- 密度 [g/cm3]: 1.45
- 缺口冲击强度: 4.5
- 弯曲模量 [MPa]: 6.30
- 热变形温度 [℃]: 220.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.00400 - 0.00600 cm/cm | 0.00400 - 0.00600 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 95.0 MPa | 13800 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 1.80 % | 1.80 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 6.40 GPa | 928 ksi | 1mm/min; ISO 527-2/1A |
| Flexural Strength | 135 MPa | 19600 psi | ISO 178 |
| Flexural Modulus | 6.30 GPa | 914 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 4.50 kJ/m² | 2.14 ft-lb/in² | ISO 180/1A |
| Charpy Impact, Notched | 0.470 J/cm² | 2.24 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 180 °C | 356 °F | ISO 75-1, -2 |
| Flammability, UL94 | HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | UL94 |