.478 BTU/lb-°F @Temperature 392 °F | ASTM E1269 | |||
| 2.10 J/g-°C @Temperature 280 °C | 0.502 BTU/lb-°F @Temperature 536 °F | ASTM E1269 | |||
| Melting Point | 239 °C | 462 °F | Crystalline Peak Melting Point; ASTM D3418 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 0.40 % | 0.40 % | ASTM D1003 | ||
| Gloss | 111 % | 111 % | at 45°; ASTM D2457 | ||
| Transmission, Visible | 90 % | 90 % | Regular Transmittance; ASTM D1003 | ||
| 92 % | 92 % | Total Transmittance; ASTM D1003 | |||
| 99 % | 99 % | Clarity; ASTM D1003 | |||
| Descriptive Properties | |||||
| Acetaldehyde | <1ppm | VKCA-A-AS-G-GC-0001 | |||
| Color, CIE a* | -0.02 | VGAS-A-AN-G-RS-001 | |||
| Color, CIE b* | 0.37 | VGAS-A-AN-G-RS-001 | |||
| Color, CIE L* | 96 | VGAS-A-AN-G-RS-001 | |||
| Fines, wt%, max | 0.05 | VGAS-A-AN-G-GA-1 | |||
| Pellet Shape | Rectangular 2x2x3 mm | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.