- 密度 [g/cm3]: 1.69
- 缺口冲击强度: 1.15
- 拉伸强度 [MPa]: 195.0
- 断裂伸长率 [%]: 300
- 弯曲模量 [MPa]: 13.8
- 热变形温度 [℃]: 249.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.69 g/cc | 0.0611 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 195 MPa | 28300 psi | ASTM D638 |
| Elongation at Break | 2.1 % | 2.1 % | ASTM D638 |
| Flexural Yield Strength | 300 MPa | 43500 psi | ASTM D790 |
| Flexural Modulus | 13.8 GPa | 2000 ksi | ASTM D790 |
| Izod Impact, Notched | 1.15 J/cm | 2.15 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 254 °C | 489 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 249 °C | 480 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 225 °C | 437 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 270 - 300 °C | 518 - 572 °F | |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |