- 吸水率 [%]: 0.07
- 缺口冲击强度: 0.75
- 弯曲模量 [MPa]: 7.50
- 硬度: 120.0
- 热变形温度 [℃]: 235.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.56 g/cc @Temperature 23.0 °C | 1.56 g/cc @Temperature 73.4 °F | ASTM D792 | ||
| Water Absorption | 0.070 % @Temperature 23.0 °C, Time 86400 sec | 0.070 % @Temperature 73.4 °F, Time 24.0 hour | ASTM D570 | ||
| Linear Mold Shrinkage | 0.0020 - 0.010 cm/cm @Temperature 23.0 °C | 0.0020 - 0.010 in/in @Temperature 73.4 °F | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 120 | 120 | ASTM D785 | ||
| Tensile Strength at Break | 123 MPa | 17800 psi | 10mm/min; ASTM D638 | ||
| Elongation at Break | 2.6 % | 2.6 % | 10mm/min; ASTM D638 | ||
| Flexural Strength | 175 MPa | 25400 psi | 2mm/min; ASTM D790 | ||
| Flexural Modulus | 7.50 GPa | 1090 ksi | 2mm/min; ASTM D790 | ||
| Izod Impact, Notched | 0.750 J/cm @Thickness 3.20 mm, Temperature 23.0 °C | 1.41 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F | ASTM D256 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 235 °C @Thickness 6.40 mm | 455 °F @Thickness 0.252 in | ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C @Thickness 6.40 mm | 410 °F @Thickness 0.252 in | ASTM D648 | ||
| Flammability, UL94 | V-0 @Thickness 0.750 mm | V-0 @Thickness 0.0295 in | |||
| V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | ||||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | <= 270 °C | <= 518 °F | |||
| Rear Barrel Temperature | 235 - 255 °C | 455 - 491 °F | Start Point: 245°C | ||
| Middle Barrel Temperature | 245 - 265 °C | 473 - 509 °F | Start Point: 250°C | ||
| Front Barrel Temperature | 255 - 275 °C | 491 - 527 °F | Start Point: 260°C | ||
| Melt Temperature | 255 - 275 °C | 491 - 527 °F | Start Point: 260°C | ||
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | Start Point: 100°C | ||
| Drying Temperature | 120 - 140 °C @Time 10800 - 18000 sec | 248 - 284 °F @Time 3.00 - 5.00 hour | Pre-dry | ||
| Descriptive Properties | |||||
| Glass Fiber Content (%) | 20 | ||||
| Injection Speed | Moderate to High | ||||