- 熔体流动速率 [g/10min]: 42.0
- 密度 [g/cm3]: 1.68
- 吸水率 [%]: 0.3
- 热变形温度 [℃]: 225.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.68 g/cc | 0.0607 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.30 % | 0.30 % | Test Sim. to ISO 62 | ||
| Moisture Absorption at Equilibrium | 0.10 % | 0.10 % | 23°C/50% R.H.; Test Sim. to ISO 62 | ||
| Viscosity Test | 80 cm³/g | 80 cm³/g | Viscosity number; ISO 307, 1157, 1628 | ||
| Melt Flow | 42 g/10 min @Load 5.00 kg, Temperature 260 °C | 42 g/10 min @Load 11.0 lb, Temperature 500 °F | Calculated from MVR using melt density; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 165 MPa | 23900 psi | ISO 527-1/-2 | ||
| Elongation at Break | 2.0 % | 2.0 % | ISO 527-1/-2 | ||
| Tensile Modulus | 16.5 GPa | 2390 ksi | ISO 527-1/-2 | ||
| Charpy Impact Unnotched | 7.00 J/cm² @Temperature -30.0 °C | 33.3 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | ||
| 7.00 J/cm² @Temperature 23.0 °C | 33.3 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 1.10 J/cm² @Temperature -30.0 °C | 5.23 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | ||
| 1.20 J/cm² @Temperature 23.0 °C | 5.71 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |||
| Tensile Creep Modulus, 1 hour | 16500 MPa | 2.39e+6 psi | ISO 899-1 | ||
| Tensile Creep Modulus, 1000 hours | 15000 MPa | 2.18e+6 psi | ISO 899-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 | ||
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 | ||
| Dielectric Constant | 4.2 @Frequency 1.00e+6 Hz | 4.2 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 4.3 @Frequency 100 Hz | 4.3 @Frequency 100 Hz | IEC 60250 | |||
| Dielectric Strength | 28.0 kV/mm | 711 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.0020 @Frequency 100 Hz | 0.0020 @Frequency 100 Hz | IEC 60250 | ||
| 0.014 @Frequency 1.00e+6 Hz | 0.014 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Comparative Tracking Index | 275 V | 275 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C | 11.1 µin/in-°F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 50.0 µm/m-°C | 27.8 µin/in-°F | ISO 11359-1/-2 | ||
| Melting Point | 225 - 250 °C | 437 - 482 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 225 °C | 437 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 8.0 MPa | 150 °C | 302 °F | ISO 75-1/-2 | ||
| Vicat Softening Point | 210 °C | 410 °F | 50°C/h 50N; ISO 306 | ||
| Flammability, UL94 | HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | IEC 60695-11-10 | ||
| HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | IEC 60695-11-10 | |||
| Oxygen Index | 21 % | 21 % | ISO 4589-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 270 °C | 518 °F | Injection Molding; ISO 294 | ||
| Mold Temperature | 90.0 °C | 194 °F | Injection Molding; ISO 10724 | ||
| Descriptive Properties | |||||
| Additives | Release agent | ||||
| Features | U.V. stabilized or stable to weather | ||||
| Form | Pellets | ||||
| ISO Shortname | ISO 7792-1-PBT+PET,GHLMR,09-160,GF45 | ||||
| Processing | Injection molding | ||||
| Region | Asia Pacific | ||||
| Europe | |||||
| Near East/Africa | |||||
| North America | |||||
| South and Central America | |||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.