- 熔体流动速率 [g/10min]: 16.0
- 密度 [g/cm3]: 1.33
- 吸水率 [%]: 0.07
- 缺口冲击强度: 0.49
- 断裂伸长率 [%]: 89.2
- 弯曲强度 [MPa]: 58.8
- 弯曲模量 [MPa]: 2.73
- 硬度: 88.0
- 热变形温度 [℃]: 75.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | DIN 53479; ASTM D792 |
| Water Absorption | 0.070 % | 0.070 % | DIN 53475; ASTM D570 |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | ASTM D955 |
| Melt Flow | 16 g/10 min @Temperature 275 °C | 16 g/10 min @Temperature 527 °F | DSC |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 88 | 88 | DIN 53505; ASTM D785 |
| Tensile Strength, Ultimate | 58.8 MPa | 8530 psi | DIN 53455; ASTM D638 |
| Elongation at Break | 400 % | 400 % | DIN 53455; ASTM D638 |
| Flexural Yield Strength | 89.2 MPa | 12900 psi | DIN 53455; ASTM D790 |
| Flexural Modulus | 2.73 GPa | 395 ksi | DIN 53452; ASTM D790 |
| Izod Impact, Notched | 0.490 J/cm | 0.918 ft-lb/in | DIN 53453; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 60 µm/m-°C @Temperature 20.0 °C | 33 µin/in-°F @Temperature 68.0 °F | DIN 53752; ASTM D696 |
| Melting Point | 241 °C | 466 °F | DIN 53736; ASTM D789 |
| Deflection Temperature at 0.46 MPa (66 psi) | 75.0 °C | 167 °F | ASTM D648 |
| Glass Transition Temp, Tg | 82.0 °C | 180 °F | DSC |
| Flammability, UL94 | HB | HB | |
| Optical Properties | Metric | English | Comments |
| Haze | 1.0 % | 1.0 % | ASTM D1003 |